Unperturbed dimension of poly(4-acetoxystyrene) measured in good and theta solvents

In order to obtain the additional data concerning the unperturbed dimension of poly-4-substituted styrene, light scattering measurements are performed on the twenty-two fractions with molecular weight of (0.91–352)·10⁴ of poly(4-acetoxystyrene) in dioxan at 25°C, from which the molecular weight obtained was found easily to be evaluated with the gel permeation chromatography using THF. Phase separation experiments for this polymer indicate that the theta state is attained in isopropyl acetate at 19.7°C and butyl acetate at 26.8°C. By making viscosity measurements at that state, the value of K_Θ is directly evaluated as 5.4·10^?4 dl g^?1. The limiting viscosity number is also obtained in good solvents, THF and dioxan, at 25°C and constants of the Mark-Houwink-Sakurada equation in each solvent are determined. Further, approximately the same K_Θ as above is obtained from these data with the Stockmayer-Fixman plot. The calculated value of steric factor, 2.37, on this polymer may be plausible, compared with those of polyvinylaromatic derivatives.     

Cif2000平台下的核磁共振测井解谱方法研究

介绍了在Cif2000多井解释平台下的核磁共振解谱方法与编程实现。解谱采用加入平滑因子后在特征矩阵的奇异值分解中截去小的非零奇异值的方法，可以在低信噪比时得到稳定的弛豫谱，在油田实际应用中证明了该方法的有效性。根据该方法在Cif2000平台上编制了完整的解谱处理程序，可以直接用于油田的生产实际。     

Synthesis, Characterization, and Formation Process of Na-X Zeolite from Coal Fly Ash

Using the SiO₂ and Al₂O₃ components of the amorphous phase in coal fly ash (Fa), Fa was converted to Na-X zeolites in NaOH-NaAlO₂ solutions by stirring at 35°C for 72 hr and then aging at 85°C for a given period. The molar ratio SiO₂/Al₂O₃ of the starting materials was controlled from 2.0 to 13.2. The resulting materials were characterized by various means. Increasing the SiO₂/Al₂O₃ ratio of the starting material increased the degree of crystallinity of faujasite, exhibiting a maximum at SiO₂/Al₂O₃ = 8.0. The faujasite formed was identified as Na-X zeolite with Si/Al = 1.20. The amorphous phase in Fa was dissolved during the stirring to form a precursor of zeolite, such as amorphous aluminosilicate. The Na-X zeolite was formed by aging for 24 hr, and the degree of crystallinity of this material was increased with the increasing aging period. The cation exchange capacity and specific surface area were increased with the increasing degree of crystallinity of the Na-X zeolites.     

用C51系列单片机设计物体分级设备的测量光幕

首先介绍了光幕测量高度的原理 ,给出了高度测量光幕的一种实现方法 ,分析了由该方法设计的系统结构和主要性能。从而彻底解决了相邻通路间的干扰 ,提高了测量精度。     

Photocatalytic Property and Electronic Structure of Lanthanide-based Oxysulfides

Lanthanide-based oxysulfides and sulfide, LnTaO_3.5S_0.5, Ln₁₀OS₁₄ (Ln = La, Pr, Nd, Sm) and La₄In₅S₁₃, were successively synthesized by sulfurization in a flowing H₂S. The sulfurization decreased the band-gap energies from >4 eV to <3eV, because of the formation of occupied S3p orbitals on the top of valence band. In accordance with the small band gap, the H₂ evolution from a 0.01 M Na₂S and 0.01 M Na₂SO₃ solution system was observed under irradiation of light up to >500 nm. The rate of H₂ evolution under light irradiation of >500 nm increased in the order of Ni/LaTaO_3.5S_0.5 < Ru/La₁₀OS₁₄ < Pt/La₄In₅S₁₃.     

Inverted Solution Processable OLEDs Using a Metal Oxide as an Electron Injection Contact.

A new type of bottom‐emission electroluminescent device is described in which a metal oxide is used as the electron‐injecting contact. The preparation of such a device is simple. It consists of the deposition of a thin layer of a metal oxide on top of an indium tin oxide covered glass substrate, followed by the solution processing of the light‐emitting layer and subsequently the deposition of a high‐workfunction (air‐stable) metal anode. This architecture allows for a low‐cost electroluminescent device because no rigorous encapsulation is required. Electroluminescence with a high brightness reaching 5700 cd m^–2 is observed at voltages as low as 8 V, demonstrating the potential of this new approach to organic light‐emitting diode (OLED) devices. Unfortunately the device efficiency is rather low because of the high current density flowing through the device. We show that the device only operates after the insertion of an additional hole‐injection layer in between the light‐emitting polymer (LEP) and the metal anode. A simple model that explains the experimental results and provides avenues for further optimization of these devices is described. It is based on the idea that the barrier for electron injection is lowered by the formation of a space–charge field over the metal‐oxide–LEP interface due to the build up of holes in the LEP layer close to this interface.     

加氢处理润滑油基础油各组分对光安定性的影响

将经紫外光照前后的加氢处理润滑油基础油分离为饱和烃、轻质芳烃、中质芳烃、重质芳烃和极性组分，分别采用薄层色谱、质谱和紫外吸收光谱分析了各组分的烃组成、硫和氮含量的变化，并通过将从原料油中分离出的各组分反加到光安定性好的饱和烃中，试验验证了加氢处理润滑油基础油中的重质芳烃和极性组分是光不安定组分，其中含有硫、氮的芳香杂环化合物光安定性差。     

液晶光阀光电导层光吸收系数的研究

用化学气相沉积法制备了液晶光阀中光电导层———非晶硅薄膜,从实验中得出最佳制备工艺的参数取值。给出了用包络线法测量非晶硅薄膜光吸收系数的原理,测量了样品的光吸收系数随波长的变化规律。得到样品在最佳工艺条件下的光吸收系数高于1×103cm-1。     

Distributed Optical Fiber Sensor for Multi-point Temperature Measurement

The distributed optical fiber sensing technology is overviewed, which is based on Raman scattering light theory. Basic operation principle, structure, system characteristics and signal processing are discussed. This structure and method of the signal processing possess of certain spatial resolution, hence will ensure the practicability of system.