含纳米ATO聚氨酯弹性抗静电涂料

以脂肪族聚氨酯弹性树脂为基体，透明纳米ATO导电粉为导电介质，添加超分散剂，采用物理与化学相结合的分散方法对纳米ATO进行预处理。主要解决纳米粒子的分散与团聚的难题，制备出可常温固化、颜色可调的含纳米ATO聚氨酯弹性抗静电涂料。讨论了基体树脂、纳米ATO含量、超分散剂种类与加量、研磨时间以及助剂等因素对抗静电涂料的表面电阻、耐候性、弹性、强度以及稳定性等性能的影响。同时对涂料的性能进行了测试与表征。     

Preparation and characterization of calcium carbonate/low‐density‐polyethylene nanocomposites

Calcium carbonate/low‐density‐polyethylene (LDPE) nanocomposites have been prepared by melting blend with twin‐screw extruder. The mechanical properties of composites and the dispersion of the nanoparticles were studied. The reinforcement mechanism was discussed. The results show that not only the tensile property but also the flexural modulus of the system have been evidently increased by the addition of calcium carbonate. The calcium carbonate particles have been dispersed in the matrix in the nanometer scale. The reinforcement mechanism of the calcium carbonate lies on that the calcium carbonate particles, acting as hetero‐nuclei, can induce higher crystallinity at the matrix‐particle interface compared to regions away from the interface. Consequently, in the process of the tensile test, the nanocomposites have better tensile yield strength. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007     

反相微乳液法制备陶瓷彩喷墨水(Ⅰ)

系统地研究了Span80-Tween60/助乳化剂/油/FeCl3反相微乳液体系。通过正交实验,进行方差分析,得出最佳反相微乳液体系。通过均匀实验和全面实验,绘制出体系的拟三元相图,并由相图得出体系的最佳比例。绘制出最大溶水量与温度的曲线,从而确定最佳乳化温度。在最佳温度、最佳比例下,配制出两种墨水,并测定了墨水的表面张力、粘度、电导率和稳定性等性能。     

反相微乳液法制备陶瓷彩喷墨水(Ⅱ)

通过红外光谱仪测定两种墨水的微乳液结构。结果表明,醚氧键中的羟基与H2O分子作用后因形成氢键,而且有强烈的相互作用;正己醇分子在该反相微乳液中水分子作用很弱,而且推断它位于反相微乳液的栅状层;随着微乳液中含水量的增大,水分子O-H伸缩振动峰的强度和频率均发生变化,其吸收强度变大,峰面积增加,频率也向低频方向位移;体系中存在三种水:结合水、捕获水和自由水。并探讨了其反应机理。     

纳米SiO_2改性外墙涂料的研究

介绍了纳米材料改性高性能建筑外墙涂料的配方及研制,着重讨论了纳米SiO2添加量对涂料性能的影响:掺入4%的纳米SiO2能明显改善涂膜的附着力、光泽度、耐水、耐碱、耐洗刷性和涂料的抗沾污性、触变性能、稳定性。     

水热法制备ZrO_2纳米微晶及对乙醇和丁烷气敏性研究

用水热法制备 Zr O2 纳米微晶的平均尺寸为直径 5 nm,长 7.5 nm。由 X射线衍射确认晶相为单斜相。并对其形状和大小进行了透射电镜和激光散射分析 ,结果表明 Zr O2 纳米粒子在水溶液中存在软团聚 ,团聚体平均尺寸约 90 nm。着重研究了 Zr O2 纳米微晶对乙醇及丁烷的气敏性能 ,结果表明用纳米级 Zr O2 粒子制备的气敏元件对乙醇和丁烷有好的气敏性。并且随着纳米粒子尺寸降低 ,对气体敏感性增强     

Offset printing inks based on rapeseed and sunflower oil. Part I: Synthesis and characterization of rapeseed oil-and sunflower oil-modified alkyd resins

Two sets of alkyd resins of variable oil lengths with the required properties for offset printing ink formulations, modified by sunflower and rapeseed oil, were synthetized according to the “monoglyceride” process. The influence of the acyl composition of the modifying vegetable oil and of the oil content on alkyds’ properties was determined by detailed chemical and rheological characterization. Molecular structure, size, and molecule size distribution appeared to be linked to these two factors. A comparative study with two usual linseed oil-modified alkyds led to determination of the more appropriate alkyds for applications in offset varnishes.     

PE基聚硅氧烷/改性SiO2超疏水薄膜的构筑

使用十八烷基三甲氧基硅烷(OTMS)对纳米SiO2进行表面疏水改性,将得到的改性纳米SiO2(OTMS-SiO2)添加到有机硅树脂(SI)中,然后采用两步法在聚乙烯(PE)薄膜表面固化制备了复合涂层SI/OTMS-SiO2.通过FTIR、1HNMR、29SiNMR、TGA对OTMS-SiO2及复合涂层进行了表征,采用接触角测量仪、SEM、AFM对复合涂层疏水特性和形貌进行了测试和观察,最后对复合涂层的耐磨性和附着力进行了分析.结果表明,SiO2表面成功引入了OTMS,且OTMS-SiO2均匀附着在硅树脂涂层上,增加了表面粗糙度,得到了PE基固化超疏水复合涂层.当OTMS-SiO2添加量为正己烷质量的8％时,制得的复合涂层的水接触角为154°,滚动角为7°,并具有良好的耐磨性,其附着力可达4A等级.     

纳米级氢氧化镍制备及电化学性能研究

介绍了一种通过合成草酸镍,进而生成β型纳米氢氧化镍的新的合成路线,从而达到大幅度提高镍氢电池正极放电容量的目的。使用X射线衍射（XRD）分析产品的晶型结构。从产品谱图中可以得知：由于特征衍射峰的出现可以判定该产品为β型,且由于（001）峰的宽化可以初步判定其为纳米级。通过透射电镜（TEM）可以看出产品粒径和形貌的具体特征,即产品为针状,长度为100～200 nm,直径为10～20 nm。将纳米级氢氧化镍制成电极,经过充放电测试可以发现电容量约为400 mA.h/g,远远高于球形微米级氢氧化镍的放电容量。     

新型氨基化磁性纳米粒子的合成

通过嫁接方法在包有二氧化硅的纳米CoFe2O4磁粒表面进行氨基化修饰,制备出一种可用于生物医学领域的新型氨基化纳米磁粒,采用TGA-DTA,IR,VSM和Zeta-potential等测定方法,对氨基化和未氨基化的CoFe2O4纳米粒子进行了表征。元素分析结果显示,有0.98 mmol/g的有机分子固定在纳米粒子表面;红外和热分析数据显示,带氨基的有机分子嫁接到磁粒表面的二氧化硅壳层上;Zeta电位数据也显示,带氨基的有机分子嫁接到纳米磁粒表面;样品的磁性参数显示,氨基化纳米磁粒仍具有好的磁学性能。