用透射电镜观察了３０ＣｒＭｎＳｉＮｉ２Ａ钢等温的微观组织，疲劳裂纹扩展行为、裂纹尖端塑性区和位错结构，结果表明，等温状态组织由马氏体和贝氏体组成。在一个奥氏体晶粒内一般存在四个板条领域、裂纹尖端的塑性区内存在主位错带，疲劳断裂的基本组织单元为板条晶或板条束。裂纹遇到板条束界时方向发生较大偏斜。     

On basic definitions of unified fracture mechanics terminology

The adoption of unified fracture mechanics terminology (UFMT) will promote efficient communication between specialists in different fields of fracture research, harmonization of national and international standards relating to fracture mechanics, and last but not least improvement of the existing methodology for teaching and education in fatigue and fracture. In this paper the definitions of some basic and related terms included in different standards on fracture mechanics terminology are confronted with one another. Alternative definitions of the same terms are offered. By this strategy the author tries to show that the definitions of basic and related terms appropriate for the UFMT should emerge as a consequence of harmonizing a crack model with an actual crack and then both taken together with a fracture model, laboratory test methods, and failure assessment codes.Published in Problemy Prochonsti, No. 1, pp. 17–29, January, 1996.This paper is published as a matter of discussion.     

GH2027铁基高温合金的第二相研究

运用电子显微分析和波谱分析等方法对ＧＨ２０２７合金的第二相进行了研究，结果表明，合金晶界相主要是片状Ｍ６Ｃ和薄膜状Ｍ２３Ｃ６，经波纹图样测得其错配度约为３％，晶内Ｍ６Ｃ和Ｍ２３     

混凝土受拉断裂的破坏机理

本文从试验现象出发,建立了以数理统计为基础的混凝土受拉全过程曲线方程。研究表明,混凝土受拉应力应变全曲线是混凝土试件内部的粘结界面与水泥胶合物在外拉力作用下逐步断裂造成的。文章所建立的方法不仅可以解释许多试验现象,模拟混凝土受拉全曲线,而且还可以得出试验中难以测出的结果。     

Measurements of Stress Intensity Factors of an Interface Crack Under Mixed Mode Loading

The optical method of caustics has been utilised to measure both the stress intensity factor for a crack lying along the interface of an aluminium/epoxy bimaterial specimen, and the mode mixity arising from the difference in the elastic properties across the interface. Measurements were carried out by using a novel modification to the method whereby caustics are produced and measured from both sides of the specimen, so compensating automatically for the distortion induced in the specimen due to misaligned loading fixtures. A flat reflective surface across the interface was obtained by adhering a reflective coating to the specimen. Verification that this coating does not affect measurement accuracy was obtained by comparing stress intensity factors measured from coated and uncoated monolithic aluminium specimens where good agreement was found to exist between both measurements.     

f—x域内提高地震资料的信噪比

在 f-x 域,地震记录可以表示成有限个调频调幅正弦波的叠合,叠合的结果是一个连续且光滑的函数。我们可以用一个简单的 n 次多项式去逼近这个函数。本文提出了一种在 f-x 域用最小平方拟合原理消除随机噪声的新方法,并证明了在噪声为自噪以及空间采样足够密的条件下,拟合结果与噪声无关,即 f-x 域最小平方拟合处理可以有效地消除记录上的随机白噪,而对有效信号的破坏甚微。由于理论上允许振幅值及同相轴形态在空间上发生变化,因而该方法不具有混波作用,是高分辨率处理的理想工具。     

光孤子相互作用对压缩态的影响

在线性近似条件下，量子化了非线性薛定谔方程，用后向传播法数值求解了光孤子相互作用对压缩比的影响。数值结果表明，在碰撞距离附近，压缩比显著增加。     

几种高强度钢腐蚀疲劳裂纹扩展行为的研究

本文研究了ＧＣ－４，３０ＣｒＭｎＳｉＮｉ２Ａ和３００Ｍ超高强钢的腐蚀疲劳裂纹扩展行为。考虑了环境，热处理制度，应力比和频率对裂纹扩展的影响。研究结果表明：腐蚀环境和热处理制度对疲劳裂纹扩展有显著影响。在侵蚀性环境中随频率降低，裂纹扩展大幅度上升，随应力比提高，环境影响加剧。利用扫描电镜对试样断口形貌进行了分析，并讨论了高强钢的腐蚀疲劳机理。     

13SiMnNiCrMoV钢切口疲劳裂纹萌生门槛值

本文研究在13SiMnNiCrMoV 结构钢中用尖裂纹的应力强度因子来反映三点弯曲缺口试样的疲劳裂纹萌生规律。当 R=0.1,f=100Hz,试样尺寸 B×W×L=12.5×25×117mm 时,缺口名义应力幅的门槛值为Δσ_(th)=3315ρ~(0.352) MPa,0.5mm≤ρ≤5mmΔK_(th)=250ρ~(0.352) MPam~(1/2)门槛值与ρ有关。同时得到缺口裂纹萌生的循环次数 N_i 与名义应力幅Δσ、缺口曲率半径ρ的定量关系是N_i=3.98×10~(22)ρ~(1.62)/Δσ~(4.85),N_i≤10~(5.5)并讨论了(ΔK_1/ρ~(1/2))_(th)与ρ无关的结论。     