Improvement in Stress Corrosion Crack Growth Resistance of an Austempered Cast Steel by a Novel Two-Step Austempering Process

An investigation was carried out to examine the influence of microstructure on the stress corrosion cracking (SCC) growth behavior of an austempered high-carbon (1.00%), high-silicon (3.00%), and high-manganese (2.00%) cast steel. Compact tension specimens were prepared from this cast steel as per American Society for Testing Materials standard E-399 and were given four different heat treatments to produce different microstructures. The SCC behavior of these specimens was studied in 3.5% NaCl solution. The test results indicate the K_ISCCvalue of the material increases as the austenite content increases. Significant improvement in SCC resistance was achieved by using a novel two-step austempering process. Intergranular crack growth was observed in all these specimens.     

复合内衬在燃油加热炉中的应用

对导热油加热炉炉壁温度升高的原因进行了分析,介绍了新型复合内衬的特点,并对其技术特点、施工工艺及应用效果进行了简单阐述。     

两栖装甲装备新型防腐材料的研究

沿海地区特殊海洋环境造成装甲装备的严重腐蚀,为了研制一种新型的耐蚀有机涂层,该文作者研究了有机硅改性环氧树脂的化学反应,并对改性树脂的性能进行了测试分析.结果表明,改性树脂克服了环氧树脂的耐温性差、亲水性强以及盐水渗透率高的性能缺陷,为进一步制备该地区装甲装备防腐涂料奠定基础.     

腐蚀环境中海工混凝土抗氯离子侵蚀性

模拟我国南方沿海浪溅区和水位变动区的海工钢筋混凝土结构物的腐蚀环境，对掺入粉煤灰和矿渣的混凝土抗氯离子侵蚀性进行了试验。结果表明，在水灰比相同的条件下，加掺和料的混凝土抗氯离子侵蚀性高于普通混凝土。     

基于缺陷评估的海底管道设计研究

针对海底管道的裂纹和腐蚀两种主要缺陷,研究了基于缺陷评估的海底管道设计方法,建立了基于缺陷评估的海底管道设计步骤。     

Corrosion Control by water‐soluble extracts from leaves of economic plants

Water extracts from leaves of date palm, phoenix dactylifera, henna, Lawsonia inermis, and corn, Zea mays, were tested as corrosion inhibitors for steel, aluminum, copper and brass in acid chloride and sodium hydroxide solutions using weight loss, solution analysis and potential measurements. The inhibition action was found to critically depend on metal type and solution composition. Only, date palm and henna extracts were found highly effective in reducing corrosion rate of steel in acid chloride solutions and aluminum in sodium hydroxide solutions. The inhibition efficiency increased with increasing the concentration of the extract. The inhibition was interpreted in terms of chemisorption of some active ingredients in the leaves according to Temkin isotherm.     

液化气铜片腐蚀原因及解决措施

本文就引起液化石油气（LPG）铜片腐蚀不合格的原因进行了分析，对JX－1A精脱硫剂工业应用效果进行了探讨，结果表明JX－1A精脱硫剂在解决了LPG铜片腐蚀不合格方面有很好的效果。     

含氮杂环季铵盐缓蚀剂在CO2-3%NaCl溶液体系中的电化学行为

为控制CO2腐蚀，合成了含氮杂环季铵盐缓蚀剂9912-1，通过电化学实验，研究了该缓蚀剂在CO2-3％NaCl-H2O体系中对碳钢于25℃和90℃下的缓蚀行为。实验结果与挂片失重法测试的结果基本一致。低温下缓蚀效果优于高温下的缓蚀效果。而且该缓蚀剂与硫脲有很好的协同效应。Tafel曲线表明，该缓蚀过程是以控制阴极腐蚀为主，并对其缓蚀机理进行了初步探讨。     

焦化加热炉空气预热器腐蚀结垢与预防

空气预热器运行的好坏直接影响到加热炉的热效率 ,文章结合焦化装置加热炉空气预热器的使用、维修、改进等 ,论述了预热器存在的露点腐蚀问题。同时提出从设计、操作、设备等方面采取有效措施 ,保障预热器的长周期高效运行。     

Corrosion behavior of NiCrMo Alloy 625 in high temperature, hydrogenated water

The corrosion behavior of NiCrMo Alloy 625 (UNS N06625) has been characterized in a 10,000 h test conducted in hydrogenated water at 260 °C. The corrosion kinetics were observed to be parabolic, the parabolic rate constant being determined by chemical descaling to be 0.074 mg dm⁻² h^−1/2. Characterizations of the corrosion oxide layer via grazing incidence X-ray diffraction and X-ray photoelectron spectroscopy in combination with argon ion milling and target factor analysis, revealed the presence of two spinel oxide phases and significant amounts of recrystallized nickel. Based on the distribution of three oxidized alloying constituents (Ni, Cr, Fe) with respect to depth and oxidation state, it was concluded that: (a) corrosion occurs in a non-selective manner, but significant amounts of nickel(II) ions are released to the water, and (b) the spinel oxides exist as a chromite-rich inner layer (Ni_0.7Fe_0.3)(Cr_0.8Fe_0.2)₂O₄ underneath a coarser, ferrite-rich outer layer (Ni_0.9Fe_0.1)(Cr_0.1Fe_0.9)₂O₄. The trivalent cation distribution in each of these phases appears to represent a solvus in the immiscible NiCr₂O₄-NiFe₂O₄ binary.