薄壁圆筒试样的扭转断裂曲线

通过比较多种材料的光滑薄圆筒和切口薄壁圆筒试样的扭断裂曲线，测向两种试验的断裂韧性ＫＩＩＣ相同，从而间接证实了利用光滑薄壁筒测定延性金属断裂韧性ＫＣ方法的正确性。     

锰铜基高阻尼合金中锌量的测定──硫氰酸盐萃取分离络合滴定法

基于甲基异丁基甲酮于稀盐酸介质中定量地萃取Ｚｎ￣（２＋）与ＣＮＳ￣－形成的络阴离子。从而达到与共存的锰、镍、铝、铬的完全分离。在有氟化物、硫脲存在时Ｆｅ￣（３＋）、Ｃｎ￣（２＋）和Ａｇ￣＋也不被萃取。有机相中的锌于ＰＨ５．５“六胺”缓冲介质中返萃取回水相，用ＥＤＴＡ滴定。在文中给定的条件下锌的一次被萃取率可达９９％以上，成功地解决了锰铜基高阻尼合金中共存离子对锌量测定的干扰问题。     

On the corrosion fatigue crack initiation model and expression of metallic notched elements

In the present study, attempts are made to extend the application of the mechanical model for the fatigue crack initiation (FCI) and the FCI life formula of metallic notched elements in laboratory air to those in the corrosive environment. The test results and analysis of the corrosion FCI (CFCI) life of aluminum alloys and Ti---6A1---4V show that the expression of the CFCI life obtained by modifying the FCI life formula in laboratory air can give a good fit to the test results of the CFCI life. The salt water (3.5% NaCl) environment has no effects on the CFCI resistant coefficient compared with the FCI resistant coefficient in laboratory air. However, 3.5% NaCl environment greatly decreases the CFCI threshold of aluminum alloy, but has little effect on the CFCI threshold of Ti---6A1---4V. The loading frequency ranging from 1 Hz to 10 Hz has no appreciable effect on the CFCI life, and thus, the CFCI threshold of aluminum alloys investigated. Hence, the expression for the CFCI life of metallic notched elements proposed in this study is a better one, which reveals a correlation between the CFCI life and the governing parameters, such as, the geometry of the notched elements, the nominal stress range, the stress ratio, the tensile properties and the CFCI threshold. However, this new expression of the CFCI life needs to be verified by more test results.     

COMPRESSION FATIGUE CRACK GROWTH BEHAVIOUR OF AN ALUMINIUM ALLOY: EFFECT OF OVERLOADING

Abstract— The behaviour of fatigue cracks in an Al-alloy under cyclic compression, either with or without overloads, was studied. For constant-amplitude compressive cycling, a non-catastrophic (saturation) character of the fatigue crack behaviour was confirmed, with the final depth of a crack depending on the applied load level. Single (tensile or compressive) intermittent overloads were shown to re-activate a previously arrested crack while reversed (tensile—compressive or compressive—tensile) ones were also shown to maintain continual fatigue crack extension under otherwise fully compressive cycling.     

纤维增强铝基复合材料变形损伤过程声发射研究

采用声发射（ＡＥ）技术，通过测定ＡＥ事件数、幅度和持续时间等发射特征参数以及恒载 Ｆｅｌｉｅｉｔｙ效应，对ＳｉＣ／Ａｌ和Ｃ／Ａｌ两类束丝纤维增强铝昨合在拉伸变形过程中的损失失效特征进行了分析探讨。实验结果表明，纤维种类、界面状况对复合材料损伤过程有着显著的影响，声发射技术是表征这类复合材料损伤特征很有潜力的方法。     

连续梁的简便计算

利用三转角方程，对连续梁的内力进行精确的计算，该方法简捷明了，便于应用。     

提高柴油机缸盖内腔铸造质量的工艺措施

缸盖是柴油机上的重要零件之一。铸造毛坯不可避免地存在劈缝、内腔粘砂、粗糙、局部不通等内腔质量问题 ,从而影响缸盖串水冷却效果。本文介绍了一些工艺措施 ,较好地解决了这个问题。     

铜线材酸性高速电镀致密光亮锡、锡铜合金

为了寻找低成本、低腐蚀、低污染高速电镀锡、锡铜合金工艺 ,在含光亮剂、柔软剂DL0 1、0 2、0 3的硫酸槽中在不同的电流密度、不同的搅拌速度下 ,在Φ0 .5mm的铜线上电镀Sn和Sn Cu合金镀层。DL0 1、0 2的主要成分是无芳香族的希夫碱 ,DL0 3的主要成分是醇醛缩合物。结果表明 ,在含有DL0 1、0 2、0 3和 35g/LSnSO4 ,137g/LH2 SO4 的镀液中 ,在Jc=10～ 90A/dm2 ,v=16 0～ 314m/min时 ,所得镀层致密、柔软、光亮。在含CuSO4 ·5H2 O 0 .5 ,3.5g/L的硫酸镀槽中 ,在Jc=9,18A/dm2 ,v=16 0m/min时获得了致密、柔软、光亮的Sn (0 .3%～ 0 .6 % )Cu合金镀层。     

Incoloy 800H合金的应用和性能分析

通过对耐热耐蚀合金Incoloy 80 0H的性能分析 ,指出它与普通奥氏体不锈钢相比具有较优的抗氧化性能、耐蚀性和高温蠕变强度。针对催化裂化装置同轴式沉降再生器内部所用Incoloy 80 0H焊件易出现裂纹的问题进行分析 ,认为在施焊过程中由于合金凝固时有低熔点金属或化合物的液态膜残留在晶界区 ,该合金具有高的焊接热裂纹敏感性 ,若焊材选择不当 ,焊丝填充不充分、缺少保护气等将导致晶间裂纹产生。提出了该合金采用TIG焊接防止热裂纹产生的措施。     

铝冷轧制油应用和生产工艺研究

通过对铝材冷轧工艺的分析。研究，以退火工艺中的斑痕为重点，提出采用加氢处理，异构化精制的石蜡基航空煤油组分为基础油，采用不同复合添加剂生产的通用铝冷轧制油完全可以满足客户要求。