化学镀Ni-P合金/TiO2复合膜的耐蚀性研究

在改进常规制备方法的基础上，提出化学镀/溶胶-凝胶复合法在碳钢表面制备TiO2复合膜的新技术。用衍射研究了复合膜的组织形态，采用环境扫描电镜（ESEM）表征了复合膜的表观和断面形貌，用极化电阻、阳极极化曲线测量等方法研究TiO2复合膜在0.5mol/L硫酸和0.5mol/L氯化钠溶液中的耐蚀性能。结果表明A3钢表面的TiO2复合膜耐蚀性能优良。     

Failure analysis of a wire rope

Wire ropes, pulleys, counterweights, and connecting systems are used for auto tensioning of contact wires of electric railways. A wire rope in one such auto tensioning system suffered premature failure. Failure investigation revealed fatigue cracks initiating at nonmetallic inclusions near the surface of individual wire strands in the rope. The inclusions were identified as Al-Ca-Ti silicates in a large number of stringers, and some oxide and nitride inclusions were also found. The wire used in the rope did not conform to the composition specified for AISI 316 grade steel, nor did it satisfy the minimum tensile strength requirements. Failure of the wire rope was found to be due to fatigue; however, the ultimate fracture of the rope was the result of overload that occurred after fatigue failure had reduced the number of wire strands supporting the load.     

烷基化换热器的腐蚀失效分析和防护措施

通过对烷基化车间换热器腐蚀形貌、特征、产物、腐蚀介质、积垢、材料以及换热器流体特性的研究和分析,认为烷基化换热器的腐蚀失效主要由空泡腐蚀和湍流腐蚀引起,并提出了4项防腐蚀措施.经现场应用证明:改变设计或安排辅助管可以有效地减缓冷却管与管板结合部位的严重腐蚀.     

快速评定砂浆配方对钢筋腐蚀的影响

用电化学方法测定砂浆试件中钢筋的极化电阻，并测定了砂浆的孔隙率，结果发现:砂浆的孔隙率、孔径分布与钢筋极化电阻大小有良好的对应关系。电化学方法能可靠、快速测定砂浆配合比、添加剂对钢筋腐蚀速度的影响。     

低压铝箔交流腐蚀研究

在３０Ｈｚ频率下，通过铝箔在ＨＣｌ＋Ｈ２ＳＯ４＋ＨＮＯ３＋Ｈ３ＰＯ４体系中的交流腐蚀，研究腐蚀液组成中腐蚀主体及缓蚀剂对铝箔腐蚀的作用，探讨腐蚀过程中电源频率、腐蚀液温度、电流密度及腐蚀时间对铝箔腐蚀的影响。腐蚀液组成的配比恰当，有利于比容的提高。在特定的频率下采用合适的腐蚀液温度、适宜的电流密度和腐蚀时间可以提高铝箔的静电容量。     

几种高强度钢腐蚀疲劳裂纹扩展行为的研究

本文研究了ＧＣ－４，３０ＣｒＭｎＳｉＮｉ２Ａ和３００Ｍ超高强钢的腐蚀疲劳裂纹扩展行为。考虑了环境，热处理制度，应力比和频率对裂纹扩展的影响。研究结果表明：腐蚀环境和热处理制度对疲劳裂纹扩展有显著影响。在侵蚀性环境中随频率降低，裂纹扩展大幅度上升，随应力比提高，环境影响加剧。利用扫描电镜对试样断口形貌进行了分析，并讨论了高强钢的腐蚀疲劳机理。     

结构陶瓷的高温疲劳强度衰减理论

提出了陶瓷材料疲劳强度衰减理论并由此导出了各种疲劳关系式。建立了疲劳基本方程ｄσ＿ｒ／ｄ＿ｉ＝一Ａσ（ｔ）￣ｎｔ￣（－ｍ），得出了疲劳寿命公式Ｔ＝Ｍ（σ＿０－σ）／Ａσ￣ｎ（静疲劳时Ｍ＝１，连续增载疲劳时Ｍ＝ｎ＋１，循环疲劳时Ｍ＝（ｎ＋１）／（１＋Ｒ＋Ｒ￣２＋……＋Ｒ￣ｎ），逐级加载时，并导出不同疲劳方式下疲劳寿命间的关系。同时，用多种Ｓｉ＿３Ｎ＿４材料在高温中作了论证试验，结果与理论一致。     

13SiMnNiCrMoV钢切口疲劳裂纹萌生门槛值

本文研究在13SiMnNiCrMoV 结构钢中用尖裂纹的应力强度因子来反映三点弯曲缺口试样的疲劳裂纹萌生规律。当 R=0.1,f=100Hz,试样尺寸 B×W×L=12.5×25×117mm 时,缺口名义应力幅的门槛值为Δσ_(th)=3315ρ~(0.352) MPa,0.5mm≤ρ≤5mmΔK_(th)=250ρ~(0.352) MPam~(1/2)门槛值与ρ有关。同时得到缺口裂纹萌生的循环次数 N_i 与名义应力幅Δσ、缺口曲率半径ρ的定量关系是N_i=3.98×10~(22)ρ~(1.62)/Δσ~(4.85),N_i≤10~(5.5)并讨论了(ΔK_1/ρ~(1/2))_(th)与ρ无关的结论。     

柔性纤维混凝土的疲劳特性研究

将柔性纤维掺入水泥混凝土可以大幅度提高混凝土的弯曲疲劳等路用性能,并通过试验建立了柔性纤维混凝土的疲劳方程.结果表明,柔性纤维不但能使混凝土的强度提高,更主要的是可以在重交通条件下,可成倍地提高混凝土的弯曲疲劳寿命.     

Estimation of the Substrate Concentration Profiles in Petroleum Pipelines Containing Biofilms

In industrial systems, the formation of biofilms can cause many problems, such as an increase in the flow resistance of pipelines, energy losses in fluid transport and heat exchangers, product contamination, materials deterioration, and biocorrosion. As a result, biofilms contribute substantially to economic losses in the industry. Corrosion is particularly an issue in the petroleum industry and its implications range from down-hole completion through petroleum processing units. Much of this corrosion is attributed to microbial activities. This paper proposes a mathematical model for predicting substrate concentration for such microbial growth. Substrate concentrations in the system and near the biofilm surface are one of the parameters that has a great effect in determining the extent of the problems associated with biofilms. In this study, a convective-diffusion model under various flow conditions (stagnant, laminar, and turbulent) has been solved using the finite difference technique, employing the alternating direction implicit (ADI) method. The model assumes that a liquid containing substrate and bacteria is flowing in a pipeline with known concentrations at the inlet and then predicts the variation of the transient (as a function of time) substrate concentration along the pipeline and as a function of the pipe radius. The model is then used to predict and estimate the substrate concentration profiles on the biofilm surface under different environmental conditions. A parametric study was also conducted to study the effect of the different parameters influencing the substrate concentration profiles in the system and on the biofilm surface.