注射成形粘结NdFeB磁体:工艺·性能·应用

综合介绍了几种适于注射成形粘结NdFeB磁体的磁粉制备方法及特点；讨论了粘结剂、改性剂及磁场取向对注射成形NdFeB磁体最终磁性能的影响及其应用市场。在此基础上，指出了今后开展研究工作的方向。     

籼米淀粉超微粉体的制备及其性质

研究了籼米淀粉超微粉体的一种新的制备方法 ,通过正交实验确定了酶处理淀粉的最佳条件 ,考察了淀粉的溶解度和膨润力。结果表明 ,酶处理淀粉的最佳工艺参数为 :水解温度４５℃ ,时间为２５ｈ ,酶用量为水解淀粉的４５%。随着粒径的减小 ,淀粉的溶解度增大 ,膨润力下降。     

化学还原法制备纳米铜粉的研究

本文采用KBH4在液相中化学还原CuSO4,并加入KOH和络合剂EDTA ,制得了纳米级的纯净的铜粉 ,通过调整反应物的浓度 ,可以消除Cu2 O等杂质。制备的纳米铜粉还存在一定程度的团聚 ,需试验加入分散剂来改善。     

高合金钢铸造用涂料的试制与开发

介绍了炉爪用合金钢1Cr25Ni20Si2Re,导板用合金钢2Cr32Ni5采用串箱铸造过程中，有关镁砂粉涂料和石英粉涂料的试制。结果表明：镁砂粉涂料为不透气涂料，不太适用，而合理配方的石英粉涂料使用性能良好。     

超细粉碎技术现状及发展趋势

综述了国内外超细粉碎技术及设备的现状、进展,指出了其发展趋势,从工作原理、结构特点等方面详细介绍了超细粉碎典型设备,同时又指出了近年来国内外在此领域中的新进展,基于现存问题指出了今后超细粉碎研究的方向。     

Experimental Study on Polymer Artificial Bone with HA Coated and Fiber Liners

1Introduction HA(hydroxyapatite)wasakindofbioactiveceram ics,whichhadexcellentbiocompatibilityandtissueaffin ityinthatitscomponentsweresimilartothoseofhuman bone[1].Soitwasthebestknownhumanbonesubstitute,andunprecedentedeffecthadbeenharvestedinrecenttwo d…     

Plasma Sprayed Hydroxyapatite Coatings with Nano-hydroxyapatite Prepared by Ultrasonic Precipitation Process

Nano-particle hydroxyapatite （ HA ） was prepared with a novel ultrasonic precipitation process and the as-prepared nanopowder was used to produce hydroxyapatite （ HA ） coatings on titanium substrate via plasma spraying. The phase and the microstructare of the coating were characterized by X- ray diffraction （XRD） and scanning electron microscopy （SEM）. Results showed that spherical particles could be prepared by ultrasonic precipitation process; and a corresponding dense HA coating with molten surface and low-porosity cross-section structure was acquired. During the plasma spraying process, new phases of Ca3 （ PO4 ）2 and Ca2 P2O7 were generated. After heat-treating at 800℃ for 1 h, the contents of Ca3 （ PO4 ）2 and Ca2 P2O7 decreased while HA content increased. Tensile adhesion tests showed that the plasma sprayed coating prepared with the spherical nanoparticles exhibited high tensile bond strength.     

Water‐Stable,Magnetic Silica–Cobalt/Cobalt Oxide–Silica Multishell Submicrometer Spheres

A method to produce monodisperse magnetic composite spheres with diameters from less than 100 nm to more than 1 μm in water solution is reported. The spheres consist of a dielectric silica core and a cobalt/cobalt oxide shell which can be protected from further oxidation with an outer shell of silica or, alternatively, they can be covered with the polymer polyvinylpyrrolidone as a stabilizer. The formation of a uniform magnetic shell proceeds with the adsorption of metallic cobalt seeds, produced by the reduction of cobalt chloride with sodium borohydride, on a self‐assembled layer of polyelectrolytes on the silica core. In the second step, an outer silica shell can be formed by the hydrolysis and condensation of (3‐aminopropyl)trimethoxysilane and tetraethoxysilane. The double‐shell composite spheres show excellent sphericity, monodispersity, and a magnetic hysteresis loop at room temperature.     

络合沉淀法制备BaTiO_3超细粉末

在分析ＢａＴｉＯ_３前驱体形成机理的基础上，提出了以草酸作为络合剂，用络合沉淀法制备超细ＢａＴｉＯ_３新工艺。用化学分析法测定产物Ｂａ／Ｔｉ比，用ＸＲＤ、ＴＥＭ、ＢＩ－９０激光散射粒度仪对产物的晶型、粒度及形貌进行表征。结果表明：采用该法合成的前驱体，微观组分确定，粒径小，粒度分布窄，近似球形，煅烧后为高纯超细ＢａＴｉＯ_３粉末。     

激光辐照制备搪瓷涂层

激光辐照制备的搪瓷涂层表面粗糙,与金属基材结合牢固。一般由 Si,Al,Na,K,B,F,O等元素组成。在激光辐照过程中 K,Na 明显地挥发,从而在涂层中的含量明显减少;Co,Ni,主要分布在界面附近;Fe 元素也由基材进入涂层,呈梯度状分布,在界面过渡区含量很高,在涂层内含量很低。搪瓷涂层的形成与激光辐照参数,特别与激光功率间存在极为密切的关系;只有选用合理的参数,才能制得搪瓷涂层。