脉冲电流处理对一种镍基耐蚀合金腐蚀行为的影响

将脉冲电流处理应用于一种镍基耐蚀合金的时效过程,研究脉冲电流对合金显微组织及耐蚀性的影响规律及机理。结果表明,脉冲电流处理后,合金在力学性能基本保持不变的前提下,其耐晶间腐蚀性能得到显著提高。脉冲电流能够显著提高合金元素的界面扩散速度,其界面扩散速度远快于体扩散速度,晶界M23C6型碳化物呈典型的不连续析出转变特征。与常规时效处理相比,脉冲电流处理后晶界碳化物的不连续析出转变,使晶界位置的合金元素的贫化程度大幅度降低,在保证合金力学性能的前提下,显著改善合金的耐晶间腐蚀能力。     

Use of EBSD to study electropulsing induced reverse phase transformations in a Zn-Al alloy (ZA22)

Multi‐phase identification and phase transformations in electropulsing treated Zn–Al based alloy wire specimens were studied using electron back‐scattered diffraction, back‐scattered scanning electron microscopy and X‐ray diffraction techniques. By using electron back‐scattered diffraction, two phases: η′_S and η′_T with a small difference of about 1% in lattice parameters (c₀/a₀) were identified, based on the determined lattice parameters of the phases, and the reverse eutectoid phase transformations: η′_T+?′_T+α′_T→η′_S and ?+α→T′+η were successfully detected. Electron back‐scattered diffraction appeared to be an effective technique for studying complex electropulsing induced phase transformations.     

脉冲电流作用下40Cr钢淬火残余应力的消除

研究了脉冲电流作用下40Cr钢淬火残余应力的消除.结果表明,当脉冲电流密度达到一定数值后,材料中的残余应力开始部分弛豫;当电流密度达到6.3 kA/mm2时,残余应力可在700μs的脉冲电流处理时间内完全消除,而试样的瞬时温升仅约为360℃.在脉冲电流作用下残余应力弛豫的主要原因,可能是电流的电致塑性效应降低了材料的屈服强度,试样在由快速加热产生的瞬时热压应力和残余应力的共同作用下发生了微量的塑性变形.     

电脉冲时效对Fe14Mn6Si8Cr5Ni合金微观组织及形状记忆效应的影响

研究了电脉冲时效对Fe14Mn6Si8Cr5Ni合金微观组织及形状记忆效应的影响。研究结果表明预变形后的合金经电脉冲时效其形状记忆效应提高幅度比不预变形合金电脉冲时效幅度大。10%拉伸预变形合金经电脉冲时效1s,其形状回复率便提高到(70.3±1.0)%;时效300s,其形状回复率提高到(87.5±1.0)%,比固溶态合金提高了82.3%,而不预变形直接电脉冲时效合金只比固溶态合金提高了22.3%。经金相和TEM分析,预变形后电脉冲时效的合金中已无热诱发ε马氏体出现,这使得基体奥氏体增多;同时电脉冲能促使预变形时引入的空位和位错迅速崩塌形成层错。正是这两方面的原因使得预变形后电脉冲时效能迅速地提高合金的形状记忆效应。     

电脉冲对金属材料性能的影响

电脉冲处理能提高金属材料的塑性变形能力,促进合金的再结晶过程,细化合金的凝固组织,提高材料的综合力学性能,并对金属材料的其他性能有显著影响。电脉冲处理作为一种材料制备和性能改善的研究方法,在材料研究领域有着广阔的应用前景。为此,介绍了电脉冲处理在上述领域的研究进展情况。     

Characterisation of electric current-treated austenite using misorientation angle distributions in martensite

ABSTRACT

The angle misorientation distribution of martensite formed from electric current treated and non-treated austenite samples are studied using electron backscatter diffraction. The electric currents are pulsed with a loading width of 80 μs, at a frequency of 100?Hz and current density of 4.21 A/mm² supplied by a DC Voltage. The majority of angle misorientations are < 5° and exist within the martensite grains, while only a minority of all misorientations are derived from the prior austenite grain boundary and were found to lie in the range 20–50°. Distinct textures develop in both electric current treated and non-treated samples with increased quenching temperature. Analysis of the prior austenite shows reduced grains in the electric current treated samples at all quenching temperatures considered.

This paper is part of a themed issue on Materials in External Fields.     

电脉冲辅助超声冲击技术对焊缝残余应力及显微硬度的影响

焊接结构件中存在焊接残余应力,使得焊接构件在使用过程中容易发生断裂,缩短构件的使用寿命.以D36钢焊缝为研究对象,使用电脉冲辅助超声冲击技术处理D36钢焊接件,研究了电脉冲辅助超声冲击技术对焊缝残余应力和显微硬度的影响.研究结果表明:电脉冲辅助超声冲击技术在适当的电流密度和处理时间下消除焊接残余应力和表面强化的作用优于传统的单一超声冲击技术,不仅能够比单一超声冲击技术降低焊缝的残余应力最多达23 MPa,提高焊缝表层的最大硬度达109HV,同时增加强化层深度最多达250μm.     

电脉冲退火处理对Fe-Si-B非晶原子结合力的影响

非晶态合金Fe78Si9B1 3样品经短时超短脉冲电流处理 ,发生了结构弛豫 ,用DTA方法及Kissinger方程计算非晶样品的晶化激活能 ,用穆斯堡尔谱学方法研究了试样在电脉冲处理后的无反冲分数的变化 .结果表明 ,随脉冲电流密度和脉冲频率的增加 ,样品的晶化激活能降低 ,穆斯堡尔无反冲分数下降 ,表明原子间结合力随电流密度和脉冲频率的增加趋向降低     

脉冲电流处理后低碳钢中的局域纳米结构

用透射电镜观察经过高密度脉冲电流处理后的粗晶低碳钢,发现该材料中有纳米结构的γ-Fe生成。讨论了纳米结构的生成机制。脉冲电流作用时间短,加热速度快,改变相变势垒的效应和快速冷却的条件是生成纳米结构的原因,电流降低热力学形核势垒是一个不容忽视的因素。