X-ray diffraction, electron paramagnetic resonance, microwave absorption and resistivity measurements were carried out on
YBa2−xBixCu3O7 (0≤x≤0·5) superconductors in order to study the effect of bismuth on the structural and superconducting properties. A decrease
in sintering temperature increased the amount of impurity phase. Transition from an orthorhombic (superconducting) phase to
tetragonal structure produced no significant change in EPR zero-field signal at liquid nitrogen temperature (LNT). The non-resonance
signal height decreased on higher concentration of bismuth. Sintered YBa2−xBixCu3O7 superconductor had a strong EPR zero-field signal at LNT. We have evaluated particle size from XRD and EPR studies. The average
particle size was about 0·4μm. 相似文献
Microalloyed high-strength low-alloy (HSLA) steels contain additions of Nb, V, Ti, or in combination, in amounts of 0.01 to 0.1 weight percent to improve mechanical properties, which are strongly dependent on the thermomechanical interaction taking place in the course of rolling mill processes. The recrystallizatian of hat-twisted austenite has been investigated in a cylindrical specimen (f 6×50 mm) machined from hat rolled plates of 0,052 wt % Niobium microalloyed steel. Continuous and interrupted torsion test were carried out in the temperature range 1123 K to 1173 K after a solution treatment of 1.5 minutes at 1423 K and torque-twist data were analysed. The various methods were discussed for obtaining results from torsion tests. The effect of precipitation kinetics was appreciated by way of connection tp/tp(red), where tp is the experimental measured time for the peak stress and tp(red) is the newly defined reduced time. The softening ratio X and time t0.05R for start of static recrystallization were established.
The correlation between precipitation and recrystallization is presented as a graphs for chosen requirements (temperature of austenitization, carbon and niobium content and strain rate). If temperature goes below 850°C, the restoration processes are hardly suppressed, both are limited by diffusion and Nb(CN) precipitation, which are extended dynamically in the range of strains rates 10−2 to 1 s−1.
In the present paper, an attempt is made to derive the PRTT diagram and to define all mathematical equations for describing recrystallization times t0.05R, t0.5R, t0.95R and t0.05P for the start of precipitation. In real metal forming processes such as the hot rolling of plates or strips the knowledge of these parameters and results is extremely important for the the correct microstructure and sheet quality to be obtained. 相似文献
Lake Qinghai, the largest saline lake with an area of 4,260 km2 (2000) and average depth of 21 m (1985) in West China, has experienced severe decline in water level in recent decades. This
study aimed to investigate water balance of the lake and identify the causes for the decline in lake level. There was a 3.35-m
decline in water level with an average decreasing rate of 8.0 cm year−1 between 1959 and 2000. The lake water balance showed that mean annual precipitation between 1959 and 2000 over the lake was
357 ± 10 mm, evaporation was 924 ± 10 mm, surface runoff water inflow was 348 ± 21 mm, groundwater inflow was 138 mm ± 9 and
the change in lake level was −80 ± 31 mm. The variation of lake level was highly positively correlated to surface runoff and
precipitation and negatively to evaporation, the correlation coefficients were 0.89, 0.81 and −0.66, respectively. Water consumption
by human activities accounts for 1% of the evaporation loss of the lake, implying that water consumption by human activities
has little effect on lake level decline. Most dramatic decline in lake level occurred in the warm and dry years, and moderate
decline in the cold and dry years, and relatively slight decline in the warm and wet years, therefore, the trend of cold/warm
and dry climate in recent decades may be the main reasons for the decline in lake level. 相似文献
A one-dimensional fluid model for homogeneous atmospheric pressure barrier discharges in helium is presented by considering elementary processes of excitation and ionization including a metastable atom effect. Using this model we investigate the behaviours of the helium metastable atoms in discharges as well as their influence on the discharge characteristics. It is shown that the metastable atoms with a relatively high concentration during the discharge are mainly produced in the active phase of the discharge and dissolved in the off phase. It is also found that the metastable atom collisions can not only provide seed electrons for discharges but also influence the concentration of ions. A reduction of matestable atom density results in a drop in the charged particle densities and causes a qualitative change in the discharge patterns. 相似文献