一种新型低成本GDL-4高速钢CCT曲线的测定

利用热膨胀法结合金相法-硬度法测定一种新型低成本GDL-4高速钢过冷奥氏体的连续冷却转变曲线(CCT图);分析该钢连续冷却过程中转变产物的组织和硬度特征。结果表明:除珠光体相变和马氏体M相变外,该钢在303～383℃转变温度区间有贝氏体相变区;Ac1为890℃;过冷奥氏体的临界冷却速度为30℃/min;冷速在11~15℃/min时得到贝氏体与珠光体的混合组织,冷速≤10℃/min得到完全的珠光体。     

台式超精密车床关键部件结构设计

随着系统小型化已不断的成为一种趋势,微小精密零部件在很多领域都显示出越来越广阔的应用前景.目前,多数微小精密零部件都是由大型超精密机床加工的,由于大型超精密机床成本高,并难以控制其外界环境,使得其加工成本很高,因此,研制了台式超精密车床.本文介绍了该车床关键部件的设计,包括空气主轴、进给机构、快速伺服刀架等.该机床精度达亚微米级,不仅促进了微小型产品的制造与研究,而且加速了制造业的发展.     

5056铝合金稳恒磁控激光深熔焊接过程熔池流动与传热行为分析

针对外加稳恒磁场条件下6 mm厚度5056铝合金激光深熔焊接过程,建立了热场—流场—电磁场耦合熔池瞬态动力学数值模型,求解了特定时刻温度场、速度场与电磁场分布,建立了熔池沿不同方向的Peclet数模型,分析了不同磁场感应强度对熔池流动与传热行为的影响.结果表明,稳恒磁场条件下熔池中产生显著的哈特曼效应,表现为液态金属M...     

Effects of deformation on microstructures and properties of submicron crystalline Cu-5%Cr alloy

Warm extrusion of submicron crystalline Cu-5%Cr from 100 ℃ to 600 ℃ was investigated. The effects of different extrusion ratios and different extrusion temperatures on microstructures and properties of submicron crystalline Cu-5%Cr were studied. The microstructures of the extruded Cu-5%Cr were characterized by backscattered electron irnages（BSE） and transmission electron microscopy（TEM）. The mechanical properties of the extruded Cu-5%Cr were measured by means of microhardness and tension test. The results show that, the deformation, dynamic recovery and dynamic recrystallization of the extruded Cu-5%Cr are mainly produced in Cu matrix. The higher extrusion ratio leads to more uniform microstructure and finer Cu grains. When being extruded in the range of 100-600 ℃, dynamic recovery of Cu is the dominant process, and dynamic recrystallization of Cu occurred above 300 ℃ is far from end. The most part of microstructure of as-extruded Cu-5%Cr is subcrystaUines produced by dynamic recovery, only a few recrystallines exist, and the average size of these grains is not larger than 400 nm. With extrusion temperature rising, the tensile strength and microhardness of Cu-5%Cr decrease, and elongation increases gradually.     

T91与1Cr18Ni9Ti异种钢焊接

T91钢是国外为提高火力发电机组的效率而研制的一种高合金耐热钢,它是完成超临界发电机组主蒸气参数由566℃向593℃过渡的关键材料.针对马氏体耐热钢(T91)与奥氏体钢(1Cr18Ni9Ti)的物理化学性能,分析了该异种钢的焊接性.通过在湘潭电厂二期工程中具体应用表明,采取适当的焊前预热及焊后热处理的措施,选取合适的焊接材料和焊接工艺参数,能够获得性能优良的焊接接头.     

半固态亚共晶高铬铸铁重熔时先共晶相的演变

对倾斜板法制备的亚共晶高铬铸铁半固态坯料在1 300 ℃进行加热保温,借助Leica图像分析仪对保温过程中先共晶奥氏体的演变规律进行了研究.结果表明,晶粒球化和合并长大为保温过程中奥氏体形态演变的主要形式,两者交替发生,球化和合并长大所需的时间随着保温过程的进行而延长.同时,合并长大而恶化也随着保温过程的进行而越发显著.保温15.0 min时,晶粒形状系数为0.86,平均等效直径为78.8 μm;保温60.0 min时,晶粒形状系数为0.70,平均等效直径为104.1 μm.     

自振式结晶器在奥氏体不锈钢方圆坯上的应用

通过对奥氏体不锈钢的表面质量控制的实际生产研究,得出可借鉴性的结论:采用高振动精度的自振式结晶器,有效的保护渣配方,合理的锥度,合适的振动参数的结合,是控制不锈钢表面质量的关键;利用结晶器热流値可很好的控制奥氏体不锈钢铸坯的表面凹陷。