Inhibition of atmospheric corrosion of mild steel by sodium benzoate treatment

The objective of this study was to evaluate the effectiveness of sodium benzoate as an inhibitor to slow down or prevent atmospheric corrosion/discoloration of the local mild steel during storage in the Arabian Gulf region. Test specimens were prepared from locally produced reinforcing steel products. The inhibitor solution was applied on steel specimens at a concentration of 100 mM for 1 day at room temperature. Wooden exposure racks were used to hold as-received and inhibitor-treated specimens during atmospheric exposure for different periods. Corrosion was evaluated through weight loss determination and electrochemical technique. As expected, the Arabian Gulf atmosphere was corrosive on the as-received local mild steel. On the other hand, treatment of steel with sodium benzoate lowered its corrosion rate during initial days of its exposure to atmosphere. However, atmospheric corrosion inhibition performance of sodium benzoate deteriorated with exposure time after 30 or more days of atmospheric exposure, and the corrosion rates of sodium benzoate-treated specimens reached that of the unprotected specimens at the end of 90 days of atmospheric exposure.     

纤维混凝土在水工建筑工程中的应用(上)

概述改性混凝土垢发展情况，介绍纤维混凝土在国内外水工建筑物上的应用实例，提出钢纤维增强钢筋混凝土水工建筑结构强度计算方法。包括受弯构件正截面强度，斜截面抗剪强度的计算；重点介绍了网状钢纤维增强混凝土（FOC）在水工建筑物上的应用，包括在渡槽，闸门，小型拦河坝，轻型岸型等工程上的应用实例，T新梁正斜截面的强度计算，板材承载力计算的方法。     

影响掺矿渣的钢纤维砼强度的主要因素

研究结果表明 :水胶比、胶凝材料用量、钢纤维掺量、矿渣代水泥量对钢纤维砼强度影响显著。当矿渣取代水泥 10 %时 ,钢纤维砼强度最高。经试验选择出一个具有良好和易性和较高强度 (118MPa)的钢纤维砼配合比 ,为掺磨细矿渣的中含量超短异形钢纤维砼的设计和施工提供了试验依据     

45钢表面超音速电弧喷涂Ti-Al涂层的组织与性能研究

采用自行开发研制的超音速电弧喷设备，在45钢表面制成了钛铝合金复合涂层。并利用金相显微镜、X射线衍射仪、扫描电镜、电子探针，对涂层的成分、相结构、显微组织及其结合强度、显微硬度进行了研究。结果表明，利用超音速电弧喷涂设备，可以在45钢表面形成 度高、孔隙率低，结合强度较好和硬度高的Ti-Al合金涂层。     

轻型钢骨结构低层住宅设计荷载分析

本文讨论了北美低层钢骨结构住宅结构设计的荷载问题，包括各类荷载的取值和计算方法，以及荷载组合模式，并提出了在我国相关规范没有出台前，在国内进行设计时应该注意的一些问题。     

薄板坯连铸连轧流程Ti微合金化高强钢开发与应用

在薄板坯连铸连轧流程上，经过对Ti微合金化技术研究，有效解决了Ti微合金化强度性能波动大的问题，开发出屈服强度450～700MPa高强钢。对试制钢组织性能和工业应用分析研究，表明该产品通板性能良好，通板强度差30MPa左右；成形性能良好，d=0时冷弯测试全部合格；同时还具有良好焊接性能，焊接后，强度波动较小，均在母材部位断开；试制钢显微组织为珠光体和铁素体，晶粒均匀细小，平均尺寸为4～8／μm；实物质量满足集装箱和汽车制造行业要求，具有广阔市场前景。     

Amorphous diffusion bonding of steel pipe and its impact toughness

An iron-based amorphous foil (FeNiCrSiB) was used as an interlayer for the amorphous diffusion bonding of low carbon steel pipes under argon flux. The microstructure and mechanical properties of the joint were analyzed using an electron probe micro-analyzer (EPMA), tensile test, bending test and impact test. The results show that the joint microstructure resembles that of the base metal and no precipitates form at the joint. Melting point depressants (B, Si) diffuse far away from the joint and the base metal element is homogenous across the joint. The joint impact toughness is greater than the base metal toughness and the mechanical properties of the joint are similar around the pipe.     

Atmospheric corrosion of reference metals in Antarctic sites

This paper presents the results obtained at three Antarctic test sites participating in the “Ibero-American Map of Atmospheric Corrosiveness” (MICAT), a project on atmospheric corrosion carried out during the period 1988–1994 at some 70 sites distributed across 12 countries of the Latin-American region, Spain and Portugal. The three Antarctic sites are located near the coastline.The singular climatic characteristics of Antarctic regions are related with the purity of the air, the absence of rainfall and the formation of ice on the metallic surface during an important part of the exposure time. However, electrochemical activity is possible below ice layers. This situation affects the structure and morphology of corrosion product films and the resulting corrosion rates of metallic surfaces.     

螺栓角钢钢节点的三维非线性有限元分析

对螺栓角钢钢节点半刚性连接采用非线性有限元分析方法 ,对连接中的主要构件的顶部、底部、腹板角钢、高强螺栓、梁翼缘、柱翼缘和柱翼缘加劲肋进行三维非线性有限元精细模拟 ,针对有无柱加劲肋、有无腹板角钢等几种连接的情况进行比较分析 ,探讨了螺栓角钢半刚性连接的受力性能。     

IF钢冷轧及再结晶初期微观组织的TEM研究

采用透射电子显微镜对不同压下量和再结晶初期的IF钢样品进行了研究．结果表明：无论是在较小形变量下还是在较大形变量下，形变不均匀性是普遍存在的；冷变形程度不同，织构组分不同，TEM形貌也不同；在再结晶的最初期，冷轧的形变组织演变为近乎等轴的亚晶，优先形成{111}〈uvw〉取向的晶核，晶核逐渐吞并周围的形变基体而长大，最终形成再结晶γ-纤维织构．