The vacuum residual from Iranian Light crude oil are separated into a series of 16 narrow fractions according to the molecular weight by the supercritical fluid extraction and fractional (SFEF) technology. The chemical element and the UV spectrum of each fraction are analyzed. The effects of several factors on the interfacial tension are investigated, which are the fraction concentration in oil phase, the ratio of oil component, the salts dissolved in the water phase and the pH value. The interfacial tension decreases rapidly as the concentration of the residual fraction in the oil increases, showing a higher interfacial activity of the fraction. The interfacial tension changes, as the amount of absorption or the state of the fractions in the interface changes resulting from different ratios of oil, different kinds or concentrations of salts in water, and different pH values. It is concluded that the intrfacial tension changes regularly, corresponding to the regular molecular parameters of the vacuum residual fractions.     

FCC汽油馏分在水热处理Zn/HZSM-5催化剂上的芳构化反应

制备了300 ℃、350 ℃、400 ℃和500 ℃不同水热处理温度下的Zn/HZSM-5催化剂，并用于FCC汽油馏分的芳构化反应。考察了水热处理温度对芳构化反应性能的影响，并与吡啶吸附红外光谱(FT-IR)相关联，研究了水热处理温度对催化剂表面酸性的影响。结果表明，水热处理Zn/HZSM-5的芳构化活性稳定性得以改善, 与未经水热处理的催化剂相比，400 ℃水热处理的Zn(2%)/HZSM-5催化剂芳构化反应36 h时，芳烃质量分数仍高达74.25%。随着水热处理温度的升高， B酸酸中心数在300～400 ℃变化不大，500 ℃显著减少，L酸酸中心数升高，400 ℃达到最大值后呈降低趋势，烯烃转化率、烷烃转化率和产品芳烃含量升高，水热处理400 ℃时均达到最大值，分别为83.62%、95.44%和92.23%，表明此时B酸中心和L酸中心比例协调性最佳。     

降低冷轧钢种结晶器液面波动的工艺实践

结合马钢四钢轧实际生产情况,分析了影响结晶器液面波动的主要原因为塞棒吹氩量和鼓肚。通过采取降低塞棒吹氩量,增加二冷水量,优化保护渣性能以及保证扇形段对中精度等工艺措施后,结晶器液面波动标准差由2.52mm降低为1.36mm,从而达到提高冷轧产品质量的目的。     

萘系化合物对FCC油浆富含芳烃馏分油制备的针状焦组成和结构的影响

以石蜡基催化裂化油浆的富含芳烃馏分油为原料,添加不同萘系单体化合物（萘、1-甲基萘、四氢萘、十氢萘）,通过两段焦化法制备针状焦。采用元素分析、傅里叶变换红外光谱、族组成分析等方法考察了萘系单体化合物对针状焦组成和结构的影响。结果表明,尽管在体系中添加的是小分子芳烃物种,随着萘系化合物含量的不断增加,对于碳质中间相的形成有着一定的促进作用;带有烷基侧链的芳烃通过自由基反应和氢转移反应可以提高体系的炭化活性,能够有效增加产物的缩合度;同时,具有环烷结构的芳烃也可通过开环反应和氢转移反应改变体系的流变性,降低体系黏度,从而降低产物缩合度。     

氩离子轰击清洗铜和不锈钢靶

利用不同压强的氩气分别对铜靶(直径为14cm)和不锈钢靶(直径为30cm)进行了离子轰击清洗试验;测量了伏—安曲线,得出了清洗铜靶的最低电压为800伏,最大电流为54毫安,不锈钢靶的最低电压为500伏,最大电流为108毫安。     

外场处理对低合金钢焊接接头组织和性能的影响

研究了电磁搅拌、氩弧表层处理、超声喷丸处理对低合金钢焊接接头组织和性能的影响。结果表明 :电磁搅拌促进奥氏体晶粒内针状铁素体生成和细化 ,使针状铁素体的含量由 85%提高到 92 % ,从而提高了焊缝金属的韧度。氩弧加热处理使焊缝表层发生熔化和重结晶 ,可消除焊缝表层的柱状晶 ,处理后的组织主要由针状和细晶铁素体组成。对接头焊趾部位进行氩弧快速重熔处理可消除焊趾部位的几何截面突变 ,使焊缝与母材圆滑过渡 ,有利于消除焊趾部位的应力集中 ,对抗应力腐蚀性能十分有益 ;焊趾部位热影响区中粗大的晶粒细化。表面高能喷丸处理使焊接接头表面层形成尺寸均匀的等轴状纳米晶 ,不仅提高了表层的硬度 ,而且可使焊接接头的疲劳强度提高 50 %。     

Interaction between alloying and hardening of cast iron surface

To improve wear resistance of surface will increase the service life of gray cast iron directly.This paper presents that gray cast iron surface coated with alloy powder is locally remelted by TIG arc of increase the wear resistance.The influences of arc current and scanning rate etc on surface properties are found.Under different conditions.the microstructure,hardness and wear resistance of remelted layer are analyzed and measured.The results indicate that the gray cast iron surface can be strengthened by TIG arc local remelting treathent.Especially,surface alloying hardening effect is best and surface properties are improved remarkably.     

Ar^39／Ar^40 dating of three typical gold deposits in southern Qinling and its implication

1　ＩＮＴＲＯＤＵＣＴＩＯＮＱｉｎｌｉｎｇｏｒｏｇｅｎｉｃｂｅｌｔａｂｕｔｓＮｏｒｔｈＣｈｉｎａ ｐｌａｔ ｆｏｒｍｗｉｔｈＳｈａｎｇｚｈｏｕ ＤａｎｆｅｎｇｇｅｏｓｕｔｕｒｅｉｎｔｈｅｎｏｒｔｈａｎｄｎｅｉｇｈｂｏｒｓＹａｎｇｔｚｅ ｐｌａｔｆｏｒｍｗｉｔｈ     

氩弧重熔对管线钢接头表层组织的影响

采用氩弧重熔单道和多道处理管线钢接头，不公使焊缝表层的柱状晶组织细化，而且使接头焊趾部位出现圆滑过渡，同时也细化了焊趾部位热影响区的粗大晶粒。接头表层组织的细化和焊趾部位的圆滑过渡都有利于提高管线钢接头的疲劳和腐蚀性能。