Based on reactive air brazing (RAB), we designed a new type of sealant (Ag–xCuAlO₂) for joining 3 mol.% yttria-stabilized zirconia (YSZ) ceramics and AISI 310S stainless steel. The CuAlO₂ content affected the wettability of the sealant on the YSZ surface, and the joints had a high shear strength when Ag–2 wt.%CuAlO₂, which had a small contact angle on the YSZ substrate, was used as the sealant. In addition, the thickness of the oxide layer was reduced compared to that for the Ag–CuO sealant. The effects of the processing parameters on the microstructure and shear strength of the joints were investigated, and the as-brazed joints reached their highest shear strength (93.7 MPa) when brazed at 1040 °C for 30 min. After high-temperature oxidation at 800 °C for 200 h, the shear strength of the joints remained at 50 MPa, and no apparent change in the microstructure was observed, proving that the joints possessed excellent oxidation resistance.     

Effects of corrosion in liquid fluoride salt on the tensile strength of domestic SiC fibers

The relationship between the tensile strength of corroded domestic second-generation (2ed-gen) SiC fibers at various temperatures for 500 h in 46.5LiF-11.5NaF-42.0KF (mol. %) eutectic salt and the typical microstructure was studied. Weibull theory was used to analyze the critical defects that caused the tensile fracture, and the microstructure of fibers before and after corrosion was characterized. It is concluded that the decrease of tensile strength after corrosion at 800 °C is caused by the surface injury of fibers, which led to the shift of critical defects from the internal defects of virgin fibers to surface defects. Moreover, corrosion at higher temperature accelerates the corrosion process and dissolve the surface O-contained layer thoroughly. This shifts the critical defects back to the internal defects and will be helpful for the recovery of tensile strength of corroded fibers at the higher temperature.     

Omega-6支撑身体，Omega-3支撑大脑：均衡摄入对儿童大脑发育的影响（网络首发、推荐阅读）

人体大脑和身体的发育，需要从食物中摄取均衡的营养物质。人类大脑是区分人类和其他动物的特征。食物中的必需脂肪酸是机体组织结构和功能的必要组成部分。Omega-6（O6）亚油酸（LA6）是皮肤组织的组成成分，且是炎症、血栓形成、免疫和其他信号分子的前体；Omega-3（O3）α-亚麻酸（ALA3），特别是其长链代谢产物——二十二碳六烯酸（DHA3），是大脑、视网膜和部分神经组织中的关键组分。从富含LA6脂肪酸（缺乏O3脂肪酸）的植物籽中提取出的廉价而优质油脂，是20世纪的西方国家食品工业生产的主要脂肪来源。在代谢通路中，高浓度的LA6脂肪酸可拮抗O3脂肪酸代谢，造成O3脂肪酸不足，因此，在给怀孕动物的饲料中，只提供富含LA6但缺乏O3脂肪酸的油脂作为唯一的脂肪来源，会导致幼崽大脑发育不良。过去20~30年的研究表明，低含量LA6且含DHA3的油脂可改善大脑的功能。近年来的研究较多集中在营养因素对大脑发育的影响，最新研究数据表明，脂肪酸平衡对营养不良儿童的大脑发育尤为重要。世界卫生组织（WHO）越来越重视大脑的营养健康，通过其下属的食品法典委员会，建议用于治疗严重急性营养不良儿童的即食治疗食品中，使用含有均衡脂肪酸组成/构成的脂肪。同样，脂肪酸均衡对老年人可能也很重要。目前，业界已经有了调整油脂成分的方法，以确保脂肪酸均衡，从而维持人体整个生命周期的大脑健康。     

高效液相色谱法测定多环芳烃的出峰顺序探讨

目的探讨水﹑气﹑土壤中多环芳烃检测标准(HJ 478-2009﹑HJ 647-2013、HJ 784-2016)的正确出峰时间和顺序。方法用高效液相色谱来对苊烯、芴、苊、?、苯并(a)蒽进行定性分析,并与3个标准中的出峰顺序进行比较。结果苊烯、苊、芴、苯并(a)蒽、?的出峰时间分别为6.450、7.923、8.233、17.760、18.740min,与标准HJ478-2009﹑HJ647-2013的出峰顺序存在差异。结论在使用标准HJ478-2009﹑HJ647-2013、HJ 784-2016同时测定16种多环芳烃时,多环芳烃的出峰顺序及时间应以HJ 784-2016为准。     

Ergonomically based design of tractor control tools

Musculoskeletal injuries are well-known disorders among the agricultural tractor operators. Overexertion is a critical factor which can agitate these injuries. Physical body characteristics should be measured for an ergonomically best-fit-optimal design for the operators. In this study, a designed setup was employed to derive the applied forces by tractor operators on the control tools. The different muscle strengths including leg/foot strength, hand push/pull strength, and torque strength applied by both hands were measured. A comparison was made for the obtained values for different strengths by considering the effects of hand dominance. The obtained data were used to estimate the maximum allowed forces in these tools. In contrast to the previous studies, the minimum allowed actuating forces of the pedals were calculated using reasonable assumptions. These values could provide more comfort and less exhaustion for the tractor operators. The obtained ranges were benchmarked against corresponding recommended values in some standards (ISO, ISIRI, and ASABE family). The results revealed the unsuitability of evaluated standards for a proper design and the excessive overestimation of those recommended values (in some cases more than 3 times). In all of the design procedure, a suitable attention was paid to accommodate it with more than 90% of target population.Relevance to industryA prosperous industry which considers ergonomic factors in the design of agricultural machine workplace can overcome the disorders and generate more comfort. Evaluating more exact mechanical forces can result in a suitable design of workplace.     

A single-phase algorithm for mining high utility itemsets using compressed tree structures

Mining high utility itemsets (HUIs) from transaction databases considers such factors as the unit profit and quantity of purchased items. Two-phase tree-based algorithms transform a database into compressed tree structures and generate candidate patterns through a recursive pattern-growth procedure. This procedure requires a lot of memory and time to construct conditional pattern trees. To address this issue, this study employs two compressed tree structures, namely, Utility Count Tree and String Utility Tree, to enumerate valid patterns and thus promote fast utility computation. Furthermore, the study presents an algorithm called single-phase utility computation (SPUC) that leverages these two tree structures to mine HUIs in a single phase by incorporating novel pruning strategies. Experiments conducted on both real and synthetic datasets demonstrate the superior performance of SPUC compared with IHUP, UP-Growth, and UP-Growth+ algorithms.     

Toughness enhancement and equivalent initial fracture toughness of cementitious composite reinforced with aligned steel fibres

Based on theoretical analysis and numerical simulation, the impact of steel fibres on the stress intensity factor (SIF) at the crack tip for cementitious composite was studied. The enhanced toughness of steel fibre reinforced cementitious composite (SFRC) in resisting cracks was explained by the decrement of SIF caused by steel fibre inclusions at the crack tip of the composite. The equivalent initial fracture toughness was used to characterize the crack initiation of SFRC. A simplified method for determining the of SFRC was proposed based on a linear regression method. Fracture tests were conducted on three‐point bending notched beams with different steel fibre volume fractions and specimen sizes to study the crack initiation behaviour of aligned steel fibre reinforced cementitious composite (ASFRC). of ASFRC was calculated, and the size effect of was analysed. The results showed that slightly increased with the steel fibre volume fraction and gradually became stable. For the tested specimens, whose heights varied between 40 and 100 mm, the specimen size had little impact on the .