Toughness enhancement and equivalent initial fracture toughness of cementitious composite reinforced with aligned steel fibres

Based on theoretical analysis and numerical simulation, the impact of steel fibres on the stress intensity factor (SIF) at the crack tip for cementitious composite was studied. The enhanced toughness of steel fibre reinforced cementitious composite (SFRC) in resisting cracks was explained by the decrement of SIF caused by steel fibre inclusions at the crack tip of the composite. The equivalent initial fracture toughness was used to characterize the crack initiation of SFRC. A simplified method for determining the of SFRC was proposed based on a linear regression method. Fracture tests were conducted on three‐point bending notched beams with different steel fibre volume fractions and specimen sizes to study the crack initiation behaviour of aligned steel fibre reinforced cementitious composite (ASFRC). of ASFRC was calculated, and the size effect of was analysed. The results showed that slightly increased with the steel fibre volume fraction and gradually became stable. For the tested specimens, whose heights varied between 40 and 100 mm, the specimen size had little impact on the .     

Damage mechanism at different transpassive potentials of solution-annealed 316 and 316l stainless steels

Electrochemical impedance spectroscopy (EIS), anodic polarization and scanning electron microscopy techniques were used to investigate the damage mechanism in the transpassive potential region of AISI ...     

Design and performance study of phase‐locked loop using fractional‐order loop filter

The present work reports the realization of an analog fractional‐order phase‐locked loop (FPLL) using a fractional capacitor. The expressions for bandwidth, capture range, and lock range of the FPLL have been derived analytically and then compared with the experimental observations using LM565 IC. It has been observed that bandwidth and capture range can be extended by using FPLL. It has also been found that FPLL can provide faster response and lower phase error at the time of switching compared to its integer‐order counterpart. Copyright © 2014 John Wiley & Sons, Ltd.     

致密油藏注天然气提高采收率研究现状

随着我国石油需求量不断增加,致密油藏的开发也愈发重要。如何高效开发致密油藏是一项重点难点,其中致密油藏注天然气提高采收率是一个极具潜力的研究方向。因此,本文着重介绍以天然气作为能量补充介质在国内外的研究现状和应用现状,并且从两相特征等方面总结了理论研究中的一些机理,对致密油藏注天然气提高采收率的发展前景进行了一定的展望。     

Temperature- and frequency-dependent hysteresis scaling behaviour and phase transitions in a [001]c 0.73Pb(Mg1/3Nb2/3)O3-0.27PbTiO3 single crystal

The dielectric properties and bipolar polarization-electric field (P-E) and strain-electric field (S-E) dynamic hysteresis of a relaxor [001]_c 0.73Pb(Mg_1/3Nb_2/3)O₃-0.27PbTiO₃ (PMN-0.27PT) single crystal were investigated to reveal more details of the temperature-induced phase transitions. Different linear scaling relations for ferroelectric hysteresis area <A>, coercive field E_c, saturation polarization P_s and remnant polarization P_r versus temperature τ were measured in different temperature regions. For each measurement frequency f, all hysteresis parameters were found to decrease linearly with temperature in the temperature range of the single rhombohedral (R) phase or tetragonal (T) phase, and the rate of decrease in the T phase was observed to be much larger than the corresponding rate in the R phase. In the temperature range near the R-T phase transition, the exponent α in the power law <A>∝f ^α for the R phase was found to be smaller than that for the T phase, and the magnitude of α depended strongly on temperature when the crystal was in the R-T coexisting phase state. Our experimental and theoretical results indicate that the difference in the activation energy and dipole moment in the R and T phases may lead to the observed discrepancy for the P-E and S-E hysteresis behaviour in different temperature regions.     

Precipitating spinel into precursor glass and its assistance in crystallization

The crystallization phenomena of spinel in CaO-MgO-Al₂O₃-SiO₂-Fe₂O₃ glass have received much attention due to the particular role in preparation of glass-ceramic materials, which represent an effective option to manage hazardous waste. In this study, both preliminary spinel and secondary spinel were precipitated in the precursor glass. The formation of these spinel was meticulously assessed by a combination of X-ray diffractometry and scanning electron microscopy. The structure of the microenvironment in the precursor glass was characterized by Raman spectrums. These advanced techniques highlight the potential for one-step crystallization of the glass. The investigation, which focused on one-step crystallization, demonstrated the growth of pyroxene on spinel accompanying a migration of chromium. The results also show the microstructure of the obtained glass-ceramic was very dependent on the heat-treat temperature. This study not only unambiguously reveals the precipitation mechanisms of spinel but also provides more documentation for one-step crystallization in the glass-ceramics field.     

Corrosion behaviors of Cr2AlC/α-Al2O3 composites in 3.5 wt. % NaCl aqueous solution

Cr₂AlC and its composites containing α-Al₂O₃ (6.1 and 15.2 wt %) were prepared by hot pressing and their corrosion behaviors in air-saturated 3.5 wt % NaCl aqueous solution were investigated by electrochemical testing methods. It was revealed that the secondary phase of Al₂O₃ particles mainly distributed along grain boundaries of Cr₂AlC matrix. The potentiodynamic polarization measurements showed that the corrosion current densities of these Cr₂AlC composites were lower than that of the pure Cr₂AlC. The Aluminum in Cr₂AlC was prone to be attacked more easily. When immersed at open circuit potential (OCP), Al readily slipped out from Cr₂AlC matrix into NaCl solution in the form of dissoluble species. But in the case of polarization, regardless of potentiostatic polarization or potentiodynamic polarization, more de-intercalated Al, reacted with the electrolyte to form corrosion products of Al₂O₃ and/or AlOOH and deposited on the sample surface. For Cr₂AlC/α-Al₂O₃ composites, the presence of Al₂O₃ weakened the corrosion along grain boundaries by partly blocking the permeation of electrolyte and inhibiting the anodic dissolution process.     

Effect of stoichiometry and Cu-substitution on the phase structure and hydrogen storage properties of Ml-Mg-Ni-based alloys

To improve the electrochemical properties of rare-earth–Mg–Ni-based hydrogen storage alloys, the effects of stoichiometry and Cu-substitution on the phase structure and thermodynamic properties of the ...     

开关磁阻直线电机的设计及其推力优化

设计了一种开关磁阻直线电机,使用JMAG软件对其进行了仿真和优化。进行了推力公式的推导,研究了导通顺序和初始位置对电机推力的影响,并分析了三种典型情况的磁力线分布。对电机的定子和动子的齿部和轭部高度、宽度及铁耗进行仿真优化,得出了最优参数。将有取向硅钢应用于该电机,研究了推力与轧制角的关系,并与使用普通硅钢的开关磁阻直线电机进行了对比,推力有一定提升。提出在动子齿部开切向槽的方案,结果表明,开切向槽对推力的影响较小,并能显著减小推力波动。