Dental amalgam – the effect of the technology of alloy powder preparation on the corrosion behaviour and the release of mercury

Dental amalgams are based on a broad spectrum of materials differing in their chemical composition, metallurgical treatment, and in the way the initial alloys powders are prepared. In addition to their chemical composition, amalgams based on various powders differ in both their microstructure and the amount of mercury needed for preparation. All these facts may affect electrochemical processes occurring during their interaction with oral fluids, and also mercury release. While verifying the effect of the technology used for the preparation of the high‐copper ternary alloy powder on the properties of resulting amalgams, this study aimed at the mechanism of their interaction with a model saliva solution as well as mercury release was included. Measurements were done in a model saliva solution using standard electrochemical methods and exposition measurements. The interaction of individual types of amalgams with artificial saliva did not reveal any significant differences. The free corrosion potential of all these amalgams in an aerated solution settled in the range of values in which tin oxidation, resulting in a layer of insoluble corrosion producsts, turned out to be the dominant anodic process. The rate of mercury release was the lowest for amalgams based on a gas‐atomized alloy. The highest rate of mercury release, and also its dependence on time, was exhibited by lathe‐cut powder based amalgam. In addition to different volume fraction of the Ag‐Hg phase and the level of its tin alloying, this different behaviour may be explained by differences in the rate at which a layer of tin corrosion products acting as a barrier to mercury release is formed.     

The hydrogenation of triglycerides using supported alloy catalysts. I. Silica-supported Ni—Ag catalysts

Silica-supported Ni-Ag catalysts with a loading of 2·1·0.6% (w/w) total metal have been prepared using the precursors nickel dimethylglyoxime and silver nitrate by means of a simple impregnation method. The resulting catalysts were activated by calcination at 260°C in air, followed by hydrogen reduction at 450°C. They were then employed for soyabean oil hydrogenation at 1 bar H2 pressure and 160°C in a stirred batch reactor. Characterisation of the catalysts using temperature-programmed reduction and electron microscopy indicated that alloying of nickel and silver had occurred, but metal particle composition, for a given overall composition, varied with metal particle size and smaller metal particles were nickel rich. The hydrogenation activity and selectivity measurements revealed that the catalysts were more active and selective than a commercial nickel catalyst. Furthermore, the specific activities of the alloy catalysts were a maximum for alloys in the range 70–90 at. % Ni. However, the supported alloy catalysts also gave rise to greater trans isomerisation than the commercial catalyst. This is attributed to hydrogen deficiency caused by large triglyceride molecules blocking hydrogen chemisorption on small nickel particles (10–50 Å in diameter), leading to enhanced cis-trans isomerisation.     

住宅建筑带钢副框铝合金门窗防渗漏施工技术

使用自粘性防水卷材对带钢副框的铝合金门窗窗边进行粘接,以防止雨水通过副框与墙体之间的缝隙渗漏到室内,重点介绍了详细的施工措施。     

铝合金穿孔板吸声墙面施工技术

以教育部综合办公楼工程的机房铝合金穿孔板吸声墙面施工为例,介绍其固定件及吸声墙面的做法。     

High-performance polymer alloys of polybenzoxazine and bismaleimide

Two series of high-performance polymer alloys were prepared by mixing typical benzoxine monomers, 3-phenyl-3,4-dihydro-2H-1,3-benzoxazine (P-a) or 6,6-(1-methylethyliden)-bis-(3,4-dihydro-3-phenyl-2H-1,3-benzoxazine) (B-a), with a typical bismaleimide, 4,4-bismaleimidodiphenyl methane by various ratios followed by thermal treatment up to 240 °C. DSC and IR of the alloys were examined to follow the curing reaction. These analyses showed that the obtained polymer alloys are AB co-cross-linked polymer networks through the formation of ether linkage between the hydroxyl group of polybenoxazine and the double bond of bismaleimide. Viscoelastic analysis and softening temperature measurement revealed that the polymer alloys have much higher glass transition temperatures than those of each homopolymer. The thermal stability also increased with the increase of bismaleimide content as evidenced by TGA.     

烧结硬化用低合金钢粉

本文将介绍三种不同成分的低合金钢粉。在混入2 0%铜和不同石墨含量的条件下,对该三种粉进行了试验评定。试件的密度为6 9g/cm3,在氮氢混合气氛中于1120℃下烧结25min,在炉内冷却带650～400℃温区的冷却速度为0 4或1 5℃/s条件下,对烧结态和回火后试件的力学性能进行了测试。回火条件为200℃下保温60min。在一定的冷却速率和碳含量条件下,各种钢粉烧结后的硬度可高达40HRC。回火后,硬度仍可以保持在30HRC以上。     

CO毒化AB5型合金分形特征研究

研究了三种贮氢合金 L a Ni5、L a Ni4 .7Al0 .3、Ml Ni4 .5Al0 .5被 10 0× 10 - 6 CO毒化后的分形特征 ,求出这三种合金在含 10 0× 10 - 6 CO的氢中循环 ,分维分别为 0 .2 5 4 7、0 .170 9、0 .0 72 5。可以较好的解释合金被毒化的宏观现象。     

Corrosion failure of Zn–Al detonator housing

Some batches of detonator housings made up of Chromium plated Zn–Al alloy were found in an extensively cracked condition after few months of storage at room temperature. An analysis of the failure showed that the cracks were due to intergranular corrosion facilitated by segregation of lead at the grain boundaries. Improper chromium plating further aggravated the corrosion problem. This failure case emphasises the need for strict control of chemical composition for components made from Zn–Al alloy and the process of Cr plating of the components.     

电磁搅拌制备ZL12Y铝合金流变半固态浆料的实验及模拟研究

对不同温度及不同搅拌工艺下得到的材料的显微组织的比较，确定了合理的半固态温度和搅拌工艺，即半固态温度为590℃，震荡电流为500A。随后对单个线圈电磁搅拌过程进行建模及电磁场和流速场的耦合模拟得到了电磁场和流速场分布，此结果与电磁搅拌的原理及实验结果相一致。计算出在该温度和工艺下熔体内部的平均流动速度为3．2cm／s，将该结果作为能否得到半固态浆料的判据。     

含Zr低合金高强度钢中夹杂物的特性

用电子探针研究了含Zr低合金高强度钢中夹杂物的形貌、大小及分布等特性。结果表明 ,钢样中的夹杂物为圆形 ,呈分散分布 ,其组成系含ZrO2 的复合夹杂物 ,而且MnS依附此复合夹杂物成核和长大。钢中添加少量Zr可明显改善夹杂物形态和分布 ,从而改善钢的强度和韧性