纳米CaSO_4晶须改性聚氨酯密封胶的制备

通过三种聚醚制成的密封胶进行对比,具体考察了CaSO4晶须对密封胶力学性能的影响。结果表明,在单组分湿固化聚氨酯密封胶中添加纳米CaSO4晶须后,密封胶的剪切强度得到提高,硬度和弹性变化不大。使用CaSO4晶须替代气相二氧化硅,在降低成本的同时,密封胶的触变性仍然很好。     

改性细菌纤维素硫酸酯对Pb(Ⅱ)吸附性能的影响

以廉价且资源丰富的细菌纤维素为原料,研究制备了改性细菌纤维素硫酸酯吸附材料,并对其进行表征分析。以典型重金属污染物Pb(Ⅱ)为去除目标,考察了不同反应时间、溶液p H和反应温度等对改性细菌纤维素吸附Pb(Ⅱ)的影响。结果表明:经改性后细菌纤维素的吸附性能有所增加;其对Pb(Ⅱ)的平衡吸附量随p H的增大而增加,随温度的增加而减小;吸附过程符合拟二级反应方程和Langmuir吸附等温方程。     

镁质低品位铁镍硫化矿的活化工艺及机理

细菌浸出是镁质低品位铁镍硫化矿的潜在处理方案之一。针对该矿石浸出活性较低的问题,研究了硫酸预浸出和硫酸铵焙烧预浸出2种活化方案,并与细菌直接浸出(空白试验)做了比较。结果表明,2种活化方案都有利于金属回收,但硫酸铵焙烧预浸出方案的活化效果更优:浸出时间为8 d时,Ni、Cu和Mg的浸出率分别为90.2%、89.56%和61.19%,分别高于硫酸预浸出方案2.08%、12.2%和8.95%。矿石中的Mg主要在硫酸铵焙烧预浸出阶段进入溶液,细菌对Mg浸出的影响不大。XRD和能谱分析表明:浸出渣中Ni和Cu的残留量很低,Mg主要存在于难浸出的蛇纹石之中。     

Application of image analysis based on SEM and chemical mapping on PC mortars under sulfate attack

The degradation mechanisms of cementitious materials exposed to sulfate solutions have been controversial, despite considerable research. In this paper, two methodologies of image analysis based on scanning electron microscope and chemical mapping are used to analyse Portland cement mortars exposed to sodium sulfate solution. The effects of sulfate concentration in solution and water to cement ratio of mortar, which are considered as the most sensitive factors to sulfate attack, are investigated respectively by comparing the macro expansion with microstructure analysis. It is found that the sulfate concentration in pore solution, expressed as sulfate content in C-S-H, plays a critical role on the supersaturation with respect to ettringite and so on the expansion force generated.     

Preparation of solid polyferric sulfate from pyrite cinders and its structure feature

1　INTRODUCTIONCoagulationisanessentialprocessintheoverallsolid liquidseparationschemeinwaterandadvancedwastewatertreatment .Hydrolyzingmetalsalts ,suchasferriccoagulants ,canpromotetheformationofag gregates.WhenFesaltsaredissolvedinwater,themetalironhydrates ,coordinatingsixwatermoleculesandforminganaquometalion ,canthenhydrolyzeandformmonomericand polymericferricspecies ,whichishighlydependentonpHofthesolution .Itispossibletodescribetheformationofseveralhydrolysisspecies ,suchaspositiv…     

Hot-Corrosion Resistance of a Sputtered K38G Nanocrystalline Coating in Molten Sulfate at 900°C

The hot-corrosion behavior of a nanocrystalline coating of K38G alloy, prepared by magnetron sputtering and cast K38G in molten 75 wt.% Na₂SO₄+25 wt.% K₂SO₄ at 900°C was studied. The coating eliminated internal sulfidation during the early stage of corrosion as a result of the formation of a continuous and compact Al₂O₃ scale. The nanocrystallization of K38G alloy prolonged the incubation of breakaway corrosion and improved the corrosion resistance of K38G. The relevant corrosion mechanism is discussed.     

硫酸盐还原菌在不同氧环境下对A3钢腐蚀的研究

通过静态培养实验,研究了在不同的氧环境下,硫酸盐还原菌对A3钢腐蚀的规律。实验结果表明,在相同的培养基中,严格厌氧条件下的硫酸盐还原菌对A3钢的腐蚀速率与连续的厌氧-有氧交替变换条件下的硫酸盐还原菌腐蚀的速率相差不是十分明显。     

Role of platinum in the Na2SO4-Induced hot corrosion resistance of aluminum duffusion coatings

Electrochemical corrosion measurements have been carried out with Pt-containing and Pt-free Al-diffusion coatings on IN 738 LC in a 90Na₂SO₄+ 10K₂SO₄ (mol%) melt at 1173 K. Pt improves the resistance to basic fluxing while there are no significant differences between both coating types in their resistance to acidic fluxing. The corrosion resistance of the Pt-containing coating is also higher in the passive potential region where protective scales rich in Al₂O₃ are formed. The reason for the different behavior of both coating types appears to be related to the high corrosion resistance of the Pt-rich surface layer of the coating and an increased Al₂O₃ content in the scale of the Pt-containing type.     

纳米氢氧化镁的制备与结构表征

以硫酸镁和氨水为原料,以获得纳米氢氧化镁粒子;并采用X射线和透射电镜等对颗粒形态进行表征.得出了制备纳米氢氧化镁的最佳条件.研究成果为纳米级氢氧化镁下一步的深入研究打下了良好基础.     

硫酸盐还原菌对海底土中锌腐蚀的影响

利用微生物分析、交流阻抗测试技术、扫描电镜及表面能谱等方法，在室内模拟条件下研究了海底土中硫酸盐还原菌对锌腐蚀的影响，以及在以接菌及灭菌的海底土构成的宏电池腐蚀中锌的腐蚀行为。180d的试验结果表明：海底土中硫酸盐还原菌增强锌的腐蚀，锌在接菌泥中的平均腐蚀速率及点蚀深度均大于在灭菌泥中的平均腐蚀速率及点饰深度，平均腐蚀速率相差7．0倍，点蚀速率相差15．0倍以上。在接菌和灭菌海底土构成宏电池时，接菌海底土中锌作为阳极，腐蚀速率比自然腐蚀状态下有所增大，加速率为12．7％，而在灭菌海底土中锌作为阴极，腐蚀速率比自然腐蚀状态下有所减小。