Phenols and Tertiary Amines: An Amazingly Simple Hydrogen‐Bonding Organocatalytic System Promoting Ring Opening Polymerization

A simple and easily available organocatalytic system was developed for the polymerization of lactide. In partnership with tertiary amines, phenol derivatives were demonstrated to be excellent single H‐bonding catalysts with high conversion within 24 h. In particular, ortho‐, meta‐ and meta,meta′‐trifluoromethylphenols revealed an amazing capacity for triggering the controlled ring opening polymerization (ROP) of lactide, through a fitted hydrogen‐bond with the monomer.     

聚乙二醇增塑聚乳酸的非等温结晶动力学研究

采用DSC方法对聚乙二醇(PEG)增塑聚乳酸的非等温结晶动力学进行了研究。结果表明,PEG的加入明显提高了聚乳酸的结晶速度。对所得数据分别用Ozawa方程和莫志深方法进行了处理,发现在给定温度范围里非等温结晶时,PLA/PEG主要是以均相成核的三维生长方式结晶;PLA的结晶速度随着PEG分子质量的增加而升高。     

反应性共混天然橡胶增韧聚乳酸

以过氧化二异丙苯(DCP)为交联剂,经哈克密炼机反应性共混,制备了聚乳酸/天然橡胶(PLA/NR)交联共混物。考察了交联剂DCP对PLA/NR共混物的熔体扭矩、形貌、结晶性、热稳定性和力学性能的影响。研究结果表明,添加DCP引发了PLA与NR体系的交联,熔体扭矩值增大。DCP对PLA/NR体系的热稳定性影响不大。当DCP含量为0.5%时,PLA/NR共混物的结晶度达到最高值,其冲击强度也达到最大值,是纯PLA的3倍。当DCP含量为2%时,共混物呈共连续相结构,其断裂伸长率达到最大值,相对于纯PLA提高了50%。     

碳纤维表面处理对C/PLA复合材料界面粘结强度的影响(Ⅱ)

对硝酸表面处理前后碳纤维增强聚乳酸（Ｃ／ＰＬＡ）复合材料的界面状态进行了研究。重点研究了碳纤维的硝酸表面处理对Ｃ／ＰＬＡ复合材料界面粘结强度的影响以及粘结机理。研究表明,硝酸表面处理可使复合材料的界面粘结强度大幅度增加,复合材料的冲击强度、弯曲强度、弯曲模量和剪切强度亦有不同程度的提高。ＸＰＳ研究发现,央纤维与ＰＬＡ基体间有化学反应发生。界面化学反应程度的增加是复合材料界面粘结强度提高的主要原因;此外,碳纤维表面粗糙度的增加也对界面粘结强度的提高有一定的贡献。     

PEG增塑PLA/成核剂复合体系的结晶行为和力学性能

通过溶液共混法制得了一系列PLA复合物,并利用差示扫描量热法(DSC)、配带热台的偏光显微镜(POM)和X射线衍射法(XRD)等研究了PLA/PEG和PLA/PEG/成核粒子的结晶行为,又通过力学实验分析了成核剂对PLA/PEG的机械强度的影响.结果表明:增塑剂PEG能加强PLA的结晶能力,但是晶体结构不完善;成核粒子的添加改善了增塑体系的晶体结构和结晶速度,从而有效地提高了复合材料的力学性能;添加Talc和LAK的三元共混物的半结晶时间t1/2仅为1.5min和1.7min,过冷度仅有47.7℃和39.3℃,结晶度达到了34.1%和36.5%,拉伸强度提高到了60.28Mpa和53.09Mpa.