Aspects of rapid crack propagation in silicon

Fracture experiments with silicon specimens in recent years have shown the need for a new approach to the analysis of rapidly propagating cracks in single crystals. Behaviour and phenomena have been revealed that fracture in these materials is rather different from the fracture of both amorphous and polycrystalline materials. We show that continuum mechanics is insufficient for analyzing crack propagation in single crystals since it is unable to consider atomistic‐scale phenomena. Accordingly, we describe basic phenomena associated with rapid crack propagation in silicon : (i) anisotropic velocity‐dependent R‐curve behaviour, as a key phenomenon dictating atomistic scale behaviour, (ii) crack deflection from one cleavage plane to another as a mesoscopic scale phenomenon in single‐crystal fracture, (iii) the Rayleigh surface wave speed as the limiting crack tip velocity is re‐examined, (vi) the lowest crack velocity in brittle crystals is examined, and finally (v) the interaction between crack path and preferred cleavage planes in single crystals is depicted.     

Elastoplastic modelling of subsurface crack growth in rail/wheel contact problems

Propagation of small subsurface cracks subjected to shear under repeated rolling contact load is studied. An analytical crack model (Dugdale) with plastic strips at the two crack tips is employed. Compressive stresses promoting crack closure and friction between crack faces are considered. The triaxial stress state is used in the yield criterion. A damage criterion is suggested based on experimental LCF data. In a numerical study, critical crack lengths are found below which propagation of an existing crack should be effectively suppressed.     

Off-axis fatigue cracking behaviour in notched fibre metal laminates

The off‐axis fatigue cracking behaviour of notched fibre metal laminates under constant amplitude loading conditions was investigated experimentally and numerically. It was found that the off‐axis fatigue crack initiation life decreased as the off‐axis angles increased. This indicated that the off‐axis laminates raised the applied stress level in the aluminium (Al) layer and subsequently resulted in earlier cracking in the Al layer. The off‐axis fatigue crack initiation lives of notched fibre metal laminates were predicted using lamination theory and an energy‐based critical plane fatigue damage analysis from the literature. After a crack initiated in the Al layer, it was observed that the crack path angles of the off‐axis specimens were neither perpendicular to the fibre nor to the loading direction. A finite‐element model was established for predicting the crack path angles.     

Crack closure in fibre metal laminates

GLARE is a fibre metal laminate (FML) built up of alternating layers of S2-glass/FM94 prepreg and aluminium 2024-T3. The excellent fatigue behaviour of GLARE can be described with a recently published analytical prediction model. This model is based on linear elastic fracture mechanics and the assumption that a similar stress state in the aluminium layers of GLARE and monolithic aluminium result in the same crack growth behaviour. It therefore describes the crack growth with an effective stress intensity factor (SIF) range at the crack tip in the aluminium layers, including the effect of internal residual stress as result of curing and the stiffness differences between the individual layers. In that model, an empirical relation is used to calculate the effective SIF range, which had been determined without sufficiently investigating the effect of crack closure. This paper presents the research performed on crack closure in GLARE. It is assumed that crack closure in FMLs is determined by the actual stress cycles in the metal layers and that it can be described with the available relations for monolithic aluminium published in the literature. Fatigue crack growth experiments have been performed on GLARE specimens in which crack growth rates and crack opening stresses have been recorded. The prediction model incorporating the crack closure relation for aluminium 2024-T3 obtained from the literature has been validated with the test results. It is concluded that crack growth in GLARE can be correlated with the effective SIF range at the crack tip in the aluminium layers, if it is determined with the crack closure relation for aluminium 2024-T3 based on actual stresses in the aluminium layers.     

Express Method for Estimation of Tensile Strength and Crack Resistance of Brittle Media

The procedure is proposed for estimating the crack resistance and tensile strength of rocks by the results of experiments on disk samples with holes. The gradient approach to the strength problem is employed in processing the experimental data.     

Study on Hot Deformation Cracks of Steel D2 Using Procesing Map

ＳｔｕｄｙｏｎＨｏｔＤｅｆｏｒｍａｔｉｏｎＣｒａｃｋｓｏｆＳｔｅｅｌＤ２ＵｓｉｎｇＰｒｏｃｅｓｉｎｇＭａｐＧａｏＳｈａｎ，ＬｉｕＸｉａｎｇｈｕａ，ＷａｎｇＧｕｏｄｏｎｇＡＢＳＴＲＡＣＴＴｈｅｈｏｔｄｅｆｏｒｍａｔｉｏｎｂｅｈａｖｉｏｒｓｏｆｓｔｅｅｌ...     

Corrosion fatigue short crack growth behaviour in a high strength steel

The influence of an aggressive environment (0.6 M, aerated NaCl solution) on short fatigue crack initiation and growth behaviour has been studied. The study involved three major test series, namely: air fatigue, corrosion fatigue, and intermittent air fatigue/corrosion fatigue. The above tests carried out under fully reversed torsional loading conditions at a frequency of 5 Hz, showed that it was the non-metallic inclusions which took part in crack initiation resulting from debonding at metal matrix/inclusion interface and pitting of inclusions in both air and corrosove environments, respectively. Short fatigue crack growth results in these two environments obtained by using plastic replication technique, indicated a large effect of microstructure i.e. prior austenite grain boundaries. The stage/stages at which the environmental contribution was dominant has been discussed by considering the results achieved from intermittent tests. However, the mechanisms involved in corrosion fatigue short crack growth have also been described in the light of results obtained from futher investigations carried out by conducting corrosion fatigue tests under applied cathodic potential conditions and tests on hydrogen pre-charged specimens under air fatigue and uniaxial tension conditions.     

低合金高强度钢的微观组织和疲劳裂纹扩展行为

用透射电镜观察了３０ＣｒＭｎＳｉＮｉ２Ａ钢等温的微观组织，疲劳裂纹扩展行为、裂纹尖端塑性区和位错结构，结果表明，等温状态组织由马氏体和贝氏体组成。在一个奥氏体晶粒内一般存在四个板条领域、裂纹尖端的塑性区内存在主位错带，疲劳断裂的基本组织单元为板条晶或板条束。裂纹遇到板条束界时方向发生较大偏斜。     

On basic definitions of unified fracture mechanics terminology

The adoption of unified fracture mechanics terminology (UFMT) will promote efficient communication between specialists in different fields of fracture research, harmonization of national and international standards relating to fracture mechanics, and last but not least improvement of the existing methodology for teaching and education in fatigue and fracture. In this paper the definitions of some basic and related terms included in different standards on fracture mechanics terminology are confronted with one another. Alternative definitions of the same terms are offered. By this strategy the author tries to show that the definitions of basic and related terms appropriate for the UFMT should emerge as a consequence of harmonizing a crack model with an actual crack and then both taken together with a fracture model, laboratory test methods, and failure assessment codes.Published in Problemy Prochonsti, No. 1, pp. 17–29, January, 1996.This paper is published as a matter of discussion.     

Measurements of Stress Intensity Factors of an Interface Crack Under Mixed Mode Loading

The optical method of caustics has been utilised to measure both the stress intensity factor for a crack lying along the interface of an aluminium/epoxy bimaterial specimen, and the mode mixity arising from the difference in the elastic properties across the interface. Measurements were carried out by using a novel modification to the method whereby caustics are produced and measured from both sides of the specimen, so compensating automatically for the distortion induced in the specimen due to misaligned loading fixtures. A flat reflective surface across the interface was obtained by adhering a reflective coating to the specimen. Verification that this coating does not affect measurement accuracy was obtained by comparing stress intensity factors measured from coated and uncoated monolithic aluminium specimens where good agreement was found to exist between both measurements.