Hot-compression behavior of Al-1Mn-1Mg alloy

The hot-compression of Al-1Mn-1Mg (mass fraction, %) alloy sample was carried out on a Gleeble-1500 thermo-simulator at deformation temperatures from 320 to 400 ℃ and strain rates from 0.1 to 10 s-1 by total strain of 1.4. Microstructure and texture evolution of the hot-compressed alloy were investigated by optical microscopy and X-ray diffraction analysis, respectively. The results show that the relationship among flow stress σ, deformation temperature T and strain rate ε can be expressed in the form of βσ...     

Deformation behavior and microstructure of an Al-Zn-Mg-Cu-Zr alloy during hot deformation

The hot deformation behavior and microstructures of Al-7055 commercial alloy were investigated by axisymmetric hot compression at temperatures ranging from 300°C to 450°C and strain rates from 10-2 to 10 s-1,respectively.Microstructures of deformed 7055 alloy were investigated by transmission electron microscopy (TEM).The dependence of peak stress on deformation temperature and strain rate can be expressed by the hyperbolic-sine type equation.The hot deformation activation energy of the alloy is 146 kJ/mol....     

Hydrogen-induced cracking behaviors of Incoloy alloy 825

The effect of hydrogen on the fracture behaviors of Incoloy alloy 825 was investigated by means of slow strain rate testing (SSRT).Hydrogen was introduced into the sample by electrochemical charging.The results show that surface microcracks form gradually during aging at room temperature when desorption of hydrogen takes place after hydrogen charging at a current density of 5 mA/cm 2 for 24 h.SSRT shows that the increase of ductility loss is significantly obvious as the hydrogen charging current density inc...     

Microscopic characterization of semi-solid aluminium alloys

The microstructural evolution and element distribution of the Al-4Cu-Mg alloy during semi-solid compression were investigated,and the precipitate behavior and dislocation morphology were discussed.The experimental results show that the microstructure,the number of CuAl2(θ phase) precipitates,and the dislocation density of the Al-4Cu-Mg alloy depend apparently on the process parameters.More segregation of Cu at the grain boundary happens with an increase of deformation temperature and a decrease of strain ra...     

Effects of yttrium on the formation and magnetic properties of bulk metallic glassy （Fe, Co）-B-Si-Nb alloys

The bulk metallic glassy (BMG) rods of [(Fe0.5Co0.5)0.72B0.192Si0.048Nb0.04]100-xYx (x=0-6) and [(FexCo1-x)0.72B0.192Si0.04]Nb0.04]96Y4 (x=0.5-0.8) were prepared by copper mold casting. The structure, thermal stability,and magnetic properties of the samples were studied by X-ray diffraction (XRD), differential scanning calorimetry (DSC), and vibrating sample magnetometer (VSM). Adding lat% to 6at% of yt-trium, the bulk glassy alloy rods of [(Fe0.5Co0.5)0.72B0.192Si0.048Nb0.04]100-xYx (x=0-6) with the diameter of 3 mm were not formed, and the sample with 4at% of yttrium showed less crystalline phase than others. When the Fe/Co atomic ratio was between 5:5 and 7:3, the bulk glassy alloy rods of [(Fe1-xCox)B0.192Si0.048Nb0.04]96Y4 (x=0.5-0.8) with the diameter of 2 mm were fabricated. In the (Fe, Co)-B-Si-Nb-Y BMGs, when the Fe content increased, the thermal stability, the supercooled liquid region, and the glass-forming ability (GFA) decreased, but the saturation magnetization (Ms) increased.     

Effect of cooling rate on the phase transformation and stability of the mushy zone during the solidification of Waspaloy

Scanning electron microscopy(SEM) and energy dispersive X-ray analysis(EDAX) were used to study the microstructure,microsegregation, and fluid flow tendency of the superalloy Waspaloy in the mushy zone,which had been solidified at different cooling rates. The investigation was accompanied with the calculation of Rayleigh numbers.It is found that Ti is the main segregating element and the content of Ti is the highest in the final liquid at the cooling rates of 3-6℃/min.The eta phase(η) precipitate present...     

热连轧工艺对GH4648合金棒材组织与性能的影响

研究了连轧生产线生产的GH4648合金热轧棒材的组织与性能.采用热连轧过程的自动化控制系统调整棒材的轧制速度、保持稳定的终轧温度,从而获得晶粒组织均匀、α-Cr相形态与分布合理的热轧棒材.与传统的横列式轧机相比,工艺更稳定、可控,热轧棒材的组织稳定、性能提高.     

定向凝固工艺下大尺寸DSM11铸件的显微组织

为了实现液态金属冷却法（LMC）的工程化应用,研究了传统高速凝固法（HRS）和液态金属冷却法两种定向凝固工艺下得到的大尺寸DSM11合金铸件的显微组织.结果表明,与HRS工艺相比,LMC工艺得到的大尺寸铸件组织更均匀,一次、二次枝晶间距小,三次枝晶不明显,共晶尺寸小、含量少,缩孔等缺陷少,枝晶干和枝晶间的γ′尺寸小、差别小,碳化物细小且分布均匀.此外,LMC工艺使合金元素微观偏析减小,抑制了块状η相析出倾向.     

Effects of welding wire composition and welding process on the weld metal toughness of submerged arc welded pipeline steel

The effects of alloying elements in welding wires and submerged arc welding process on the microstructures and low-temperature impact toughness of weld metals have been investigated.The results indicate that the optimal contents of alloying elements in welding wires can improve the low-temperature impact toughness of weld metals because the proentectoid ferrite and bainite formations can be suppressed,and the fraction of acicular ferrite increases.However,the contents of alloying elements need to vary along with the welding heat input.With the increase in welding heat input,the contents of alloying elements in welding wires need to be increased accordingly.The microstructures mainly consisting of acicular ferrite can be obtained in weld metals after four-wire submerged arc welding using the wires with a low carbon content and appropriate contents of Mn,Mo,Ti-B,Cu,Ni,and RE,resulting in the high low-temperature impact toughness of weld metals.     

Fabrication of high nitrogen austenitic stainless steels with excellent mechanical and pitting corrosion properties

A series of high nitrogen austenitic stainless steels were successfully developed with a pressurized electroslag remelting furnace. Nitride additives and deoxidizer were packed into the stainless steel pipes, and then the stainless steel pipes were welded on the surface of an electrode with low nitrogen content to prepare a compound electrode. Using Si3N4 as a nitrogen alloying source, the silicon contents in the ingots were prone to be out of the specification range, the electric current fluctuated greatly...