长距离油、气、水混输管道内壁流动腐蚀的研究进展

就近几十年来，多相流管线的流动腐蚀（CO2腐蚀，H2S腐蚀，腐蚀/冲蚀协同作用），腐蚀/冲蚀数学模型和设计准则，腐蚀检测，腐蚀防护与控制技术等方面的研究进展进行了综述。指出了当前研究中所存在的一些问题，就多相流的研究方向提出了相应的建议。     

高温预析出对Al-Zn-Mg系铝合金时效硬化和应力腐蚀的影响

研究了高温固溶后降温处理工艺对中强可使预析出LC52和7039铝合金的组织、时效硬化和应力腐蚀的影响。金相观察发现,高温预析出可优先在晶界处产生,并提高随后时效状态下晶界析出相的不连续分布程度,温度降低到一定程度晶内和晶界产生大量析出。合金拉伸性能和应力腐蚀结果表明,预析出在保持强度和塑性的同时,可提高抗应力腐蚀性能。而预析出温度降低,合金强度呈下降趋势。     

巨型结构的抗震分析

采用ANSYS有限元程序对巨型框架结构、巨型框架隔震结构进行了抗震动力时程分析,讨论了两种结构在多条地震波作用下的动力位移及内力等地震响应,其计算结果对于确保巨型框架结构的抗震安全性具有较大的意义,对巨型框架结构的抗震设计有较大的参考价值。     

输油管线防垢防腐及新药剂试验

讨论影响输油管线结垢和腐蚀的主要因素，从理论上分析了结垢形成，推导计算结垢量的公式。介绍了输油管线防止硫酸钡垢的清防方法。     

EIS evaluation of the filiform corrosion of aluminium coated by a cataphoretic paint

Filiform corrosion is mainly considered as a cosmetic attack and is undesirable in most applications. The initiation and propagation of the filaments are related to different parameters such as the presence of defects, the permeability of the coating to water and oxygen, the adherence of the paint system and the presence of salts.

The aim of this work is to study the behaviour of painted aluminium samples towards filiform corrosion or delamination. The 6082 Aluminium alloy was selected and the samples were covered with a cataphoretic epoxy primer without lead (PPG Industries France). Prior to the application of the electrocoat, the samples were pre-treated by a commercial Zr/Ti or chromate conversion treatment or simply etched with a commercial acid etching product.

Filiform corrosion was studied by the normalized test (ISO/DIS 4623): painted and scratched samples were inoculated in HCl and exposed in a constant humidity chamber at 40 °C and 82% RH for 3 weeks. After exposure the samples were subjected to a visual and optical microscopic examination.

Electrochemical impedance spectroscopy was used to study the sensitivity to filiform corrosion. The operating mode of this test is similar to the normalized one. The samples were scratched before inoculation for 1 h in HCl and then exposed to the humidity chamber for a maximum of 4 days. The samples were tested by EIS in an acidified 0.1 M Na₂SO₄ electrolyte solution. The resulting impedance spectra were analyzed with an appropriate equivalent electrical circuit which allows the evaluation of the exposed metallic surface area, directly related to the extent of filiform corrosion or delamination. Different parameters were varied: the exposure time in the humidity chamber; the immersion time in the electrolyte sulphate solution as well as its pH and the coating thickness.     

Random errors caused by temperature in magnitude of principal strains evaluated ith 3-element strain gauge rosettes

The effects of the uncertainties associated ith the apparent strain and gauge factor data, given by the manufacturer, in the evaluation of principal strains are examined. Principal strains are obtained by a reduction of the strains measured ith electrical resistance strain gauge rectangular or delta rosettes. The theoretical analysis points out the relevance of the effects caused.     

Atmospheric corrosion of reference metals in Antarctic sites

This paper presents the results obtained at three Antarctic test sites participating in the “Ibero-American Map of Atmospheric Corrosiveness” (MICAT), a project on atmospheric corrosion carried out during the period 1988–1994 at some 70 sites distributed across 12 countries of the Latin-American region, Spain and Portugal. The three Antarctic sites are located near the coastline.The singular climatic characteristics of Antarctic regions are related with the purity of the air, the absence of rainfall and the formation of ice on the metallic surface during an important part of the exposure time. However, electrochemical activity is possible below ice layers. This situation affects the structure and morphology of corrosion product films and the resulting corrosion rates of metallic surfaces.     

Corrosion Behavior of 316LN and 316 Stainless Steels During Long-term Exposure to Aerated 0.5 M NaCl Using Electrochemical Noise Technique

In the present work 316LN as well as 316 stainless steel (SS) coupons each of dimensions (0.025 × 0.018 × 0.006 m³) in well-polished condition were used as two nominal electrodes which were immersed in the aerated solution of 0.5 M NaCl. Correlated current and potential electrochemical noise (EN) signals were collected at 1 Hz sampling frequency for 1 h daily over a period of 30 days. The detrended EN data were used to calculate the noise resistance (R _N) as well as the spectral noise resistance at zero frequency (R _SN^o) values and other statistical parameters. To study the nature of pits and distribution of their diameters as well as depths, extensive observations of the pitted and the blank specimens were carried out using Confocal Laser Scanning Microscopy (CLSM). The current and the potential records of the two alloys showed distinct differences in their corrosion behavior. It was observed that within less than 4 h of immersion, 316SS showed signals indicative of unstable pitting and onset of stable pitting was noticed after 48 h of exposure. However, until about 24 h, 316LN showed just the random signals and unstable pitting was observed after 28 h. The signals clearly indicated continuous growth of the stable pits in 316SS as against the repassivation of the unstable pits in 316LN after 7 days exposure. It was observed that R _N values showed a continuous decrease in the case of 316SS, but were quite stable in the case of 316LN over the exposure period. Concurrent to these observations it was observed that 316SS specimen was extensively pitted. The frequency distributions of pit diameters as well pit depths were observed to be highest at 10-20 μm and 5-10 μm, respectively. However, pits with as large as 70-80 μm diameter and as deep as 20-25 μm too were observed. No pits were observed in case of 316LN even after 30 days of exposure, an observation that corroborates well with the stable R _N values. Thus, in the present investigation, the long-term tests using EN technique coupled with CLSM studies conclusively prove that many unstable pits initiated in 316SS turn into stable ones resulting in insidious localized corrosion attack whereas the unstable pits initiated in 316LN get passivated in the simulated coastal environment.     

聚苯硫醚复合涂层的耐磨性能

研究了用固体润滑石墨、碳化硅、二硫化钼等填料改性的聚苯硫醚 (PPS)涂层的耐磨性能。实验结果表明 ,聚苯硫醚复合涂层具有优良的耐磨性 ;加入适量 ( 3 0 % )的石墨、碳化硅等固体润滑剂 (石墨 :碳化硅 =2∶3 ) ,可以有效提高涂层的耐磨性能 ,而二硫化钼和三氧化二铬的减摩效果更佳     