Formation of ST12 phase Ge nanoparticles in ZnO thin films

In this work, we focus on the Ge nanoparticles (Ge-np) embedded ZnO multilayered thin films. Effects of reactive and nonreactive growth of ZnO layers on the rapid thermal annealing (RTA) induced formation of Ge-np have been specifically investigated. The samples were deposited by sequential r.f. and d.c. sputtering of ZnO and Ge thin film layers, respectively on Si substrates. As-prepared thin film samples have been exposed to an ex-situ RTA at 600 °C for 60 s under forming gas atmosphere. Structural characterizations have been performed by X-ray Diffraction (XRD), Raman scattering, Secondary Ion Mass Spectroscopy (SIMS), and Scanning Electron Microscopy (SEM) techniques. It has been realized that reactive or nonreactive growth of ZnO layers significantly influences the morphology of the ZnO: Ge samples, most prominently the crystal structure of Ge-np. XRD and Raman analysis have revealed that while reactive growth results in a mixture of diamond cubic (DC) and simple tetragonal (ST12) Ge-np, nonreactive growth leads to the formation of only DC Ge-np upon RTA process. Formation of ST12 Ge-np has been discussed based on structural differences due to reactive and nonreactive growth of ZnO embedding layer.     

Preparation and characterization of Fe‐Tetranitro phthalocyanine/polyurethane blends

In this article, Fe‐Tetranitro phthalocyanine (Fe‐TNPc)/polyurethane (PU) blends were prepared by solution blending. The mechanical properties of the samples were studied by tensile tests. The results showed that the tensile strength and the elongation at break of the samples increased with increasing Fe‐TNPc content. The improved mechanical properties for the samples containing Fe‐TNPc was attributed to the increased microphase separation degree of PU, which was further investigated by dynamic mechanical analysis (DMA) and Fourier transform infrared analysis. The lower T_g of the soft segments and the higher T_g of the hard segments for the samples containing Fe‐TNPc indicated an increase of microphase separation degree of PU. The increased hydrogen bonded carbonyl groups in the samples with increasing Fe‐TNPc content also proved the conclusion. Quantitative evaluation of the interaction between Fe‐TNPc and PU was also investigated by analyzing the physical crosslinking density of the samples. The results indicated that the physical crosslinking density of the samples increased with increasing Fe‐TNPc content. The antibacterial properties of the samples were investigated. The results showed that the percentage bacterial inactivation toward S. aureus and E. coli of the samples were 98.9% and 90.9%, respectively, when Fe‐TNPc was added to 1%. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 41284.     

High-Tg porous polyimide films with low dielectric constant derived from spiro-(adamantane-2,9′(2′,7′-diamino)-fluorene)

Porous polyimide (PI) films with low dielectric constants and excellent thermal properties have been a pressing demand for the next generation of high-performance, miniature, and ultrathin microelectronic devices. A series of novel porous PI films containing fluorenyl-adamantane groups were prepared successfully via thermolysis of poly(ethylene glycol) (PEG) added in the PI matrix. The cross-sectional morphologies of porous PI films showed closed pores with diameters ranging from 135 to 158 nm, which were uniform and regular in shape without interconnectivity. These porous PI films exhibited excellent thermal properties with a glass-transition temperature at 376 °C whereas the 5% weight loss temperature in air excess of 405 °C due to enhanced rigidity afforded by fluorenyl-adamantane groups. Accompanied by thermolysis content of PEG increasing from 0 to 20 wt %, the density of porous PI films decreased, and the corresponding porosity grew significantly from 0 to 11.48%. Depending on porosity, the dielectric constant and dielectric loss of porous PI films significantly declined from 2.89 to 2.37 and from 0.050 to 0.021, respectively. These excellent properties benefit the as-prepared porous PI films for application as interlayer dielectrics, integrated circuit chips, or multichip modules in microelectronic fields. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 47313.     

Annealing effects on structural and electrical properties of fluorinated amorphous carbon films deposited by plasma enhanced chemical vapor deposition

The annealing effects on the structural and electrical properties of fluorinated amorphous carbon (a-C:F) thin films prepared from C₆F₆ and Ar plasma are investigated in a N₂ environment at 200 mTorr. The a-C:F films deposited at room temperature are thermally stable up to 250 °C, but as the annealing temperature is increased beyond 300 °C, the fluorine incorporation in the film is reduced, and the degree of crosslinking and graphitization in the film appears to be enhanced. At the annealing temperature of 250 °C, the chemical bond structures of the film are unchanged noticeably, but the interface trapped charges between the film and the silicon substrate are reduced significantly. The increased annealing temperature contributes the decrease of both the interface charges and the effective charge density in the a-C:F film. Higher self-bias voltage is shown to reduce the charge density in the film.     

Silicon for thin-film transistors

We are standing at the beginning of the industrialization of flexible thin-film transistor (TFT) backplanes. The two important research directions for the TFTs are (i) processability on flexible substrates and (ii) sufficient field-effect mobilities of electrons and holes to support complementary metal insulator semiconductor operation. The most important group of TFT capable semiconductors are the several modifications of silicon films: amorphous, nanocrystalline and microcrystalline. We summarize their TFT properties and their compatibility with foil substrate materials.     

新型高K栅介质ZrO2薄膜材料的制备及表征

采用超高真空电子束蒸发法制备了新型高 K栅介质-非晶 ZrO2薄膜. X射线光电子能谱 (XPS) 中 Zr3d5/2 和 Zr3d3/2 对应的结合能分别为 182.1eV和 184.3eV, Zr元素的主要存在形式为 Zr4+,说明薄膜由完全氧化的 ZrO2组成 ,并且纵向分布均一.扩展电阻法( SRP)显示 ZrO2薄膜的 电阻率在 108Ω@ cm以上,通过高分辨率透射电镜( HR- XTEM)可以观察 ZrO2/Si界面陡直,没有 界面反应产物 ,证明 600℃快速退火后 ZrO2薄膜是非晶结构.原子力显微镜( AFM)表征了薄膜的 表面粗糙度,所有样品表面都很平整,其中 600℃快速退火样品 (RTA)的 RMS为 0.480nm.     

Effect of Sb implantation on copper silicides formation and morphology after annealing of Cu/Si structures

In this work, the solid state reaction between a thin film of copper and silicon has been studied using Rutherford backscattering spectroscopy, X-ray diffraction, scanning electron microscopy and microprobe analysis. Cu films of 400 and 900 Å thicknesses are thermally evaporated on Si(1 1 1) substrates, part of them had previously been implanted with antimony ions of 5×10¹⁴ or 5×10¹⁵ at. cm⁻² doses. The samples are heat-treated in vacuum at temperatures in the range 200–700 °C for various times. The results show the growth and formation of Cu₃Si and Cu₄Si silicides under crystallites shape dispatched on the sample surface, independently of the implantation dose. On the other hand, it is established that the copper layer is less and less consumed as the antimony dose increases, resulting in the accumulation of Sb⁺ ions at silicide/Si interface and in the silicide layer close to surface. The exposure of samples to air at room temperature shows the stability of Cu₄Si phase whereas the Cu₃Si silicide disappears to the benefit of the silicon dioxide formation. The observed phenomena are discussed.     

PECVD法低温沉积多晶硅薄膜的研究

在玻璃衬底上采用常规的PKCVD法在低温(≤400℃)条件下制得大颗较(直径＞100nm)、择优取向(220)明显的多晶硅薄膜。选用的反应气体为SiF4和H2混合气体。加入少量的SiH4后，沉积速率提高了近10倍。分析认为，在低温时促使多晶硅结构形成的反应基元应是SiFmHn(m n≤3)，而不可能是SiHn(n≤3)基团。     

Preparation, patterning and luminescent properties of nanocrystalline Gd2O3:A (A=Eu, Dy, Sm, Er) phosphor films via Pechini sol–gel soft lithography

Nanocrystalline Gd₂O₃:A (A=Eu³⁺, Dy³⁺, Sm³⁺, Er³⁺) phosphor films and their patterning were fabricated by a Pechini sol–gel process combined with a soft lithography. X-ray diffraction (XRD), atomic force microscopy (AFM), scanning electron microscopy (SEM) and optical microscopy, UV/vis transmission and photoluminescence (PL) spectra as well as lifetimes were used to characterize the resulting films. The results of XRD indicated that the films began to crystallize at 500 °C and that the crystallinity increased with the elevation of annealing temperatures. Uniform and crack free non-patterned phosphor films were obtained by optimizing the composition of the coating sol, which mainly consisted of grains with an average size of 70 nm and a thickness of 550 nm. Using micro-molding in capillaries technique, we obtained homogeneous and defects-free patterned gel and crystalline phosphor films with different stripe widths (5, 10, 20 and 50 μm). Significant shrinkage (50%) was observed in the patterned films during the heat treatment process. The doped rare earth ions (A) showed their characteristic emission in crystalline Gd₂O₃ phosphor films due to an efficient energy transfer from Gd₂O₃ host to them. Both the lifetimes and PL intensity of the rare earth ions increased with increasing the annealing temperature from 500 to 900 °C, and the optimum concentrations for Eu³⁺, Dy³⁺, Sm³⁺, Er³⁺ were determined to be 5, 0.25, 1 and 1.5 mol% of Gd³⁺ in Gd₂O₃ films, respectively.