微波辐射干燥氟化铝的工艺研究

介绍了微波干燥的原理和主要特点，研究了利用微波辐射干燥氟化铝工艺，探讨了微波功率、微波辐射时间、物料质量、物料厚度对氟化铝脱水率的影响。实验的最佳条件为微波功率2．0kW、干燥时间80s、物料质量400g、物料厚度2．0cm。实验结果表明，利用微波辐射干燥，氟化铝含水质量分数小于1％，且干燥时间短、能耗低，实验为工业化提供了必要的参考数据。     

Relationship between oxidative stability of vitamin E and production of fatty acids in oils during microwave heating

Effects of microwave heating on the oxidative stability ofd-tocopherols were studied in relation to the production of fatty acids in oils. During microwave heating, the stability of tocopherols decreased in the orderδ>β>γ>α. This order did not depend on the types of ethyl esters of fatty acids or oils present. But, the shorter the chainlength and the lower the degree of unsaturation of the fatty acid ethyl esters, the greater was the reduction in amount of individual tocopherols. A similar tendency was observed when tocopherol-stripped vegetable oils, with equimolar mixtures of tocopherols added, were treated under the same conditions. The reduction in tocopherols became greater with increasing levels of free fatty acids.     

单晶金刚石膜与多晶金刚石膜的制备工艺及性能

本文主要介绍了用微波等离子体化学气相沉积法(以下简称MP CVD法)以甲醇-氢气混合气和丙酮-氢气混合气为源气体,分别以单晶硅的(111)面和人造金刚石的(100)面为衬底材料,制备出了面积为20mm×20mm厚为10μm的多晶金刚石膜和面积为1.0mm×1.0mm厚为5μm的单晶金刚石膜。通过试验发现,源气体配比和衬底温度对薄膜质量起决定性作用。另外,衬底在反应腔中的位置对薄膜的生成也有很大影响。单晶金刚石膜制备过程中衬底金刚石的晶体取向与金刚石薄膜的生长及质量有密切的关系。在金刚石的(100),(110)和(111)面上分别获得了单晶金刚石膜和金刚石多晶粒子。选用扫描电镜、显微激光拉曼、反射电子衍射对多晶金刚石膜及单晶金刚石膜的性能进行了测试。     

微波辐射磷钨酸催化合成环己酮1,2-丙二醇缩酮

在微波辐射下,以磷钨酸为催化剂,对以环己酮和1,2-丙二醇为原料合成环己酮1,2-丙二醇缩酮进行了研究.较系统的研究了反应物投料比、微波辐射功率、微波辐射时间、催化剂用量、带水剂用量诸因素对产品收率的影响.最佳反应条件为:环己酮为0.2mol,n(环己酮):n(1,2-丙二醇)=1.0:1.5,微波辐射功率600W,辐射时间16min,催化剂用量为反应物总质量的0.5%,带水剂(环己烷)15mL.在此条件下,环己酮1,2-丙二醇缩酮的产率可达82.0%.     

Straightforward modeling of dynamic I–V characteristics for microwave FETs

This work presents a straightforward approach aimed at modeling the dynamic I–V characteristics of microwave active solid‐state devices. The drain‐source current generator represents the most significant source of nonlinearity in a transistor and, therefore, its correct modeling is fundamental to predict accurately the current and voltage waveforms under large‐signal operation. The proposed approach relies on using a small set of low‐frequency time‐domain waveform measurements combined with numerical optimization‐based estimation of the nonlinear model parameters. The procedure is applied to a gallium nitride HEMT and silicon FinFET. The effectiveness of the modeling procedure in terms of prediction accuracy and generalization capability is demonstrated by validation of the extracted models under operating conditions different than the ones used for the parameters estimation. Good agreement between measurements and model simulations is achieved for both technologies and in both low‐ and high‐frequency range. © 2013 Wiley Periodicals, Inc. Int J RF and Microwave CAE 24:109–116, 2014.     

Application of a multiline material characterization method to inkjet printed electronics

Material characterization has become increasingly important with the adoption of simulation‐based workflow for microwave electronics design. This article focuses on the characterization of printable electronics materials using transmission‐line measurements and demonstrates the capability of the multiline characterization method to separate dielectric and conductor losses when line geometry and material properties vary between the lines. The effects of multiline algorithm, number of line standards, and methods for selecting optimal line lengths are demonstrated. Consistent characterization results are obtained from inkjet‐printed transmission lines on two different substrate materials. In addition, local conductor thickness variations are demonstrated as an effective way to decrease losses. Finally, the simulation‐based procedure for determining the material properties is outlined and applied to printable electronics characterization. © 2013 Wiley Periodicals, Inc. Int J RF and Microwave CAE 24:177–183, 2014.     

微波辐射对甲苯磺酸催化合成乙酸环己酯

以冰醋酸和环己醇为原料 ,环已烷为带水剂 ,对甲苯磺酸作催化剂 ,采用微波辐射技术 ,在常压下直接合成乙酸环己酯。最适宜反应条件为 :n(环己醇 )∶n(乙酸 ) =1 5∶1 0 ,对甲苯磺酸用量 0 2 0 g ,带水剂用量 5mL ,微波功率 5 95W ,辐射时间 15min ,产率达 97%以上     

微波辅助合成1-(3-羟丙基)-4-哌啶酮

以3-羟基丙胺和丙烯酸甲酯为起始原料,在微波辅助下进行Michael加成、Dieckmann环合和脱羧反应合成了1-(3-羟丙基)-4-哌啶酮.并对Michael加成、Dieckmann环合和脱羧反应的工艺参数进行了优化,通过核磁共振波谱对目标化合物和中间体的结构进行表征.得到的最优Michael加成工艺条件为:n(3-羟基丙胺):n(丙烯酸甲酯)=1.0:2.4,微波辐射功率为120 W,反应温度40℃,反应时间30 min.在该条件下制备3-[(2-甲氧羰乙基)(3-羟丙基)氨基]丙酸甲酯的收率为92.6％;在微波辐射功率为200 W下,Dieckmann环合反应和脱羧反应分别为20和25 min,以88.5％的收率得到1-(3-羟丙基)-4-哌啶酮;目标产物总收率为82.0％.     

微波烧结Al2O3-TiC复合材料的研究

以纳米级TiC、Al2 O3 为原料 ,用微波烧结制备Al2 O3 -TiC复合材料 ,并与常规烧结比较。分析了两种烧结方法对制备试样的力学性能的影响 ,并探讨了添加剂对Al2 O3 -TiC复合材料烧结性能的影响     

Poly(methyl methacrylate) nanoparticles prepared through microwave emulsion polymerization

The emulsifier‐free emulsion polymerization of methyl methacrylate (MMA) was conducted with microwave irradiation. Superfine and monodisperse poly(methyl methacrylate) (PMMA) microspheres were obtained. Microwave irradiation notably promoted the polymerization reaction. This phenomenon was ascribed to the acceleration of the initiator [potassium persulfate (KPS)] decomposition by microwave irradiation. The experimental results revealed that the apparent activation energy of KPS decomposition decreased from 128.3 to 106.0 kJ/mol with microwave irradiation. The average particle size of the prepared PMMA latex was mainly controlled with the MMA concentration; it increased linearly from 103 to 215 nm when the MMA concentration increased from 0 to 0.3 mol/L and then remained almost constant at MMA concentrations of 0.3–1.0 mol/L. The KPS concentration had no effect on the average particle size, but the particle size dispersity was significantly reduced by a high KPS concentration. With a mixed polymerization phase (water/acetone = 1:3 v/v) or a redox initiation system, PMMA nanoparticles were obtained with an average particle size of 45 or 67 nm, respectively. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 93: 2815–2820, 2004