The improvement of the self-healing ability of MoSi2 coatings at 900–1200 °C by introducing SiB6

The brittleness of MoSi₂ ceramic and the thermal mismatch between MoSi₂ coating and C / C composite lead to brittle cracking of the coating at 900−1200 °C. This problem has been overcome in this studyby introducing submicron-SiB₆ into the coating. The pre-fabricated cracks and a kinetics model of hot-pressed SiB₆-MoSi₂ ceramic could quantitatively predict the glass growth and crack healing. As expected, enhancing temperature and SiB₆ content increased the growth rate of the borosilicate glass and the crack healing ability of MoSi₂ ceramic, which was ascribed to the lower oxidation activation energy and larger specific surface area of submicron-SiB₆. For the plasma sprayed coating, SiB₆ with submicron structure was benefit for cracking inhibition and formation of borosilicate glass during oxidation, reducing the oxygen permeability and the consumption of inner coating. Hence, the 15 % SiB₆-MoSi₂ coatings raised the protection times to 84 and 120 h at 900 and 1200 °C respectively, presenting favorable oxidation protective performance.     

Behavior of 316L stainless steel containing corrosion pits under cyclic loading

The environmental performance of 316L grade stainless steel, in the form of tensile specimens containing a single corrosion pit with various aspect ratios, under cyclic loading in aerated chloride solutions is investigated in this study. Results from environmental tests were compared and contrasted with those obtained using finite element analysis (FEA). Fractography of the failed specimens obtained from experiments revealed that fatigue crack initiation took place at the base of the shallow pit. The crack initiation shifted towards the shoulder and the mouth of the pit for pits of increasing depth. This process is well predicted by FEA, as the strain contour maps show that strain is the highest around the centric strip of the pit. However, for shallow pits, local strain is uniformly distributed around that strip but begins to concentrate more towards the shoulder and the mouth region for increasingly deep pits.     

Hot corrosion Type II of FeCr‐based model alloys for boiler and heat exchanger applications

The hot corrosion Type II of the alloys FeCr20, FeCr20Ni10, FeCr20Ni20, and FeCr20Co10 is investigated at 700°C in air + 0.5% SO₂ with deposits consisting of Na₂SO₄ and a eutectic mixture of Na₂SO₄ and MgSO₄ for 24, 100, and 300 h. The alloying elements nickel and cobalt have a positive influence when tests are conducted using a MgSO₄‐Na₂SO₄ deposit. In this case, they reduce the metal loss and increase the time to the propagation stage. In contrast, when the alloys are exposed with a Na₂SO₄ deposit, these alloying elements increase the metal loss and allow for the transition to the propagation stage because they can form molten phases with the Na₂SO₄. During the incubation stage an oxide scale forms on the FeCr20 alloy, which is thicker than the one formed during exposure without a deposit, and iron oxides are observed, which precipitate in the deposit. The propagation stage occurs by a dissolution and precipitation mechanism forming localized pitting attack. Iron is the main species that dissolves and precipitates, while chromium remains mainly as an oxide beneath the initial surface. The additional elements are found in the pit and in the salt deposit.     

300M超高强钢在中性盐雾环境中的腐蚀行为及机制

摘要：为了研究300M超高强钢在中性盐雾环境中的腐蚀行为及腐蚀机制，采用失重法，宏观、微观腐蚀形貌分析，三维表面轮廓分析及电化学分析的研究方法，来表征腐蚀实验现象并进行分析。结果表明：300M超高强钢在中性盐雾环境中的腐蚀产物为FeOOH、Fe2O3、Fe(OH)3和Fe3O4；腐蚀速率随着腐蚀时间逐渐降低，腐蚀后期（72h）腐蚀速率降低50%；腐蚀初期以点蚀为主，点蚀坑通过横向扩展，逐渐发展为后期的均匀腐蚀，腐蚀表面形貌呈沟壑状；外腐蚀层对基体的保护能力很弱，Cr元素在锈层靠近基体的一侧偏聚使内腐蚀层具有一定的抗腐蚀性。     

Corrosion of hot-dip-galvanised steel and zinc alloy-coated steel in ammonia and ammonium chloride

There are many potential causes of corrosion in animal buildings. Animals exhale large quantities of moisture into the air creating high relative humidity in the building if the moisture is not properly vented. High humidity increases the potential for condensation. In addition, ammonia may be found in large quantities in animal buildings. Ammonia is released from manure and urine. In addition, ammonium chloride is used as a nitrogen source in fertilisers. In this study, the atmospheric corrosion of hot-dip-galvanised steel and zinc alloy-coated steel such as zinc–aluminium and zinc–aluminium–magnesium has been studied in atmospheres containing different levels of ammonia. Investigations have also been conducted at different levels of ammonium chloride. The results are discussed in view of the mechanisms of corrosion of zinc and zinc alloy-coated steel in ammonia and ammonium chloride-containing environments.