Mixing in Wave Processes Propagating in Gas Mixtures (Review)

A review is made of uptodate investigations in the field of physicomathematical modeling of mixing of solid particles with highvelocity gas flows arising under the action on shock waves, compression waves, and expansion waves on unstable dust deposits on the boundaries of channels or plates and in cavities, as well as on free clouds of particles. In particular, experiments in shock tubes with particles initially located in cavities and on surfaces are described. The experimental data presented in the form of distributions of particle concentrations at various points of space above the unstable layer, pressure distributions on the lower wall of the shock tube, etc., are used for verification of proposed mathematical models in regimes of single particles, interacting continua, and turbulent diffusion. An analysis of experimental and numerical data shows that the models considered sometimes allow adequate identification of the wave structure of motion of the mixture and the field of parameters inside and outside the layer.     

Adhesion Effects of Intermediate Layers on the Densification of Ceramic Powders

In the ceramic technology the first step to produce sintered bodies is the manufacturing of powders which then are densified. The adhesion mechanisms between the single particles and the agglomerates produced from them determine the densification process. Starting from theoretical considerations adhesion mechanisms, such as solid bridge formation, adhesive bonding and glide-promoting effects, are discussed in principle. Subsequently, the effects of surface-active substances on the densification behaviour of clay-ceramics and oxide-ceramic bodies are discussed. Further, the evaluation of the action of additives to the powder mixtures on the microstructure of the compacts, such as porsity and texture, leads to a compaction equation which describes the transition from the powder pile to a densified green body.     

Fissure evolution and evaluation of pressure-relief gas drainage in the exploitation of super-remote protected seams

Based on nonlinearity contact theory and the geological structure of the Xieqiao Coal Mine in the newly developed Huainan coal field, rock movements, mining fissures and deformation of overlying strata were simulated by using the interface unit of FLAC3D to evaluate the pressure-relief gas drainage in the exploitation of super-remote protected seams. The simulation indicates that the height of the water flowing fractured zone is 54 m in the overlying strata above the protective layer. The maximum relative swelling deformation of the C 13 coal seam is 0.232%,while the mining height is 3.0 m and the distance from the B8 roof to the C13 floor is 129 m, which provides good agreement with a similar experiment and in situ results. The feasibility of exploitation of a super-remote protective coal seam and the performance of the pressure-relief gas drainage in a super-remote protected layer are evaluated by comparisons with practice projects. It demonstrates that the relieved gas in the super-remote protected layers could be better drained and it is feasible to exploit the B8 coal seam before the C13 super-remote protected coal seam. The method is applicable for the study of rock movements, mining fissures and deformation of the overburden, using the interface unit to analyze the contact problems in coal mines.     

全化学法制备缓冲层和YBaCuO超导涂层

用化学溶液沉积法,尤其是金属有机物沉积法（MOD）制备第二代超导带材,包括缓冲层和YBaCuO涂层,在当前超导带材研究中具有重要的意义．因为其成本低、操作简单、便于规模化生产,可能成为制备高温超导带材最有前途的方法．文内详述了用化学气相沉积,化学溶液沉积,电泳共沉积以及超声雾化热分解等方法制备YBaCuO超导涂层的国内外进展,介绍了在LaAlO3单晶上以及金属基带上制备钙钛矿结构缓冲层的主要种类和特征,也介绍了当前研究的热点之一,导电缓冲层的作用、制备方法和研究进展．     

应力吸收层沥青混合料的低温抗裂性能

通过对自主研发的Sampave等3种改性沥青结合料和不同级配的应力吸收层沥青混合料进行低温弯曲和低温蠕变试验,分析沥青结合料和矿料级配对应力吸收层沥青混合料低温抗裂性能的影响.结果表明:自主研发的Sampave特种改性沥青混合料具有优良的低温抗裂性能,但单一改性剂SBR改性沥青并不能达到应力吸收层沥青结合料的性能要求;矿料4.75 mm、0.075 mm筛孔通过率对其低温抗裂性能影响较敏感.     

The Mechanical Behaviour of Polyimide/Copper Laminates Part 2: Peel Energy Measurements

The mechanical peel behaviour of laminates consisting of polyimide films adhered to copper foil using a modified acrylic adhesive has been studied over a wide range of test rates and temperatures. The laminates were prepared from polyimide films which had been subjected to either a “high-thermal history” or a “low-thermal history” treatment during the production of the film. The measured peel energies of the laminates could be superimposed to give a master curve of peel energy versus the reduced rate of peel test, Ra_T, where R is the rate of peel test and a_T is the time-temperature shift factor. The appropriate shift factors were a function of the test temperature and were mainly deduced from tensile tests conducted on the bulk adhesive. The “high-thermal history” laminates gave higher peel energies and the locus of failure of the laminates was mainly by cohesive fracture through the adhesive layer. At low values of log₁₀ Ra_T, i.e. Low rates of peel and high test temperatures, the “low-thermal history” laminates also failed in the adhesive layer and possessed similar peel energies to those measured for the “high-thermal history” laminates. However, at high log₁₀ Ra_T values, the peel energies measured for the “low-thermal history” laminates were lower and showed a wider scatter. These arose from a different locus of failure occurring in these “low-thermal history” laminates when tested under these conditions. Namely, it was found that most of these laminates failed in a weak boundary layer in the outer regions of the “low-thermal history” polyimide film.     

高温气候下沥青混凝土心墙连续碾压施工结合面温控试验研究

在夏季高温气候沥青混凝土心墙连续多层施工时,为减少等待结合面温度降至规范要求上限值90℃的时间,通过室内试验模拟结合面温度提高后心墙连续两层铺筑的情况,分别研究了结合面温度在90℃、100℃、110℃情况下沥青混凝土的压实性和变形情况,并进行了现场试验论证。室内试验结果表明:心墙沥青混凝土结合面温度降至100℃时,上层沥青混凝土的孔隙率为2.88%,下层沥青混凝土的最大侧向应变值为2.78%;结合面温度为110℃时,上层沥青混凝土的孔隙率为3.85%,下层沥青混凝土的最大侧向应变值为4.00%。现场试验结果表明:结合面温度为100℃时的上层沥青混凝土孔隙率和渗透系数均满足规范要求。因此,沥青混凝土心墙连续多层碾压时,结合面温度提高至100℃的施工质量可以得到保证。     

NH_4Cl薄层液膜下X70钢腐蚀的电化学研究

采用电化学阻抗法和阴极极化曲线法研究了X70钢在含NH4Cl薄层液膜下的电化学行为.研究了液膜厚度、NH4Cl浓度对X70钢腐蚀行为的影响.结果表明,液膜厚度降低,X70钢腐蚀电位正移,阴极极限扩散电流增大.液膜厚度为130μm时,阴极极限扩散电流达最大值.液膜厚度为130~100μm时,阴极极限扩散电流反而降低.液膜厚度进一步减薄,阴极极限扩散电流又增大.薄层液膜下,NH4Cl浓度增大,阴极极限扩散电流减小,抑制了阴极过程;随着NH4Cl浓度增大,X70钢腐蚀的电荷传递电阻减小,对阳极过程有一定的促进作用,从而加速X70钢的腐蚀速率.     

含软弱夹层的某公路边坡开挖支护数值模拟分析

基于某含有软弱夹层的公路边坡工程,利用有限元软件对其开挖支护过程进行数值模拟分析,计算考虑了2种不同的开挖工况：1）只开挖不支护;2）开挖并及时支护。研究表明：在开挖未支护时,边坡开挖完成后安全系数小于1,边坡整体都发生很大位移,将沿着软弱夹层带发生破坏;在开挖并及时支护时,边坡位移明显减小,软弱夹层附近塑形变形区得到了有效控制,且开挖完成后安全系数为1．87,满足设计要求。     

萨中开发区“二三结合”开发实验数值模拟

应用数值模拟方法,分析大庆油田萨中开发区二、三类油层(萨Ⅱ10~萨Ⅲ10)"二三结合"开发实验井网部署,实验层段组合优化方案,注聚开发合理衔接时机,二、三类油层最佳组合开发模式等.结果表明:二、三类油层各自部署一套新井网,协调布井,同步钻井选择性射孔、同步水驱挖潜,协调平面和纵向注采关系,同期注入不同相对分子质量的聚合物进行三次采油能有效地挖潜油藏剩余油,提高采收率.