Characterization of a plasma polymer coating from an organophosphorus silane deposited at atmospheric pressure for fire-retardant purposes

Protective coatings from diethylphosphatoethyltriethoxysilane (DEPETS) have been deposited on different polymer substrates in a plasma discharge operated at atmospheric pressure. Plasma polymer chemistry and structure were characterized by means of Fourier transform infrared spectroscopy (FTIR), laser desorption ionization-mass spectrometry (LDI-MS), nuclear magnetic resonance (NMR) and scanning electron microscopy (SEM). A chemical structure of the plasma polymer has been proposed based on the coating molecular characterization. Coatings were deposited on polycarbonate (PC) and polyamide 6 (PA6) substrates. The flame retardant properties of coated substrate samples were assessed using cone calorimetry and compared to those of bare substrates. A significant increase in the time to ignition (TTI), up to +143%, was recorded after coating deposition due to the formation of a high-performance barrier layer at the surface of both polymer substrates.     

Spray coating process variable and property analysis of UV-curable polyurethane acrylate coating on polycarbonate substrate

A series of spray coating experiments were conducted on an UV-curable, polyurethane-modified, acrylate-based coating formulation with the aim to control defects, coating thickness, and thickness variation. Statistical approaches including design of experiment, residual examination, analysis of variance, and t-test were used in designing the experiments and analyzing data. Viscosity of formulation, atomizing pressure, liquid feeding pressure, distance between nozzle and substrate, and travel speed of substrate were the process variables studied. The ranges of process variables that gave defect-free coating were identified and used in the subsequent experiments to determine process variables and interactions that had significant contribution to the changes in coating thickness and thickness variation. All process variables studied were found to have contribution to the change in coating thickness, but they showed no significant contribution to the variation of coating thickness. No interaction displayed significant contribution. Confirmation tests performed on extra samples prepared with varying coating thicknesses indicated a good agreement with the experimental results. Additional samples were tested for total transmittance, transmission haze, adhesion, surface roughness, hardness, scratch hardness, abrasion resistance, and durability to attack of car wash chemicals. Spray coated samples showed slight improvement in the total transmittance over the uncoated samples, while maintaining the transmission haze and exhibiting rougher surfaces. Only samples with thin coatings were found to possess sufficient adhesion to the substrate. These thin coatings gave improved hardness, scratch hardness, and durability to car wash attack to the level comparable to commercial coated polycarbonate headlamp lenses, whilst giving better abrasion resistance.     

Growth,mechanical properties,and tribological performance of TiAlN/NbN and NbN/TiAlN bilayer coatings

Three different coatings, namely TiAlN, TiAlN (external)/NbN (internal) and NbN (external)/TiAlN (internal), were deposited on cemented carbides by arc ion plating. The comparative investigation conducted in this study elucidates the effect of the NbN layer and coating systems on the growth, mechanical properties, and tribological performance of the coatings. The results showed that the surface of the TiAlN and TiAlN/NbN coatings was smoother when TiAlN served as the external layer. The NbN/TiAlN coating, wherein NbN formed the external layer, had a much rougher but more symmetrical surface. With the introduction of the NbN layer, the increased micro stress induced a lower adhesion strength in the TiAlN/NbN and NbN/TiAlN coatings. The TiAlN/NbN and NbN/TiAlN coatings exhibited higher hardness and hardness/effective elastic modulus (H/E*). During the friction test, when the temperature was elevated to 700 °C, the tribological performance of the monolayer TiAlN coating was the lowest because of the TiO₂-induced breakage of the dense tribo-oxide film. The NbN layer participated in the formation of a NbO_x film at elevated temperatures, which was responsible for the high tribological performance of the two bilayer coatings. When the NbN layer was on the outermost layer and in direct contact with the elevated temperature atmosphere, the NbN/TiAlN coating generated a tribo-oxide film with high integrity, and its coefficient of friction decreased by 27% of that at room temperature. Therefore, the NbN/TiAlN coating exhibited the highest wear resistance at 700 °C.     

Selective Coating of SnS on the Bio‐Inspired Moth‐Eye Patterned PEDOT:PSS Polymer Films

A new strategy for the selective coating of tin sulfide (SnS) on the surface of moth‐eye patterned (MEP) conducting polymer film is studied by considering the optical properties of the antireflective moth‐eye pattern and flexibility of polymer films. The semiconductor SnS is selectively coated on the surface of MEP microdomes of poly(3,4‐ethylenedioxythiophene) poly(styrene‐sulfonate) (PEDOT:PSS) film. The SnS coated MEP film is obtained by using pore selectively SnS thin layer functionalized polystyrene honeycomb‐patterned porous (HCP) film as a template. Aqueous PEDOT:PSS solution is poured on the SnS functionalized HCP films and detached for the fabrication of SnS coated MEP films. The films show a satisfactory photo‐responsive property under solar stimulated light illumination due to the antireflective MEP structure of PEDOT film and homogenous SnS coating on the surface of the conducting polymer.     

Separation of hematite from banded hematite jasper (BHJ) by magnetic coating

The separation of iron oxide from banded hematite jasper(BHJ) assaying 47.8% Fe, 25.6% Si O2 and 2.30%Al2O3 using selective magnetic coating was studied. Characterization studies of the low grade ore indicate that besides hematite and goethite,jasper, a microcrystalline form of quartzite, is the major impurity associated with this ore. Beneficiation by conventional magnetic separation technique could yield a magnetic concentrate containing 60.8% Fe with 51% Fe recovery. In order to enhance the recovery of the iron oxide minerals, fine magnetite, colloidal magnetite and oleate colloidal magnetite were used as the coating material. When subjected to magnetic separation, the coated ore produces an iron concentrate containing 60.2% Fe with an enhanced recovery of56%. The AFM studies indicate that the coagulation of hematite particles with the oleate colloidal magnetite facilitates the higher recovery of iron particles from the low grade BHJ iron ore under appropriate conditions.     

高强WSTi544221合金组织与性能研究

研究了轧制变形量对WSTi544221合金棒材显微组织和力学性能的影响,并对Φ10 mm规格的棒材进行不同制度的固溶+时效处理,对比了不同热处理状态下棒材的组织和力学性能。结果表明,随着轧制变形量的增大,WSTi544221合金棒材的晶粒细化程度增大,强度逐渐提高,但塑性变化不大。经870℃×1 h/WC+520℃×6 h/AC固溶+时效处理后,强度与塑性可以获得良好匹配,当抗拉强度达到1 610 MPa、屈服强度达到1 531 MPa时,延伸率和断面收缩率可分别保持在12%和43%。     

Ni,Cr, and Fe surfaces corroded by molten ZnCl2

Understanding the corrosion of molten ZnCl₂ on metal surfaces is significant for the corrosion protection of metals, sustainable use of molten salts, preparation of ZnO coatings, and so on. In this paper, surfaces of pure Ni, Cr, and Fe corroded by molten ZnCl₂ were investigated. The results show that Ni suffered very slight corrosion, while Cr experienced more serious corrosion than Ni, but lighter corrosion than Fe. The morphology of the corrosion of Cr and Fe, respectively, presented pitting and intergranular corrosion characteristics. Furthermore, nanostructured ZnO coatings were obtained on the surfaces of Ni and Fe, but not on the surface of Cr. The ZnO coating on the Ni surface was doped with a small amount of Zn₅(OH)₈Cl₂, and the ZnO coating on the Fe surface was doped with ZnFe₂O₄ and Zn₂OCl₂. The coatings on the Ni and Fe surfaces had an average thickness of 1.5 and 50 μm, respectively.