流量比对等离子体基团分布和薄膜结构的影响

使用光强标定的发射光谱(AOES)测量了CHF3／C6H6混合气体的微波电子回旋共振(ECR)放电等离子体中基团的分布状态。实验发现随着CHF3流量的增加，成膜基团CF、CF2、CH等的相对密度增大，而刻蚀基团F的密度也会增加，从而使得a—C：F薄膜的沉积速率降低。同时红外吸收谱(IR)分析表明，在高CHF3流量下沉积的a—C：F薄膜中含有更高的C—F键成分。可见在a—C：F薄膜的制备中CHF3／(CHF3 C6H6)流量比是重要的控制参量。     

铝薄膜CMP影响因素分析

提出了在碱性抛光液中铝薄膜化学机械抛光的机理模型,对抛光液的pH值、磨料、氧化剂浓度对过程参数的影响做了一些试验分析。试验结果表面粗糙度的铝薄膜所需的最优化CMP过程参数:硅溶胶粒径为15～20nm,pH值为10.8～11.2,氧化剂浓度为2.5%～3%。     

BaxSr（1—x）TiO3多层膜椭偏光谱研究

用溶胶－凝胶技术在Bi(100）衬底上制备了单层和渐变型多层的BaxSr(1-X)TiO3薄膜，其膜层组分分别为：Ba0.7Sr0.3TiO3,Ba0.8Sr0.2TiO,Ba0.9Sr0.1TiO3,BaTiO3，对生长制备出的多层BaxSr(1-X)TiO3薄膜进行了变角度椭偏光谱测量，通过椭偏光谱解谱分析研究，首次得到了BaxSr(1-X)TiO3多层膜结构不同膜层的膜厚和光学常数，其结果显示：椭偏光谱分析得到的不同膜层的膜厚与卢瑟福背向散射测量得到的结果基本相符；渐变型多层膜中BaTiO3薄膜的折射率比单层BaTiO3薄膜折射率大许多，与体BaTiO3的折射率相接近，这说明渐变型多层膜中BaTiO3薄膜的光学性质与体材料的光学性质接近。     

Simulations of Temperature Field in HFCVD Diamond Films over Large Area

A three-dimensional model was developed to investigate the influence of various hot filaments parameters on substrate temperature fields that significantly affect the nucleation and growth of diamond films over large area by hot-filament chemical vapordeposition (HFCVD). Numerical simulated results indicated that substrate temperature varies as a function of hot filamentsnumber, radius, temperature, emissivity, the distance between filaments, and the distance between substrate and filamentsarrangement plane. When these filaments parameters were maintained at the optimal values, the homogeneous substrate temperature region of 76 mm×76 mm with the temperature fluctuation no more than 5% could be obtained by a 80 mm×80 mmhot filaments arrangement plane. Furthermore, the homogeneous region could be enlarged to 100 mm×100 mm under thecondition of supplementary hot filaments with appropriate parameters. All of these calculations provided the basis for speciallyoptimizing the hot filaments parameters to dep     

二氧化锡溅射工艺研究

SnO2 是最早使用也是目前使用最广泛的一种气敏材料 ,使用该材料设计制作的气敏传感器具有许多优点。在简要介绍溅射镀膜的成膜过程和特点的基础上 ,着重介绍了SnO2 膜的制备流程 ,分析了功率和温度变化对成膜质量的影响     

Investigation into polishing process of CVD diamond films

A new technique used for polishing chemical vapor deposition (CVD) diamond films has been investigated, by which rough polishing of the CVD diamond films can be achieved efficiently. A CVD diamond film is coated with a thin layer of electrically conductive material in advance, and then electro-discharge machining (EDM) is used to machine the coated surface. As a result, peaks on the surface of the diamond film are removed rapidly. During machining, graphitization of diamond enables the EDM process to continue. The single pulse discharge shows that the material of the coated layer evidently affects removal behavior of the CVD diamond films. Compared with the machining of ordinary metal materials, the process of EDM CVD diamond films possesses a quite different characteristic. The removal mechanism of the CVD diamond films is discussed.     

L－B膜修饰电极循环伏安行为模拟──（Ⅰ）电荷转移速度常数对循环伏安性能的影响

本文用计算机数字模拟方法研究了电活性分子多层Ｚ型Ｌ－Ｂ膜修饰电极的循环伏安行为。计算了电极与修饰Ｌ－Ｂ膜分子第一层之间的电荷转移速度常数Ｋ_ｏ，Ｌ－Ｂ膜分子层间的电荷转移速度常数ｋ_ｉ；对峰电位差△Ｅ_ｐ及阳极峰面积Ｑ的影响，以及在不同条件下各层分子的氧化态分数随扫描时间的变化。为研究和设计电活性分子修饰电极的实际体系提供了大量数据和信息。     

微型真空力敏器件的研究

本文首次用电荷模拟法计算了真空微电子力敏传感器的场致发射阴极与阳极间的电场分布,同时计算了<100>晶向的方形硅薄膜受压形变与压力的关系,进而得出了这种传感器的电流-压力曲线.还做了水槽模拟电场分布的实验,理论与实验符合的很好.     

水溶性防氧化剂在SMT用印制板上的应用

水溶性的防氧化剂是一种有机可焊性保护剂。其方法是在印制板完全阻焊、字符层的印刷，并经电检之后，通过表面浸渍在裸铜的贴片位或通孔内形成一种耐热性的有机可焊性膜层。这种有机、可焊、耐热的膜层，膜厚可达0.3-0.5mm，其分解的温度可达约300℃，传统的印制板的热风整平法亦无法满足QFP愈来愈密集的需求，同时也无法满足SMD表面平整度的要求，更无法适应PCB薄型化生产。烷基苯并咪唑的OSP法能弥补这项缺陷，因而在PCB业乃至SMT产业中得到了广泛的应用。     

预处理工艺对硬质合金与金刚石膜间粘结力的影响

在两种经不同预处理的硬质合金YG8基底上，采用微波等离子体化学气相沉积法，在微波功率2kW，压强4.0kPa和6.5kPa，CH4和H2流量分别为1.6cm/s和100.0cm/s的条件下生长金刚石薄膜。利用X射线衍射检测了金刚石薄膜是否存在，用拉曼光谱分析了薄膜的质量，用金相显微镜观察了薄膜的洛氏硬度压痕，标定并比较了不同预处理工艺膜与基底的结合力。实验结果表明，不同的预处理方法对于粘结力的影响不大，最主要的因素是钴含量的多少。