爆炸焊接——热轧双相不锈钢复合钢板研制

本文主要阐述了通过爆炸焊接和热轧的方法,研制成功可焊性良好的且具有较好强度、韧性与综合性能的双相耐应力腐蚀的不锈复合钢板。还将热轧与热处理的两种试验作了较全面的常规、特殊检验试验,结果完全达到使用要求。     

钛容器的特点

根据钛材的化学、物理、力学和工艺性能介绍了钛容器在设计、制造、检验和应用方面的特点。     

省煤器管开裂原因分析

对省煤器开裂管进行了化学成分及宏、微观分析。分析结果表明，在高温高压条件下，在其焊缝溶合区出现粗大的魏氏组织，管材中的珠光体组织产生了不同程度的球化，而母材组织又存在严重的带状组织。在过热条件下熔合区极易出现裂纹，并由此快速扩展，造成省煤器管开裂。     

Biaxiale Ermüdung reibrührgeschweißter Strukturelemente

Biaxial fatigue of friction stir welded stiffened panels Within the framework of the European WelAir project, cruciform specimens made from stiffening FSW overlap joints were fatigued in the DLR biaxial test rig. To resemble the loading situation of pressurized fuselage structures, proportional loading without any phase shift, but with different load ratios λ between the loading components in both directions was applied.Natural crack initiation and subsequent crack growth were governed by the stiffness gradient caused by introducing the stringer. Cracks initiated and propagated at run‐in and run‐out locations in a direction perpendicular to the weld seam. The shortest fatigue life was observed for uniaxial loading in welding direction (λ = 0). An additional stress component perpendicular to the joint line (λ > 0) resulted in a higher number of cycles to failure. Similar to single stringer panels, increasing the load ratio also increased the number of cycles to failure for FSW clip‐stringer structural members, but additionally gives a different location of the fatal crack.     

海洋平台双相不锈钢管线的焊接

就双相不锈钢的特异性能．介绍双相不锈钢管线的焊接特点与技术。     

Influence of Ni Interlayers on the Mechanical Properties of Ti6Al4V/(WC-Co) Friction Welds

Ni interlayers were introduced prior to dissimilar friction welding of Ti6Al4V base material to three cemented carbide substrates. The fracture strength of Ti6Al4V/(WC-6 wt% Co) welds were poor and were markedly improved when 20-µm thick Ni interlayers were introduced prior to dissimilar friction welding. These results were only produced when the (WC-6 wt% Co) cermet was electroplated prior to friction welding. When the Ti6Al4V alloy was electroplated prior to friction welding, fractured WC particles and cracking were observed in the (WC-Co) carbide substrate. The fracture strengths of Ti6Al4V/(WC-11 wt% Co) and Ti6Al4V/(WC-24 wt% Co) welds were not improved when 20-µm thick Ni interlayers were introduced prior to friction welding. During mechanical testing, the Ni layer retained at the dissimilar joint interface created a region of weakness.     

钻机绞车滚筒体的窄间隙埋弧焊

针对钻机绞车滚筒体采用手工电弧焊工人劳动强度大、焊接效率低、质量不稳定及返修率高等问题,研制了钻机绞车滚筒体窄间隙埋弧焊专机。该专机由ESAB—A2埋弧焊电源和焊接小车、窄间隙焊头、滚轮架、防窜装置、旋转地线夹、三维焊接工作台、焊剂自动回收机组成。使用表明,采用该焊机焊接的滚筒体焊缝质量完全符合设计要求,合格率100%,焊接效率比原来提高6倍。每件滚筒体的焊接可降低人工成本约80%。     

Finite elements in the analysis of pressure vessels and piping-a bibliography (1976–1996)

The paper gives a bibliographical review of the finite element methods (FEMs) applied for the analysis of pressure vessel structures/components and piping from the theoretical as well as practical points of view. The range of applications of FEMs in this area is wide and cannot be presented in a single paper; therefore the aim of this review is to give the reader an encyclopaedic view of the differnt possibilities that exist today for the finite element analysis in the fields of pressure vessels and piping. The bibliography at the end of the paper contains approximately 1900 references to papers, conference proceedings and theses/dissertations on the subject that were published in 1976–1996. These are classified in the following categories: linear and non-linear, static and dynamic, stress and deflection analysis; stability problems; thermal problems; fracture mechanics problems; contact problems; fluid-structure interaction problems; manufacturing of pipes and tubes; welded pipes and pressure vessel components; development of special finite elements for pressure vessels and pipes; finite element software; and other topics. Also finite element software, general purpose and special purpose codes, used for the analysis of pressure vessels and pipes are briefly discussed and presented.     

激光法合成SiC超细粉末物理化学过程的研究——Ⅰ.实验规律及粉末特性

用50W连续波CO_2激光器为热源,诱发SiH_4和C_2H_4反应,合成SiC超细粉末。实验确定了反应腔体内压力p、气源中的C/Si原子比、喷嘴内径2r以及激光功率密度与粉末特性之间的关系,并对合成的产物进行物理、化学表征。