Business publications and the popular press have stressed the importance of creating conditions for meaningful employee expression in work roles, also known as engagement. Few empirical studies, however, have examined how individual or situational factors relate to engagement. Consequently, this study examines the interplay between employee age, perceived coworker age composition, and satisfaction with older (older than 55) and younger (younger than 40) coworkers on engagement using a sample of 901 individuals employed in the United Kingdom. Results indicated that satisfaction with one's coworkers related significantly to engagement. Moreover, perceived age similarity was associated with higher levels of engagement among older workers when they were highly satisfied with their coworkers over 55 and lower levels of engagement when they were not. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

从关联分析法看如何改善沥青抗老化性能

用灰色关联分析法研究了沥青抗老化性能与沥青化学组成之间的关联程度，结果表明，影响再生沥青性质的主要因素是沥青中的芳烃和胶质的含量。通过添加芳香组分能改善沥青四组分之间的配伍性，从而可以改善再生沥青的抗老化性能。并通过对再生剂进行富芳处理，验证了上述结论。     

The effects of widowhood on physical and mental health, health behaviors, and health outcomes: The Women's Health Initiative.

This study examined whether widowhood was associated with physical and mental health, health behaviors, and health outcomes using a cross-sectional (N=72,247) and prospective (N=55,724) design in women aged 50-79 years participating in the Women's Health Initiative observational study (85.4% White). At baseline, married women reported better physical and mental health and generally better health behaviors than widowed women. Whereas women who remained married over the 3-year period showed stability in mental health, recent widows experienced marked impairments and longer term widows showed stability or slight improvements. Both groups of widows reported more unintentional weight loss over the 3-year period. Changes in physical health and health behaviors were inconsistent, with generally small effect sizes. Findings underscore the resilience of older women and their capacity to reestablish connections, but point to the need for services that strengthen social support among women who have difficulty during this transition. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

提高超小型铝电解电容器生产一次合格率

恰当选择原材料、确保铆接工序质量、重视工作电解液的配比、严控各工序成品率是提高超小型铝电解电容器投入产出一次合格率的关键。以１０Ｖ－４７μＦ（４ｍｍ×７ｍｍ）产品为例，投入产出一次合格率达９４％以上。     

硫化胶交联结构及其性能

综合讨论了聚合物／聚合物之间的交联结构及聚合物／填料之间的偶联结构对硫化胶抗硫化返牟性，抗氧老化性及动态疲劳性能的影响。     

聚醚酰亚胺热焓松弛的分子量依赖关系

采用ＤＳＣ对不同分子量的聚醚酰亚胺的等温及动态热焓松弛行为进行了研究，并以ＫＷＷ方程对实验数据进行了非线性拟合。结果表明，分子量对热焓松弛的影响是由高分子端基引起自由体积的差异所致。不同分子量的聚醚酰亚胺分子具有不同数量的端基，淬冷时端基数目的差异将产生不同数量的过剩自由体积，从而影响松弛热焓及松弛速率、低分子量的聚醚酰亚胺松弛相对较快，且起始热焓高，松弛的表观活化能亦较小。     

铝－锂合金中δ’（Al＿3Li）沉淀相时效粗化行为及体积分数的测定

对经固溶处理的二种Ａｌ－Ｌｉ合金（１．９４ｗｔ．％Ｌｉ和２．７５ｗｔ．％Ｌｉ）的时效过程进行了研究。结果表明：δ’的生长速率遵从Ｏｓｔｗａｒｄ粗化动力学。１．９４ｗｔ．％Ｌｉ合金δ’产生于时效过程中，而２．７５ｗｔ．％Ｌｉ合金的δ’产生于时效的前期阶段。前者的表现体积分数明显大于根据相图估算的数伍，真实体积分数则与此值接近；后者的体积分数低于根据相图估算的数值，这可能归咎于δ’固相线的位置、统计学误差及Ｌｉ更易在时效过程中贫化。     

Durability of hygrothermally aged graphite/epoxy woven composite under combined hygrothermal conditions

The objective of this study was to examine the effects of hygrothermal aging on the durability of a graphite/epoxy woven composite material system. The study was part of a larger project in which the objective was to evaluate and model the effects of moisture, temperature, and combined hygrothermal conditions on the strength and life of a graphite/epoxy woven composite material system. The results presented here represent an extension of the work by Patel and Case (Int. J. Fatigue 22 (2000) 809).

The hygrothermal aging consisted of cyclical temperature and moisture variations which were meant to simulate mission conditions for an advanced subsonic aircraft. Durability studies were carried out on the aged material system in the form of fatigue and residual strength testing under humid and elevated temperature environments. Damage mechanisms and failure modes were determined through fatigue testing, residual strength testing, and nondestructive evaluation.

Changes in physical appearance, thermal analysis results, fracture surfaces, and moisture diffusion behavior all supported the idea that the material was affected by the aging process. However, experimental testing also showed that the initial and residual tensile properties of the aged material were virtually unaffected by the imposed environmental aging (as compared to unaged material testing results), except when tested at elevated temperature. At elevated temperature, both the dynamic stiffness and residual strength were noticeably reduced from that at room temperature.     

Effect of powder painting procedures on the filiform corrosion of aluminium profiles

In this work, the filiform corrosion behaviour of powder painted aluminium profiles was studied, and the coating barrier properties together with adhesion to the substrate were analysed. Samples coated with a traditional painting procedure (one powder layer application followed by curing), and other samples coated using a special cycle to obtain wood grain effect were compared using accelerated filiform corrosion tests. Moreover, in order to better understand the degradation mechanisms of painted metal substrates, thermal stresses were applied to accelerate the natural weathering. The effects of the thermal aging were analysed by electrochemical impedance spectroscopy.     

复合绝缘子耐电腐蚀特点及其电蚀老化区域性的差异

为了了解复合绝缘子外绝缘材质电蚀老化状态和区域性的差异,对Al(OH)3耐电腐蚀机理、外绝缘材质中Al(OH)3颗粒分布状态和环境污湿因素的实际情况进行了研究。Al(OH)3颗粒分解成水蒸气、析出白色粉末状氧化铝,并催化生成二氧化碳,将使外绝缘材质逐渐微观减薄和加大表面的粗糙度,而引起电蚀老化的污湿环境因素,近期不可能得到改善,因此必然引起其电蚀老化出现区域性差异。此外,外绝缘憎水表面污珠场强变化引起的电晕也是促使电蚀老化的重要因素。