Two-component modified polyurethane sealant for insulating glass: Design,preparation, and application

A new two-component modified polyurethane (PU) sealant was designed and synthesized for insulating glass. This sealant was designed based on a crosslinked reaction between a p-chlorophenol-blocked PU pre-polymer (Pre-polymer 2 ) in Component A and a poly-functional hyperbranched polyamine polymer (polyamide resin 300^#) in Component B. During the synthesis of Pre-polymer 2 , Fourier transform infrared spectral analysis was used to track the process, and the optimal reaction time and temperature were 1.5 h and 80 °C, in the presence of 4, 4′-diphenylmethane diisocyanate (MDI). Different curing agents also used as deblocking agents were screened and it was found that polyamide resin 300^# was a good candidate for the curing reaction. In addition, the low-temperature curing rate was also improved by using dibutyltin dilaurate (DBTDL) and organobentonite together as a composite catalyst. Finally, the prepared two-component modified PU sealant for insulating glass was successfully used in an assembly line with good performance. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 48219.     

激光测厚技术在液晶玻璃基板生产中的应用

在液晶玻璃生产过程中,采用激光测厚技术不仅可以大幅度提高玻璃基板品质厚度的测量频率,实现每片基板玻璃厚度一次测量;同时也能反映玻璃基板品质厚度实时的真实性,加快厚度异常对策效率,而且能有力的推动我国光电产业技术及玻璃基板品质的提升。以玻璃基板厚度为研究对象,对激光测厚系统在液晶玻璃基板中的应用进行分析。     

玻璃纤维增强聚丙烯微孔注塑发泡成型

对不同填充形式下的3种聚丙烯(PP)进行Mucell微孔注射成型试验。根据扫描电镜(SEM)结果得出:3种PP发泡差别较大且出现了明显的分层现象。通过单因素四水平试验法,考察了在微孔注射成型过程中3种PP的熔体温度和注射速度对制品拉伸强度的影响。结果表明:随着熔体温度的增加,发泡材料的拉伸强度基本呈现上升趋势;较低的注射速度得到的样条残余玻纤长度较长,材料力学性能较好;进而得到了发泡样条的宏观力学性能与残余玻纤长度之间的关系。     

硅烷偶联剂改性玻璃纤维增强硅气凝胶的研究

为了达到增强硅气凝胶力学性能的目的,采用硅烷偶联剂KH550与KH560二步改性接枝玻璃纤维,进而制备纤维增强硅气凝胶。利用扫描电子显微镜、红外光谱仪、比表面及孔径分布仪、热重-差热分析仪、导热系数仪、电子动静态疲劳试验机等对其表征。实验结果表明：硅烷偶联剂改性玻璃纤维与硅气凝胶复合后网络结构更加均匀、骨架强度更加稳定、孔径多在30 nm以下、具有良好的热稳定性;同时,改性玻璃纤维的最佳添加量为20%（质量分数）,此时其密度为0.167 g/cm³,导热系数为0.018 5 W/（m·K）,接触角为127°,抗弯强度为1.042 MPa,抗压强度为0.669 MPa,达到预期实验目的。     

添加剂对铅硅酸盐低熔点玻璃热性能的影响

采用常规玻璃熔融退火工艺制备了两组铅硅酸盐玻璃试样,玻璃组成为(物质的量含量,下同):(55-x)PbO-(10+x)B2O3-30SiO2-5ZnO(x=0,5,10,15)和(55-x)PbO-10B2O3-30SiO2-5ZnO-xSB2O3(x=5,10,15),以及与两组参照的传统铅硅酸盐玻璃55PbO-5Al2O3-10B2O3-30SiO2.利用热膨胀仪观察氧化物添加剂对玻璃转变温度范围△T(T1-Tg)的影响.实验结果表明,随着氧化硼加入量的不断提高,玻璃的转变温度(Tg)与软化温度(Tf)随之提高,而△T先减小后增大,即出现所谓的硼反常现象.当添加的氧化锑量在5%～10%(物质的量含量,下同)范围时,与参照样品相比,玻璃的软化温度(Tf)基本保持不变而转变温度(Tg)则提高10℃以上.当添加的氧化锑量达到15%时,玻璃的转变温度(Tg)与软化温度(Tf)均显著下降,但△T基本保持不变.     

组成对铜离子扩散着色玻璃光谱性能的影响研究

红色玻璃以其鲜艳的色彩备受消费者的青睐。本文以氯化亚铜为主要原料,添加一定量的黏结剂和填充剂,在空气气氛中制备了铜离子扩散红色玻璃。研究发现组成中氯化亚铜、硫酸亚铁、氧化亚锡等对铜离子扩散着色有很大的影响。通过控制氯化亚铜、硫酸亚铁、氧化亚锡等的用量可以制备出应用广泛的红色玻璃。     

树脂基复合材料中埋入大直径光纤性能的研究

本文依据国家有关的复合材料测试标准对树脂基复合材料埋入与不埋空心光纤进行了对比实验。实验结果表明大直径空心光纤埋入树脂基复合材料中对其性能的影响是比较小的,不会影响到树脂基复合材料工程结构中性能和使用。从而为复合材料的智能自诊断与自修复提供了一种研究的新方法。     

大规格抛光砖抛后变形问题的初步探讨

针对目前全国较多抛光砖生产企业中存在的大规格抛光砖抛后变形的问题,本文对抛光砖的坯料及瓷坯分别做了化学成分分析和吸水率测试,并利用扫描电对瓷坏进行了显微分析。结果表明,一方面坯料中Ｎａ２Ｏ和ＳｉＯ２含量偏高,ＣａＯ、ＭｇＯ、Ａｌ２Ｏ３含量偏低,导致瓷坯中存在较多的钠长石玻璃相;另一方面,大规格抛光砖较厚,抛光砖上下层存在明显的吸水率梯度,瓷坯在抛光及放置的过程中吸水后产生不可逆的吸湿膨胀,不同部分     

丙烯腈与丙烯酸乙酯乳液共聚合及其表征

用氧化还原引发体系在低温下研究了丙烯腈与丙烯酸乙酯的乳液共聚合。考察了聚合温度、乳化剂浓度和分子量调节剂浓度对聚合的影响 ,结果表明 ,随温度升高 ,乳化剂浓度增大 ,单体转化率和分子量增大 ,乳液更稳定 ;链转移剂十二烷基硫醇浓度增加 ,分子量显著降低 ,转化率有所降低 ,表明十二烷基硫醇在调节分子量的同时也起着缓聚剂的作用。用激光粒径分析仪考察了 2 0℃时聚合过程中乳胶粒子大小的变化 ,发现聚合过程的成核和增长均在胶束中进行的。用凝胶渗透色谱法研究了十二烷基硫醇对聚合物分子量的影响 ,发现聚合时加入分子量调节剂 ,活性链寿命较短并呈单峰分布 :聚合时不加入分子量调节剂 ,活性链寿命较长并呈双峰分布。 DSC结果表明 ,随聚合体系中软单体含量增加 ,共聚物的玻璃化温度降低。