Spectroscopic analysis of a novel Nd3+-activated barium borate glass for broadband laser amplification

Spectroscopic parameters of a novel Nd³⁺-activated barium borate (BBONd) glass have been analyzed for broadband laser amplification. The Judd–Ofelt (JO) intensity parameters were determined through a systematic analysis of the absorption spectrum of Nd³⁺ ions in the BBONd glass. High values of the JO intensity parameters reveal a great centro-symmetrical loss of the Nd³⁺ sites and high covalency degree of the ligand field. The very high Ω₆ intensity parameter value makes evident both a great structural distortion of the Nd³⁺ sites and a strong electron–phonon coupling between Nd³⁺ and free OH⁻ ions, which is consistent with the phonon energy maximum (3442.1 cm⁻¹) recorded by Raman spectroscopy. This strong electron–phonon coupling favors high effective bandwidth and gain bandwidth values of the laser emission (⁴F_3/2 → ⁴I_11/2) of Nd³⁺ ions. The electric-dipole oscillator strengths of all the Nd³⁺ absorption transitions, and in particular that of the hypersensitive transition (⁴I_9/2 → ⁴G_5/2), are enhanced by this great structural distortion of the host. Broadband laser amplification of the ⁴F_3/2 → ⁴I_11/2 emission (1062 nm) of Nd³⁺ ions in the BBONd glass pumped at 805 nm (⁴I_9/2 → ⁴F_5/2 + ²H_9/2) is evaluated through the main fluorescent parameters in competition with non-radiative processes. In general, the BBONd glass exhibits spectroscopic parameters comparable with those reported in the literature for broadband laser amplification into the IR region.     

Sb_2O_3对富钛型钛酸锶钡基陶瓷结构及性能的影响

采用传统固相法制备Sb_2O_3掺杂(Ba_(0.7_Sr_(0.3))Ti_(1.005)O_3系介电陶瓷,通过扫描电镜、X线衍射仪及LCR测试系统,研究不同含量的Sb_2O_3及烧结工艺参数对TiO_2过量的钛酸锶钡体系微观结构及介电性能的影响。结果表明,随Sb_2O_3掺杂量增大,(Ba_(0.7)Sr_(0.3))Ti_(1.005)O_3陶瓷由立方钙钛矿结构单相固溶体转变为多相化合物。在TiO_2过量的(Ba_(0.7)Sr_(0.3))Ti_(1.005)O_3陶瓷中,Sb~(3+)进入钙钛矿晶格A位。Sb_2O_3添加量较大时,(Ba_(0.7)Sr_(0.3))Ti_(1.005)O_3基陶瓷晶粒异常长大,粒径分布不均匀,且有柱状晶粒出现。随Sb_2O_3掺杂量增大,(Ba_(0.7_Sr_(0.3))Ti_(1.005)O_3基陶瓷居里温度及介电常数峰先增大后减小。提高(Ba_(0.7_Sr_(0.3))Ti_(1.005)O_3基陶瓷的烧结温度并延长保温时间有利于改善Sb_2O_3掺杂量较高时(Ba_(0.7_Sr_(0.3))Ti_(1.005)O_3基陶瓷室温的介电性能。     

Preparation and characterization of aluminum borate whiskers reinforced ceramics with MnO2 addition

Ceramics with aluminum borate whiskers (ABWs) were prepared from H₃BO₃ and Al₂O₃ reagent, with and without 6 wt% MnO₂ used as an addition. The microstructures, phase composition, and crystal structure of the ceramics were analyzed via scanning electron microscopy, energy dispersive spectroscopy, and X-ray diffraction, respectively. The results show that MnO₂ is an effective addition for enhancing the flexural strength of ceramics. The MnO₂ could lead to the distortion of lattice, and improve the mechanical strength via a solid solution strengthening mechanism. Moreover, the content of H₃BO₃ and the sintering temperature were also key factors in the manufacture of optimal ceramics. The ceramic made from 6 wt% MnO₂ addition, 25 wt% H₃BO₃, and sintered at 1200°C, showed the highest flexural strength of 88.5 (±1.9) MPa, and had a bulk density of 1.64 g/cm³ and porosity of 44.2%.     

新型近红外咔唑吲哚类硼酸酯荧光探针的合成与表征

以咔唑为起始原料,经过与亲电取代反应、Vilsmeier反应、溴化反应以及与双联频哪醇硼酸酯的偶联反应,合成了N-乙基咔唑-3-甲醛-6-苯硼酸酯,以合成的N-乙基咔唑-3-甲醛-6-苯硼酸酯,以合成的乙基取代咔唑硼酸,以合成的乙基取代咔唑硼酸酯醛与1,2,3,3-四甲基-3H-吲哚碘化物缩合,合成了一种新型近红外咔唑吲哚啉类硼酸酯荧光探针,其结构经过1H NMR,IR进行了表征。     

超细(Ba,Sr,Cd)TiO3基多层陶瓷电容器陶瓷的研究

采用溶液-溶胶-凝胶法制备(Ba0.70Sr0.25Cd0.05)TiO3纳米粉体,利用所得到的纳米粉体研究了(Ba0.70Sr0.25Cd0.05)TiO3基多层陶瓷电容器用超细陶瓷的制备.对比研究了超细电容器陶瓷和传统固相法电容器陶瓷的性能.采用扫描电镜分析了两种方法得到的陶瓷的显微结构.结果表明:采用纳米粉体制备的(Ba0.70Sr0.25Cd0.05)TiO3基电容器陶瓷具有晶粒尺寸约为1μm,其性能为:介电常数为140 9.44,介质损耗为0.017 5,陶瓷的密度是5.22 g*cm-3,烧结温度为1300 ℃,大大降低了烧结温度,比传统固相法的陶瓷性能有较大的改善.     

纳米掺锶羟基磷灰石的制备及其吸附性能研究

采用溶胶-凝胶-超临界流体干燥法制备了粒径在100 nm以下的纳米掺锶羟基磷灰石(SrHAP),以牛血清白蛋白(BSA)为吸附目标,研究了纳米SrHAP的吸附性能.结果发现在偏酸性条件下,纳米SrHAP比纳米HAP对BSA的吸附量大,表明掺锶后吸附性能提高;但在碱性条件下,纳米SrHAP对BSA的吸附量减小.纳米SrHAP对BSA的吸附是个快速吸附过程,增加Sr/[Ca Sr]原子比XSr和BSA的起始浓度有利于吸附,升高温度不利于吸附.     

纳米掺锶羟基磷灰石的制备及其抗菌性能研究

以硝酸钙、氯化锶、磷酸氢二氨等为原料,采用溶胶-凝胶-超临界流体干燥法,制备了纳米掺锶羟基磷灰石(SrHAP).通过元素含量分析、TEM、XRD、FT-IR等手段对其结构进行了表征,分析了锶的掺入对羟基磷灰石(HAP)的结构、晶形及结晶度的影响;研究了HAP掺入锶后对大肠杆菌、金黄色葡萄球菌、乳酸杆菌的抗菌性能.结果表明:采用溶胶-凝胶-超临界CO2干燥法,可制备结晶性较好的纳米HAP和Sr/[Sr Ca]原子比为0.5的纳米SrHAP;在给定的条件下,锶可以按化学计量比掺入到HAP的结构中;HAP掺入锶后,其主要官能团红外光谱吸收峰的振动频率降低,晶形从HAP的短棒状改变为SrHAP的针状,结晶度降低,对大肠杆菌、金黄色葡萄球菌、乳酸杆菌的抗菌性能提高.     

用三氟化硼乙醚络合物合成硼酸三甲酯

试验研究了常压下,在甲醇介质中,用甲醇钠与三氟化硼乙醚络合物反应制备硼酸三甲酯的工艺流程,并探索其最佳工艺条件.结果利用气相色谱、色谱-质谱联用、红外光谱等分析表征手段,鉴定反应产物确实是硼酸三甲酯.并摸索其最佳工艺条件为：反应温度55℃;回流时间32 h.然后分馏,收集硼酸三甲酯甲醇恒沸物.最后用LiCl盐析法提纯硼酸三甲酯,得到硼酸三甲酯的含量在99%以上.