砖混结构现浇楼板的裂缝分析及预防措施

针对目前多层住宅采用砖混结构现浇钢筋混凝土产生裂缝的情况，分析了其产生原因，提出了预防措施。指出这些预防措施可使裂缝得到有效控制。     

Crack growth in aluminium alloy sheet material under flight-simulation loading

Crack propagation tests were carried out on 2024-T3 sheet specimens to study the effects of omitting low-amplitude cycles from the gust-dominated TWIST load sequence (MiniTWIST) and the removal of small load ranges from the manoeuvre-dominated FALSTAFF load sequence (short FALSTAFF). In other tests high-amplitude loads of TWIST and MiniTWIST were truncated at different levels. The results are compared with data from similar test programmes, including crack initiation. Attention is paid to unstationary crack growth retardation and a transient retardation during initial crack growth started by an artificial crack.     

Microstructure-related fracture toughness and fatigue crack growth behaviour in toughened, anhydride-cured epoxy resins

Fracture toughness and fatigue crack propagation (FCP) of plain and modified anhydride-cured epoxy resin (EP) were studied at ambient temperature. Liquid carboxyl-terminated acrylonitrile-butadiene (CTBN) and silicon (SI) rubber dispersions were used as tougheners for the EP. The morphology of the modified EP was characterized by dynamic mechanical analysis (DMA) and by scanning electron microscopy (SEM). The fracture toughness, K_c, of the compositions decreased with increasing deformation rate. K_c of the EP was slightly improved by CTBN addition and practically unaffected by incorporation of the SI dispersion when tests were performed at low cross-head speed, v. Both modifiers improved K_c at high v, and also the resistance to FCP, by shifting the curves to higher stress intensity factor ranges, ΔK, by comparison with the plain EP. It was established that both fracture and fatigue performance rely on the compliance, J_R, at the rubbery plateau, and thus on the apparent molecular mass between crosslinks, M_c. The failure mechanisms were less dependent upon the loading mode (fracture, fatigue), but differed basically for the various modifiers. Rubber-induced cavitation and shear yielding of the EP were dominant for CTBN, whereas crack bifurcation and branching controlled the cracking in SI-modified EP. The simultaneous use of both modifiers resulted in a synergistic effect for both the fracture toughness at high deformation rate and the FCP behavior.     

Effect of crack-growth mechanism on the prediction of fracture load of adhesive joints

This paper presents observations regarding the cracking behavior of tensile-loaded structural adhesive joints. Experiments showed that fracture occurred by the development and propagation of a damage zone, rather than a single, sharp crack, and that the presence of the adhesive spew fillet did not affect the fracture load of the adhesive joints studied. For joints bonded with the mineral-filled epoxy Cybond 4523GB (American Cyanamid), there was approximately 5 mm of subcritical crack propagation prior to final fracture. Fracture-load predictions based on the initial uncracked geometry made in previous papers were unaffected by this small change in geometry. For joints bonded with the rubber-toughened epoxy Permabond ESP 310, approximately 50 mm of subcritical crack propagation was observed. It was again found that predictions made in previous papers on the basis of the initial geometry gave a good estimate of the final fracture load even though this subcritical crack propagation significantly altered the geometry, and thus the applied energy release rates. The effect of shear deformations of the adherends was also investigated, and it was found that shear deformations could be neglected in engineering calculations for joints subject to remote tensile loading.     

Thermomechanical fatigue—damage mechanisms and mechanism-based life prediction methods

An existing extensive database on the isothermal and thermomechanical fatigue behaviour of high-temperature titanium alloy EVII 834 and dispersoid-strengthened aluminum alloy X8019 in SiC particle-reinforced as well as unreinv conditions was used to evaluate both the adaptability of fracture mechanics approaches to TMF and the resulting predictive capabilities of determining material life by crack propagation consideration. Selection of the correct microstructural concepts was emphasised and these concepts were, then adjusted by using data from independent experiments in order to avoid any sort of fitting. It is shown that the cyclic /-integral (δJ_eff concept) is suitable to predict the cyclic lifetime for conditions where the total crack propagation rate is approximately identical to pure fatigue crack growth velocity. In the case that crack propagation is strongly affected by creep, the creep-fatigue damage parameter δ_CF introduced by Riedel can be successfully applied. If environmental effects are very pronounced, the accelerating influence of corrosion on fatigue crack propagation can no longer implicitly be taken into account in the fatigue crack growth law. Instead, a linear combination of the crack growth rate contributions from plain fatigue (determined in vacuum) and from environmental attack is assumed and found to yield a satisfactory prediction, if the relevant corrosion process is taken into account.     

Asymptotic stress intensity factor density profiles for smeared-tip method for cohesive fracture

The paper presents a computational approach and numerical data which facilitate the use of the smeared-tip method for cohesive fracture in large enough structures. In the recently developed K-version of the smeared tip method, the large-size asymptotic profile of the stress intensity factor density along a cohesive crack is considered as a material characteristic, which is uniquely related to the softening stress-displacement law of the cohesive crack. After reviewing the K-version, an accurate and efficient numerical algorithm for the computation of this asymptotic profile is presented. The algorithm is based on solving a singular Abel's integral equation. The profiles corresponding to various typical softening stress-displacement laws of the cohesive crack model are computed, tabulated and plotted. The profiles for a certain range of other typical softening laws can be approximately obtained by interpolation from the tables. Knowing the profile, one can obtain with the smeared-tip method an analytical expression for the large-size solution to fracture problems, including the first two asymptotic terms of the size effect law. Consequently, numerical solutions of the integral equations of the cohesive crack model as well as finite element simulations of the cohesive crack are made superfluous. However, when the fracture process zone is attached to a notch or to the body surface and the cohesive zone ends with a stress jump, the solution is expected to be accurate only for large-enough structures.     

Characterisation of plasticity-induced closure--crack flank contact force versus plastic enclave

This paper presents some results from a totally new and powerful fusion between automated, digital photoelastic techniques and mathematical analysis of a crack experiencing closure. In essence, real-time photoelastic stress field data is acquired and fitted to a Muskhelishvili complex potential model of a loaded crack experiencing closure. The fit entails optimisation of multiple variables via a memetic algorithm, which combines a genetic algorithm and a local search. From observations made in this work, it is proposed that the plastic enclave around a crack tip will shield the crack from the full influence of the applied stress field. Furthermore, the effects of this ‘back stress’ are overcome by the applied tensile load in a way that, often, cannot be readily correlated with crack contact length, wake contact force, or with compliance.     

双头螺栓失效分析

与汽车电机装配在一起的双头螺栓在拧紧后不久便发生断裂。采用扫描电镜、化学分析、金相检验等方法对失效件进行了检测，同时又进行了氢脆试验验证。结果表明，螺栓在进行表面酸洗及电镀时，氢向金属内部扩散和富集，当氢浓度达到一定临界值后，促使氢致裂纹的产生和扩展。在外应力的作用下，即出现氢脆现象导致螺栓断裂。     

A time series approach to fatigue crack propagation

The inherently nonlinear phenomenon of fatigue crack propagation is modeled as a linear random process. To a first approximation, simple, nonstationary time series models are introduced and standard techniques for determining the parameters of autoregressive integrated moving-average processes are applied. Multiplicative time series models are next utilised for the representation of a group of crack history curves. Implementation of the models on the Virkler experimental data set yields satisfactory results. Reliable Gaussian approximations to the distribution of the time required by a crack to reach a specified critical length are obtained, and the usefulness of the approach is demonstrated when updating lifetime predictions after periodic inspections.     

Oscillatory crack tip triangular elements for finite element analysis of interface cracks

In this paper a special crack tip element has been developed in which displacements and stresses have the same behaviour as those of bi‐material interface cracks with open tips. The element degenerates into a traditional triangular quarter point element in cases of homogeneous cracks. An isoparametric co‐ordinate system (ρ, t) is defined in this study, and numerical techniques using these co‐ordinates to evaluate Jacobian matrices, shape function derivatives, and element stiffness matrices are developed. Also, equations calculating the complex stress intensity factor using displacements are obtained in this study. Numerical results are in good agreement with known analytical solutions in two examples. Copyright © 2003 John Wiley & Sons, Ltd.