An improved method for the determination of starch by sequential hydrolysis with thermostable bacterial α-amylase and fungal amyloglucosidase is described. Glucose was determined colorimetrically by a glucose oxidase-peroxidase-chromogen system at pH 7. Native normal and waxy starches, and distarch phosphate, gave quantitative yields of glucose with a high degree of precision (coefficient of variation less than 1%). Acetylated distarch phosphate, high-amylose starch and retrograded amylose were initially treated with 1M NaOH for 30 min, then neutralised and analysed successfully as normal starch. Oxidised starch did not give a quantitative yield of glucose because of the presence of dicarboxylic groups in the polymer. For samples containing normal and waxy starch the analysis was carried out in about 4 h. The method was applied to a range of starch-containing foodstuffs and the results are reported.     

MBS树脂改性PVC的研究

研究了不同类型及用量的MBS树脂对PVC抗冲击性、光学性能、拉伸性能及加工塑化性能的改性效果以及加工条件等因素的影响。结果表明 :在低用量条件下 ,随MBS树脂含量增加 ,MBS/PVC抗冲击性能有所提高 ,光学性能略有下降。此外 ,MBS/PVC制品的拉伸性能和加工性能受MBS树脂类型及用量影响不大。     

修正步冷温度曲线试验研究

按修正步冷温度曲线对经步冷脆化的 2 .2 5Cr 1Mo和在加氢反应器内运行 5a的 2 2 5Cr 1Mo试块进行了修正步冷试验 ,评定了材料的回火脆性。结果表明 ,按修正步冷曲线进行修正步冷试验能使已经脆化的材料进一步脆化 ,为加氢反应器材料损伤的研究提供了一条途径。     

异丁烷与丁烯在炭化树脂负载PW_(12)催化剂上的烷基化

探讨了炭化树脂负载杂多酸PW1 2 催化剂制备的适宜条件 ,反应工艺条件对催化剂催化异丁烷与丁烯烷基化反应及产物分布的影响 ,分析了催化剂具有较高活性的原因 ,进行了催化剂稳定性实验。并与其它类固体酸催化剂进行了对比。     

耐高温绝缘GFRP管的真空辅助树脂传递成型工艺研究

阐述了耐高温绝缘GFRP管的成型工艺及原材料选择，并对影响成型工艺的主要因素作了理论分析及试验验证。研究表明，以TDE－85／DDS体系为为基体，以无碱无捻玻璃纤维方格布为增强材料，用VARTM工艺成型的石油勘探高性能平衡管完全满足技术要求。     

硫脲型整合树脂在分析上的应用 Ⅰ.岩样中微量银的中子活化分析

前言银和其他贵金属元素一样,在地壳中比较稀少,按其自然丰度为第67号元素,平均含量仅0.07 ppm。由于地质样品成分非常复杂,为测定其微量银,必须进行严格的化学分离。但是迄今文献中报道的许多分离分法,步骤都相当冗长,一般采用氯化银反     

苯基荧光酮分光光度法测定聚烯烃树脂中的钛

应用苯基荧光酮 -聚乙烯醇 -Tween -80显色体系测定了聚烯烃树脂中的钛 ,建立了测定聚烯烃树脂中钛离子的灵敏、快速的分析方法。考察了测定条件 ,在测定过程中 ,以抗坏血酸还原作用消除了Fe3+ 、V5+ 等干扰。配合物最大吸收波长为 5 3 5nm ,其表观摩尔吸光系数ε =1 0× 10 5L/ (mol·cm) ,线性范围为 0～ 0 12 μg/ml。合成试样回收率为 97 3 %～ 10 1% ,相对标准偏差不大于 1 63 % ;加标回收率为 99 95 %～ 10 1 3 % ,该方法选择性高 ,准确性好 ,简便易行     

超强吸水树脂的吸水性能研究

对自制的超强吸水树脂的吸收性能进行了研究，分别考察了吸水树脂的粒径，溶液的pH值，几种离子如Na^ ,K^ ,Ca^2 ,Mg^2 等的水溶液对吸水树脂吸收性能的影响。实验结果表明，在pH为6－8，树脂粒径为100mesh-120mesh时，树脂的吸水性能最好，各种离子对吸水树脂吸收性能的影响大小顺序为：Na^ ＜K^ ＜Mg^2 ＜Ca^2 。     

偶联剂处理硅灰石填充不饱和聚酯树脂的研究

对针状硅灰石 (L∶D≥ 10∶32 5目 )提纯后 ,采用偶联剂进行表面处理 ,将硅灰石按不同比例填充于不饱和聚酯树脂体系中 ,研究了材料的性能。结果表明 ,改性后的硅灰石可显著改善不饱和聚酯的性能。     

Formation and investigation of epoxy intumescent compositions modified by active additives

Results are reported of research on intumescent composites based on epoxy resin cross‐linked with polyethylene polyamine and containing ammonium polyphosphate and such modifying additives as calcium borate, manganese dioxide, nickel, and chromium, containing tubulenes as gas‐formers and carbonization stimulators. The changes in composition and physicochemical properties of modified compositions under conditions of heat and fire were investigated by X‐ray photo‐electron spectroscopy, atomic force microscopy, and local force spectroscopy. Ammonium polyphosphate mainly stimulates carbonization processes on the inner surface of a bubble being formed during foam coke formation. The introduction of metal‐containing tubulenes leads to the formation of fire‐retardant and low flammability‐compositions with high coke and carbon structures content. The use of calcium borate in the compositions considerably increases the strength of foam coke being formed. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 85: 1477–1483, 2002