采用液相还原法从废铜料中制备纳米铜粉

采用处理废铜料所得的硫酸铜溶液为原料,低毒害的铝粉为还原剂,使用液相还原法制备纳米铜粉。利用XRD和SEM对所制纳米铜粉进行表征。在反应温度80℃时,加入物质的量为硫酸铜10%的CTAB,获得晶粒粒径约45 nm的铜粉,其表面未有氧化。利用此法制备纳米铜粉,提高了废铜料的应用价值,实现了贵重资源的再生利用。     

不同维度纳米铜对锂基润滑脂摩擦学性能的影响机制

As an excellent anti-wear and friction-reducing additive, nano-copper has attracted extensive researches and attention in tribology field. However, the existing researches are still limited to zero-dimensional nano-copper, that is, the effect of copper nanoparticles on the tribological properties of lubricants. In this paper, the effects of nano-coppers with different dimensions (copper nanoparticles, copper nanowires and copper nanoplates) on the anti-wear ability and friction-reducing performance of lithium grease were systematically investigated. And the mechanism of interaction between dimension and tribological properties was explained in detail. It is concluded that the tribological properties of lithium grease can be improved by the addition of nano-coppers with different dimensions and the dimension of nano-copper has great influence on its tribological property.     

均匀沉淀法制备不同粒径的纳米Cu（OH）2

以无水硫酸铜和氢氧化钡为原料,采用均匀沉淀法研究了不同粒径纳米Cu（OH）2的制备,考察了搅拌温度、硫酸铜溶液浓度等反应条件对纳米Cu（OH）2粒径的影响。实验结果表明,用均匀沉淀法可以制备出不同粒度的纳米Cu（OH）2颗粒。反应条件对纳米Cu（OH）2的粒径有显著影响,反应温度越高,纳米粒子的粒径越小;硫酸铜溶液的浓度越高,纳米粒子的粒径越大。     

Preparation of nano-copper as lubrication oil additive

Nano-copper used as lubrication oil additive has good tribological property and active self-repairing effect for friction pairs. The reduction in liquid phase for preparing nano-additive is one of the most common method.Nano-copper was prepared by reduction in liquid phase. The different project and routine practice for preparing nano-copper were researched. The dispersion problem of nano-copper was investigated by surface treatment and high dispersion. The particles dimension, the dispersion stability and the purity of nano-copper were characterized by TEM and XRD. The conclusion indicates that the methods of the preparation and dispersion can obtain 20 nm copper additive with good dispersion property in lubrication oil.     

铜催化剂纳米粒子的尺寸对碳纤维形貌的影响

通过化学气相沉积法高重复性制备了纳米螺旋碳纤维和直线性碳纤维,并研究了金属铜纳米粒子催化剂的尺寸大小对碳纤维形貌的影响,认为粒径较大的铜纳米粒子容易催化聚合生成直线形碳纤维;反之,粒径较小的铜纳米粒子倾向于合成纳米螺旋碳纤维.利用场发射扫描电镜(FESEM)、透射电镜(TEM)和X射线粉末衍射(XRD)等测试方法对产物进行了表征.     

纳米润滑添加剂的润滑自修复效应

采用湿式机械化学法制备纳米铜并对其进行二次化学修饰，使其稳定地分散在基础油中；获得了自修复纳米润滑添加剂NT1。用透射电镜观察了纳米铜的表面形貌；用XP销-盘试验机考察了NT1的摩擦学性能。试验结果表明：自修复纳米润滑添加剂具有良好的分散稳定性、抗磨性和自修复性。     

纳米铜复合焦脱除含硝基苯废水的研究

采用焦炭作载体,通过KBH4还原法制备了纳米铜复合焦催化剂,并进行了催化剂制备和硝基苯脱除工艺的研究以及催化剂的表征.结果表明,KOH预处理焦有利于丰富焦的中孔.当KBH4还原等含量的CuSO4溶液时,1～3nm的Cu和Cu2O负载在焦的中孔表面,形成纳米Cu2O/Cu复合焦催化剂.当pH为6时,吸附时间大于6.5 h...     

甲酸钠/氧化铜复合相变材料的制备与热力学性能测试

配制了甲酸钠/氧化铜复合相变材料。通过恒温槽实验对比了甲酸钠,乙酸钠,丙酸钠以及氯化铵的性能,选择了性能最优的甲酸钠。通过配制不同浓度的甲酸钠溶液,对比其性能,发现29.4 wt%甲酸钠溶液的效果最好。为了优化溶液的导热性能,通过对比不同纯金属纳米材料和金属氧化物纳米材料的种类以及对比添加同种纳米材料不同的质量分数,发现添加0.5 wt%的氧化铜效果最优。通过Hot Disk和DSC实验对配方进行了导热值以及潜热值的测量,结果显示添加了纳米材料的配方其潜热为250.4 J/g,相变温度为-16℃,导热系数为1.078 W/（m·K）,比未添加的导热能力提高了9.66%。实验过程中未发生化学沉降等现象。     

磁场环境下含纳米Cu润滑油摩擦学特性及其机理

合成了油酸修饰的纳米Cu润滑油添加剂，并用改装的四球摩擦磨损试验机考察了添加纳米Cu的润滑油在不同磁场条件下的摩擦学性能。结果表明，磁场作用下，含纳米Cu添加剂润滑油中钢球的磨斑直径和摩擦因数均小于无磁场环境。采用扫描电子显微镜和X射线光电子能谱分析了磨斑表面，并探讨了磁场条件下纳米Cu添加剂的摩擦学机理。分析认为：一方面，外加磁场引起的感应电流促进了Cu的软化涂抹；另一方面，外加磁场可能促进了Cu参与摩擦化学反应生成了CuO。     

导电墨水用纳米铜的制备及表征

以CuO为铜源,水合联氨为还原剂,首次制备出适合导电墨水用的高浓度、高纯度纳米铜颗粒混合溶液。试验结果表明:该方法可获得质量分数在11%以上的纳米铜固体颗粒,平均颗粒尺寸约为98nm;制备工艺简单,不需要水洗或复杂的电渗析处理。方法有较大的工业应用前景。