A Dual Physical Cross-Linking Strategy to Construct Tough Hydrogels with High Strength,Excellent Fatigue Resistance,and Stretching-Induced Strengthening Effect

Hydrogels with excellent stiffness, toughness, anti-fatigue, and self-recovery properties are regarded as promising water-containing materials. In this work, a dual physically cross-linked (DPC) sodium alginate (SA)/poly[acrylamide (AAm)-acrylic acid (AAc)-octadecyl methacrylate (OMA)]-Fe³⁺ hydrogel is reported, which is constructed by hydrophobic association (HA) and ionic coordination (IC). The optimal DPC hydrogel demonstrates excellent mechanical performance: tensile modulus of 0.65 MPa, tensile strength of 3.31 MPa, elongation at break of 1547%, and toughness of 27.8 MJ m^–3. SA/P(AAm-AAc-OMA)-Fe³⁺ DPC hydrogels also exhibit prominent anti-fatigue and self-recovery performance (99.1–109.7% modulus recovery and 90.4–108.9% dissipated energy recovery after resting for 5 min without additional stimuli at ambient temperature) through the reconstruction of reversible physical cross-linking. Some of the SA/P(AAm-AAc-OMA)-Fe³⁺ DPC hydrogels even exhibit a stretching-induced strengthening effect, which is similar to the performance of muscle—“the more training, the more strength.” Hence, the combination of HA and IC will provide an effective approach to design DPC hydrogels with desirable mechanical performances and a longer service life for wider applications of soft materials.     

不锈钢复合板热疲劳性能分析

利用冷热疲劳试验机模拟分析了冷热循环对不锈钢复合板热疲劳性能的影响,并采用扫描电镜、电子探针和电子背散射衍射仪对热疲劳试样V形缺口及裂纹区域的形貌和成分进行了深入分析。结果表明,不锈钢复合板热疲劳试样经 20~550 ℃ 7 500次冷热循环后,结合界面处V形缺口区出现微裂纹,且微裂纹起裂于V形缺口尖端基层侧。随着冷热循环的继续进行,微裂纹向基层内扩展,但并非沿着结合界面处扩展,而是沿着基层侧扩展。此外,热疲劳裂纹的起裂和扩展与氧化和应力作用有关,微裂纹起裂于热疲劳试样 V 形缺口区域基层侧表层局部氧化孔洞,并在冷热循环的应力作用下向基层内扩展,同时加剧氧化。随着冷热循环的继续进行,晶界氧化逐渐加剧,导致微裂纹扩展成更为明显的裂纹。     

热处理对Ti-Al-Sn-Zr-Mo-Si-X系合金性能的影响

研究了热处理对3种Ti-Al-Sn-zr-Mo-Si-X（X为ⅤB，ⅥB族一种或几种元素）系合金（A、B、C）室温拉伸性能的影响，对优化合金的热处理制度及优选热处理制度下3种合金的疲劳裂纹扩展行为也进行了探讨。结果表明，优选热处理制度下A、C合金的裂纹扩展速率差别不大，B合金560℃时效处理后，裂纹扩展速率比540℃时效处理的小。在相同热处理制度下，比较3种合金裂纹扩展速率的结果表明，IgΔK在1．2～1．5范围内B合金的抗疲劳裂纹扩展性能较优。     

Microstructures and mechanical properties of welded Fe-12Cr-20Mn austenitic stainless steel

The effects of welding on the tensile and fatigue properties of fully annealed and cold-worked Fe-12Cr-20Mn austenitic stainless steel were evaluated. Room temperature and 500 °C tensile tests and room temperature cantilever beam fatigue tests were accomplished on specimens that contained autogenous bead-on-plate welds. The tensile and fatigue properties of the fully annealed material were not significantly influenced by welding. The tensile properties of the welded cold-worked material were also not significantly affected by the presence of a weldment. However, welding caused a large reduction of the fatigue life of the cold-worked material. Fatigue cracks preferentially initiated at large Mn-Si inclusions that formed in the fusion zones of the weldments.     

汽车变速箱同步性能试验台的研制

汽车变速器同步性能直接影响车辆操控性,其量化测试十分重要。文中对变速箱同步器在换档过程中的同步时间,同步的轴向位移,同步时的换档力变化等参数借助于传感器进行采集。各路传感器信号经过调理电路转变为模拟量,然后经高速并行A/D转换为数字信号,并由单片机通过RS232上传给上位机进行数据分析并作出各项参数的曲线,对变速箱的性能作出评估。     

1.4%C超高碳钢显微组织与疲劳性能的研究

对1．4％C超高碳钢试样热处理后的疲劳极限与断裂韧性进行测定，观察了显微组织与试样断口。结果表明，经950℃淬火700℃回火热处理后，又经860℃正火处理，试验用钢的组织结构超细化且碳化物弥散均匀分布，获得良好的综合强度与韧性及较高的疲劳极限，断裂强度较40CrNiMo调质态提高48％，屈服强度提高15％，延性指标相当，是一种优良的结构钢材料。     

STUDY ON THE TENSILE FATIGUE DAMAGE OF QUASI—ISOTROPIC COMPOSITE LAMINATES

Quasi-isotropic. laminates have isotropic elastic properties in all in-plane directions. Therefore, this kind of laminate is widely used for structural elements. The simplest stacking sequence of quasi-isotropic laminates is [0/-60/60]s. When the direction of applied axial load to [0/-60/60]s laminate is inclined at a 30-degree angle, we have the other quasi-isotropic laminate [30/-30/90]s under axial load. The failure mechanisms of these two laminates are, however, entirely different from each other because these two laminates have different distribution of the interlaminar stresses. It was confirmed by tensile fatigue tests that the [0/-60/60]s laminate does not show any visible fatigue damage, but the [30/-30/90]s laminate develops edge-delamination during cyclic loading. The analytical results were in good agreement with the experimental results.     

300M钢腐蚀疲劳裂纹萌生的超载特性

本文对３００Ｍ钢在空气与３．５％ＮａＣｌ溶液中疲劳裂纹萌生的周期超载和单次超载特性进行了试验研究与理论分析。试验结果表明，３．５％ＮａＣｌ溶液中，单次超载所致腐蚀疲劳裂纹迟滞萌生的迟滞强度远小于周期超载的对应值。３．５％ＮａＣｌ溶液与空气中，超载迟滞强度均随超载比增大或等效应力幅水平的提高而增大，在腐蚀疲劳裂纹萌生寿命估算中，只考虑单次超载的迟滞规律，会得出大大保守的寿命估计，只有将单次超载和周期     

Effects of Thermal Exposure on the Tensile and Fatigue Properties of Cast Ti—47Al—2Cr—2Nb--0.15B Alloy

测量了铸造Ti—47Al—2Cr—2Nb-0．15B(原子分数，％)合金的高温疲劳强度以及650℃／100h和800℃／100h热暴露后的拉伸性能和疲劳强度，采用X射线衍射和扫描电镜等方法分析了经热暴露后合金基体组织的变化和表面层的结构．随暴露温度的提高，合金的室温塑性和疲劳强度降低，650℃附近有一转折点，大于650℃时上述性能加速下降；合金高温疲劳性能具有相似的变化规律．显微分析表明，在热暴露或高温疲劳实验时，表面形成的脆性层是导致合金性能降低的直接原因；而随温度的提高，表面层由渗氧层转变为氧化层是导致合金性能随温度变化出现转折的原因．     

高强度钢腐蚀疲劳裂纹扩展的温度效应和过载迟滞效应

通过在18,35和55℃蒸馏水中疲劳裂纹扩展试验,证明了超高强度钢30CrMnSiNi2A腐蚀疲劳具有强烈的温度效应,得到了ΔK值和温度对裂纹扩展速率影响的复合表达式。由于扩展速率数据拟合得到的表观激活能值(36.7kJ/mol)十分接近于氢在γ-Fe中的扩散激活能值,支持了氢助裂纹扩展的观点。对大气中疲劳裂纹扩展具有重要价值的过载迟滞效应,在腐蚀疲劳时显著地减小,在0.1Hz的低频率下尤其明显。