Effect of Biochar as Reductant on Magnetizing-roasting Behavior of Pyrite Cinder

The effect of biochar substituted for anthracite as reductant on magnetizing-roasting pyrite cinder was investigated.The key of magnetizing-roasting is the gasification reaction between reductants and CO2.Since biochar could react with CO2 more rapidly at lower temperature,the reactivity of biochar is better than that of anthracite.The gasification of biochar could produce reducing condition ofφCO/(φCO+φCO2)about 10%-20% between 700-800 ℃,which is in accord with the atmosphere and temperature of Fe2O3 reduction.So it is beneficial to the reduction of iron mineral of pyrite cinder.Compared with anthracite,biochar could decrease the roasting temperature from825 to 750 ℃ and roasting time from 20 to 15min,which shows that a better effect of magnetization could be obtained in the condition of lower temperature and shorter time.Using biochar as reductant,iron concentrate extracted from pyrite cinder as about 64%iron grade could be produced,and the recovery is over 90% under the condition of above 90% grinding particle less than 0.045 mm and magnetic intensity of 0.124-0.194 T.     

降低气体悬浮焙烧炉焙烧过程中Al_2O_3粒度破损的措施

为了降低气体悬浮焙烧炉焙烧过程中Al_2O_3粒度的破损,对气体悬浮焙烧炉焙烧过程中氧化铝粒度的影响因素进行了分析,提出了降低粒度破损的一些措施。     

烧结处理小矿山精矿的应用研究

研究小矿山精矿的性质，分析小矿山精矿对烧结过程的影响，提出了增加小矿山精矿配入量的途径及方法．     

阳平关砂金矿精选厂尾矿综合回收的研究

本文详细的介绍了陕西省阳平关砂金矿精选厂尾矿金和其他可利用的矿物综合回收方法和最佳分选流程。     

钒冶炼焙烧添加剂选择研究

对小型钒冶炼厂焙烧工艺所用添加剂进行改进的可能性进行了探讨，研究了几种常用添加剂的焙烧条件，分析比较了其性能，提出用ＮａＣｌ－Ｎａ２ＣＯ３作焙烧添加剂替代ＮａＣｌ可大幅度减少大气污染，提高冶钒转化率；且不改变工艺流程，无需设备投资，具有较好的经济效益和环境效益。     

Investigation of the Effects of some Parameters in the Production of Chromate from Chromite Ores in Iskenderun Region

The conversion of chromite ore from iskenderun region into chromate was investigated. Firstly, the chromite ore was analysed using conventional chemical methods. Then, the effect of some parameters such as roasting time, temperature and the amount of additives on the conversion efficiency to the chromate was examined. The optimum roasting conditions were determined as 300°C, 2 hours, 10 times the stoichiometrically required amounts of NaClO₃ and 6 times the stoichiometrically required amounts of KOH. Under these conditions, the maximum recovery of chromate was found to be 100%. The product obtained from the roasting process was leached with water to produce a clean chromate solution. The effect of temperature and solid/liquid (S/L) ratio was investigated in the water leaching experiments. The optimum experimental results obtained were 100% at a 1:5 solid to water ratio at 25°C and 20 min leaching period. The chromate solution was purified using conventional purification processes.     

利用正交试验确定钒渣焙烧的最佳工艺条件

介绍了钒分厂利用正交试验法进行试验方案的设计及试验结果的直观分析，确定出钒渣烙烧的最佳工艺条件是：钒渣粒径小于0．12mm，烙烧气中氧气体积分数大于10％，焙烧温度850℃，烙烧时间60min，碱比(碱与钒渣质量比)16％，盐比(盐与钒渣质量比)5％，从而改变了以往在生产和转渣时组织生产的被动局面，为公司创造了可观的经济与社会效益。     

从废钼合金催化剂中提取钼等有价元素方法的研究

ＭｏＣｏＮｉ合金料首先氧化焙烧碱浸出，滤饼再加纯碱焙烧水浸出使钼与钴镍分离，最后用萃取法分离钴镍的工艺流程，对废钼合金催化剂进行了综合回收。采用该工艺流程和生产线分别生产出合格的工业级钼酸钠、氧化钴和氧化镍。     

固氟氯化铵焙烧法从包头稀土矿中回收稀土的动力学

研究了固氟氯化铵焙烧法分解包头混合型稀土精矿回收稀土的动力学.结果表明:固氟焙砂的氯化反应过程符合Bagdasarym提出的区域反应速率模型,氯化反应过程经过了两个串联反应步骤,且反应生成物的核按一个方向长大;反应速率方程遵从Erofeev方程的串联反应步骤模型,反应表观活化能Ea为36.831 KJ·mol-1,过程控制步骤是内扩散控制.     

贵州天柱重晶石回转窑还原焙烧生产工艺研究

中国重晶石资源储量丰富,为科学合理利用,避免重晶石开发过程中浪费,采用?3.2 m×60 m回转窑还原焙烧处理贵州天柱重晶石,考察了焙烧温度、抛煤对重晶石还原效果的影响。结果表明,当高温区温度为1 050~1 200 ℃、窑尾温度为500~600 ℃、窑头温度为750~850 ℃、回转窑转速为0.20~0.40 r/min、处理量为15~20 t/h、吨矿耗煤为191.64 kg时,获得粗钡中硫化钡质量分数为70.5%、粗钡浸出率为91.3%的良好指标,焙烧矿石及浸出考核指标均合格,对合理利用中国储量巨大的重晶石矿资源具有重要的现实意义。