Possibilities and extension of XRD material response analysis in failure research for the advanced evaluation of the damage level of Hertzian loaded components

Due to clearly distinguishable damage symptoms, it is differentiated between the surface and sub‐surface failure mode of rolling bearings. Material states red out by X‐ray diffraction (XRD) residual stress measurements point to a variety of loading conditions especially at raceway surfaces that are associated with several competing failure mechanisms. The corresponding lifetime reduction can range from the lower fatigue strength region to material ratcheting in extreme cases. Relevant position of the microstructural changes and nature of the failure mechanisms are characterized. The time alteration of the XRD material parameters measured at or near the surface and at the depth of the maximum equivalent stress correlates, in a different manner, with the statistical parameter of the 10 % bearing life. Both failure modes are illustrated by concrete examples. Contaminated lubricant and boundary lubrication, which represent practically important surface‐induced failures, are discussed in more detail. Gray staining, i.e. shallow pitting, often occurs without distinct indication of global material aging by means of XRD characteristics. Here, scanning electron microscopy observations and electron microprobe analyses point to corrosion fatigue as acting surface failure mechanism. The interaction between material and lubricant under complex loading regimes particularly of mixed friction and corrosion opens further failure research areas in the field of tribology.     

预应力钢-混凝土组合梁的应用与研究

回顾了预应力钢 混凝土组合梁国内外应用与研究历史 ,分析了现有规范及理论的不足 ,并指出了有待解决的问题。     

主动约束层阻尼板结构动力学建模研究

将有限元法和GHM法相结合，给出了建立主动约束层阻尼（ACLD）板结构动力学模型的新方法。建模时，考虑到粘弹材料（VEM）的纵向位移影响，采用GHM方法描述VEM的本构关系，解决了VEM的力学特性随温度和频率变化的难点，避免因VEM的复杂本构关系而产生的微分积分方程。算例表明本文给出的建模方法是准确的，ACLD结构能够有效控制结构振动。     

Bi3+对纳米MnO2水热合成的影响研究

在中性和酸性条件下，以MnO2作为锰源，通过水热合成了纳米MnO2，通过XRD和TEM对产物进行的观察表明，在酸性条件下，向溶液中添加一定量的Bi^3 ，产物的晶型由α型向γ型转化，产物形貌由针状、丝状向颗粒状转变。     

Thermomechanical stress fields in high-temperature fibrous composites. I: Unidirectional laminates

This two-part paper presents a closed-form procedure for evaluation of estimates of local thermomechanical stress fields in two-phase fibrous composites and laminates. The first part is concerned with a unidirectional elastic laminate subjected to uniform mechanical loads and to uniform changes in temperature. Both phases are assumed to be elastic, with temperature-dependent moduli and expansion coefficients; the solution reflects the influence of thermomechanical interactions. Exact solutions are not possible for any real system, because the local geometry is not known in detail. Instead, estimates of the fields are found from a modified Mori-Tanaka approximation. Examples are presented for two SiC/Ti---Al---Nb composites. Local stresses of interest are found after cooling from fabrication to room temperature. The presence of local yielding, and the influence of coupling terms on the local stress magnitudes are examined. Extension of the results to laminated plates is presented in Part II (Dvorak, G.J., Chen, T. & Teply, J., Composites Science and Technology, 43 (1992) 359–368, this issue).     

金属－橡胶硫化粘接过程中分子取向行为的间接证据

对金属－橡胶热硫化粘接复合体的剥离行为进行了研究，同一粘接试样的双向１８０°剥离试验显示出了巨大的差异。本文分析了弹性材料在硫化过程中的分子行为，并提出了相应的新假设，认为这是由于金属－橡胶在硫化粘接过程中分子取向交联行为所致。这种双向１８０°剥离破坏现象可被看作是金属－橡胶硫化粘接过程中分子取向行为的间接证据。     

T_C≥400°C高温PTC陶瓷的研制

利用国产原料，采用传统的陶瓷材料制备工艺，研制了居里温度ＴＣ≥４００°Ｃ的高温ＰＴＣ陶瓷，制成了居里温度ＴＣ＝４１２°Ｃ，电阻Ｒ≤１０３Ω，ｌｇ（Ｒｍａｘ／Ｒｍｉｎ）＝４的高性能ＰＴＣ热敏陶瓷材料     

燃煤MHD发电Cr25Al5电极材料的腐蚀行为研究

采用Ｃｒ＿（２５）Ａｌ＿５合金进行煤渣／种子条件下静态腐蚀试验（温度１３７３－１５７３ｋ，时间５０－１５０ｈｒ），试验后得出三种温度下腐蚀重量变化与腐蚀时间的关系，并借助金相显微镜、扫描电镜和俄歇分析进行有关形貌及成份分析，试验表明，温度是材料腐蚀的主要因素，在１４７３ｋ条件下材料的抗蚀性最好，Ａｌ、Ｓｉ元素在腐蚀过渡层中富集，Ｃｒ元素变化不大，但有从基体向外扩散的趋势。由此，这一材料若能进一步改进，可望在控制壁面温度的半热壁型通道中进行试验研究。     

聚吡咯导电材料合成方法的进展

本文对聚吡咯及聚吡咯导电复合物的合成方法进行了综述。     

超细铁粉和氧化铁颗粒的研究

用透射电镜和图像分析仪等研究了超细铁粉和γ-Fe_2O_3粉末的结构、形貌、粒子的平均尺寸以及粒度分布。研究结果表明,多数超细铁粉粒子近似呈球形,并且,铁粉粒子由两相组成,粒子的核心部分是金屑a-Fe,表面的包裹层为氧化物层,它由Fe_3O_4和7-Fe_O_3的混合物组成。氧化层的平均厚度大约占整个粒子直径的20％左右。羰基铁粉粒子(含氧化层)的平均直径为16nm。直径在4～24nm范围的粒子数占总粒子数的91％,而7-Fe_2O_3粉末既有雪茄状粒子,也有小球状粒子。分析表明,球状粒子的平均直径为113nm,雪茄状粒子的平均直径(按<长 宽>/2计算)为148nm。由于超细铁粉粒子很细,且有磁性,制备电镜试样时分散比较困难。本文比较了几种分散方法后,使用了一种较好的分散方法——超声喷管分散法。