碳化物在高铬铸铁高应力磨料磨损中的影响

对不同载荷作用下的高铬铸铁在耐磨实验机上进行了磨料磨损试验;对在不同的碳化物对基体的保护作用与碳化物的剥离进行了相关的分析.结果表明载荷在一定值以下磨损较为缓慢,当载荷超过一定值时,磨损急剧加剧,随着载荷的增加"尺寸较小"的碳化物首先剥离基体,当载荷继续增大时,"尺寸较大"的碳化物也剥离基体并有碎裂现象.这要求高铬铸铁中的碳化物不仅要分布均匀,碳化物的尺寸也要合适.     

GRAIN SHAPE EFFECT IN SUPERPLASTIC DEFORMATION

The method controlling grain shape in TMT processing and the effect of grain shape on char-acteristic parameters in superplastic deformation were discussed.The accommodation velocityof grahl boundary sliding,which is the dominant mechanism in superplastic deformation,andthe contribution of each mechanism to the total strain,as influenced by grain shape,were ana-lyzed.Grain shape has been shown to be an essential structural factor for superplasticity.Thenan analysis was made about the effect of grain shape on the region transition strain rate sothat a new concept,critical aspect for superplasticity,was worked out.These predictions werecompared with the measured results in an Al-Zn-Mg alloy.     

针对通过噪声的空滤器声学特性研究与改进

通过实验方法分析研究了一种中型乘用车通过噪声的特性,比较该车进、排气两侧通过噪声的声级和频谱特性,确定了进气噪声对车辆进气侧通过噪声的重要影响.为了解决该车进气噪声的问题从而达到整车降噪的目的,应用实验与边界元法计算两种手段,对该车空滤器的频率响应特性进行了研究.研究发现空滤器声系统的第一阶声固有频率与进气噪声基频相耦合是造成该车辆进气侧通过噪声高于排气侧的重要原因.基于这一研究结果,在计算和实验的基础上利用Helmholtz共振腔对空滤器的声学特性进行了改进,改进后的空滤器对降低车辆进气侧通过噪声有很好的作用.     

纳米TiN改性金属陶瓷刀片的铣削性能

制备了两种纳米TiN改性金属陶瓷可转位铣刀片ToolA和ToolB。研究了这两种新型面铣刀在切削正火态45#钢时的铣削性能及其失效机理。试验结果表明,两种试验铣刀片在Vc=294m/min,fz=0.16mm/z,ap=0.5mm条件下铣削45#钢时,均未发现“崩刃”现象,并全都以“磨损”的形式失效,刀具寿命较长。此外,在同样切削条件下,ToolA具有良好的抗氧化磨损性能,而ToolB有更高的耐机械冲击能力;高温扩散和氧化磨损成为导致纳米TiN改性铣刀片磨损失效的主要原因。     

Influence of alloy ingredients on mechanical properties of ternary boride hard alloy clad materials

Using Mo, B-Fe alloy and Fe powders as raw materials, and adding C, Cr and Ni ingredients, respectively, or C, Cr and Ni mixed powders, ternary boride hard alloy clad materials was prepared on Q235 steel substrate by means of in-situ reaction and vacuum liquid phase sintering technology. The influence of alloy ingredients on the mechanical properties of ternary boride hard alloy clad materials was investigated. The results indicate that a mixture of 0.8% C, 5% Cr and 2% Ni ingredients gives a ternary boride hard alloy clad material with optimal mechanical properties, such as high transverse rupture strength, high hardness and good wear resistance.     

搅拌摩擦加工SiC复合层对镁合金摩擦磨损性能的影响

研究了搅拌摩擦加工（FSP）AZ91D镁合金SiC复合层的微观组织和磨损性能。结果表明,复合层SiC粒子分布均匀,晶粒细小,成分均一,抗摩擦磨损性能较基体有大幅度提高。     

合金元素对低合金耐磨铸钢力学性能的影响

研究了低合金耐磨铸钢中台金元素C、Si、Mn、Mo，对钢的力学性能等的影响。结果表明，合金元素的合理有效搭配，可使钢在连续空冷条件下得到贝氏体为主的显微组织：钢中C、Mn含量增加，其硬度上升，冲击韧度下降，其中以Mn影响最大，C次之：Si、Mo对钢性能影响程度较小，均在研究的中等含量处取得性能的最佳值。     

深冷处理与工模具的耐磨性

热处理后的金属材料再经低落曙处理，其力学能明显提高，尤其是高碳高合金工模具钢的耐磨性提高特别显著。本文着重研究了应用面较广的Ｗ６Ｍｏ５Ｃｒ４Ｖ２钢的处理工艺制度，组织性能及其磨损机理。     

Ni3Al中B和Mg的非平衡晶界共偏聚

在1023－1373K的初始温度和0.05-268.91K/s的冷速范围内，用Auger剖层分析确定含B和Mg的Ni3Al合金中B和Mg的非平衡晶界共偏聚行为，按照溶质－空位复合体迁移机制所导出的描述非平衡晶界偏聚的扩散速率方程解析表达式，很好地模拟了本实验结果，并确定了Ni3Al-B-Mg合金中B及B－空位复合体，Mg及Mg-空位复合体的扩散系数及复合体激活能。