烧结与冷镦过程中铝硅共晶合金显微结构与密度的演变

采用烧结及后续的镦粗工艺制备了铝硅共晶合金块体材料,研究了烧结温度对烧结体显微结构、抗压强度及相对密度的影响。结果表明：烧结温度显著影响烧结体的显微结构和抗压强度,以临近铝硅共晶合金液相线的温度烧结时,发生了局部熔化,产生的熔融液体破坏了颗粒表面的氧化膜,颗粒之间相互黏结,形成了烧结骨架。以优化的555℃烧结,Si颗粒呈球状,抗压强度达到最佳,但相对密度未发生变化。在后续的冷镦过程中,烧结骨架及粉末颗粒均产生变形,孔隙减小,颗粒呈扁平状,相对密度达到了98%。     

储氢与合金材料

介绍了储氢合金材料和开发应用动态。     

Room temperature oxidation of lead-indium alloy films

The kinetics of growth of thin (14 to 40Å) oxide layers on lead-indium alloys was investigated ellipsometrically, using: 3000Å thick films at 23°C; and oxygen exposures at 760 torr for times ranging from five minutes to five days. Assuming that the oxide layer is comprised of a two-phase mixture of PbO and In₂O₃ having a negligible extinction coefficient made it possible to estimate the oxide composition from the ellipsometrically-obtained oxide refractive index. Under these oxidizing conditions, the volume fraction of PbO in the oxide mixture decreases from a value of unity for pure lead to zero for alloys containing more than 30 at. percent In, in agreement with the Auger Electron Spectroscopy results of Chou and coworkers. The oxidation rate equals a exp (X₁/X), where α and X₁ will be seen to vary complexly with alloy composition. A theoretical explanation of these results is also presented.     

合金钢中白点缺陷超声反射波辨析

通过对进口合金钢中白点缺陷超声反射波形的分析研究，为白点缺陷的判定提供借鉴，保证工程材料的使用安全。     

电炉还原熔炼氧化钴矿的生产实践

介绍了刚果(金)钴铜冶炼厂电炉还原熔炼处理钴铜氧化矿工艺的设计特点及生产实践。     

SHS结合热压制备TiC-Al2O3/Fe-Al复合材料

以天然钛铁矿、铝粉和石墨为主要原料,采用自蔓延高温合成技术、铝热还原法并结合热压烧结技术,制备出TiC—Al2O3／Fe—Al复合材料．研究表明：预热时间少于120s时,预热时间越长,反应燃烧波速度越大,当预热时间继续增大,对反应燃烧波速度的影响不再显著;加入添加剂Y2O3为0．2％时,金属相较均匀地弥散分布在陶瓷颗粒周围．晶粒尺寸约为2～3μm,复合材料的相对密度达到94％,抗弯强度和硬度分别为599．29MPa、83．7HRA．     

The Effects of Aging Precipitation on the Recrystallization of CuNiSiCr Alloy

The interaction between precipitation and recrystallization and its effect on the properties of the Cu-Ni-Si-Cr alloy during aging were discussed. The results show that the deformation results in much more dispersed precipitation of the phases. The precipitations have accelerating or retarding effects on the recrys allization. On the formation and growth of recrystallization, the precipitated phases are coarsed or dissolved in front of grain boundaries following a re-precipitation in the recrystallization area.     

GH4169合金的X射线荧光光谱分析

采用x射线荧光光谱仪测定GH4169合金中的锰、硅、镍、铬、钼、铝、钛、铌。研究了测量条件及基体 吸收—增强效应的校正。还时测量精度进行了研究,各元素的相对标准偏差分别为0．0466％～O．6777％。与 化学分析结果对照结果良好。