离心铸造高速钢轧辊铸造缺陷形成与控制技术研究

采用离心铸造方法制造高速钢轧辊工艺简单,操作方便,但易出现偏析、裂纹、气孔、缩孔及夹杂等缺陷,影响轧辊的力学性能和使用性能.采用稀土-钛复合变质处理改善合金的组织和性能,同时改进离心铸造工艺参数可以消除高速钢轧辊铸造缺陷,提高力学性能,改善使用效果.     

运用均衡凝固模数法设计液压试验平台铸铁件压边浇冒口系统

液压试验平台,材质HT200,铸件重2 800 kg,轮廓尺寸2 400 mm×1 000 mm×275 mm,平板壁厚95 mm,肋条壁厚40 mm,周边框壁厚50 mm,粘土砂,干型。选用直浇道-横浇道-压边冒口系统,运用均衡凝固收缩模数法设计压边冒口体和冒口颈尺寸,运用大孔出流理论计算压边冒口金属液充满高度。计算结果:直浇道φ75 mm,横浇道45/65 mm×70 mm,压边冒口体φ104 mm,高度200 mm,冒口颈尺寸104 mm×8 mm,冒口体浇注过程充满高度80 mm,具有挡渣能力。生产结果表明,铸件无缩孔、气孔、夹渣缺陷,铸件工艺出品率95%。实践证明采用均衡凝固收缩模数法设计液压试验平台浇冒口系统是可行的。     

改善银首饰铸造质量的措施

斯特林银首饰铸造时经常会出现气孔、缩孔、砂眼、氧化物夹杂等,其原因主要来自2个方面,一是在铸造过程中各工序的操作不当,尤其是水线的设置、开粉操作、焙烧制度等关键工序,必须加强操作过程的控制;二是与银本身的性质有关,银在凝固时氧的溶解度骤减,气体容易析出导致气孔;斯特林银主要以铜作为合金化元素,容易氧化形成夹杂。在熔炼或铸造过程中要尽量避免金属液接触大气,采用真空、或使用惰性气体、还原性火焰、硼酸等进行保护,可以减少铸造缺陷的发生。     

转炉-连铸工序生产低碳铝镇静钢中夹杂物的研究

采用添加示踪剂的方法对转炉-CAS-连铸工艺生产低碳铝镇静钢中的夹杂物进行了研究,结果表明:出钢或CAS精炼过程中炉渣与钢液作用生成的夹杂物,尺寸在30 μm以下的夹杂物很难从钢液中完全上浮排出.铸坯中的主要夹杂物为来源于钢包渣与钢液作用生成的球状夹杂物、块状Al 2O 3夹杂物.连铸坯中的全氧含量在(38～53)×10 -6之间,夹杂物的含量在 2.3 mg/kg左右,表明该工艺可以生产较高纯净度的低碳铝镇静钢坯.     

大型铝合金叶片金属型铸造工艺分析

针对铝合金叶片的铸造缺陷，分析指出浇注位置、浇注系统设计、型腔排气和充型温度场是造成铸造缺陷的主要因素，据此，有针对性地提出了铸型倾斜、平浇竖冷、沿分型面开设排气槽、改变涂料层厚度以及调整凝固顺序等改进措施，其效果在生产中得到验证。     

ZA27合金金属型铸造时的凝固特性,伴生缺陷和壁厚效应

金属型铸造是ZA27的主要铸造方法之一。本文试验研究了ZA27合金金属型铸造时的凝固特性、伴生缺陷和壁厚效应。结果表明,ZA27合金在金属型中以糊状方式凝固,铸件易于产生缩松和比重偏析,铸件的力学性能对于壁厚有明显的敏感性。     

Preparation, thermal stability, and magnetic properties of Fe---Co---Zr---Mo---W---B bulk metallic glass

A bulk metallic glass (BMG) cylinder of Fe₆₀Co₈Zr₁₀Mo₅W₂B₁₅ with a diameter of 1.5 mm was prepared by copper mould casting of industrial raw materials. The amorphous state and the crystallization behavior were investigated by X-ray diffraction (XRD). The thermal stability parameters, such as glass transition temperature (T_g), crystallization temperature (T_x), supercooled liquid region (ΔT_x) between T_g and T_x, and reduced glass transition temperature T_rg (T_g/T_m) were measured by differential scanning calorimetry (DSC) to be 891, 950, 59 K, and 0.62, respectively. The crystallization process took place through a single stage, and involved crystallization of the phases -Fe, ZrFe₂, Fe₃B, MoB₂, Mo₂FeB₂, and an unknown phase, as determined by X-ray analysis of the sample annealed for 1.5 ks at 1023 K, 50 K above the DSC peak temperature of crystallization. Mössbauer spectroscopy was studied for this alloy. The spectra exhibit a broadened and asymmetric doublet-like structure that indicated paramagnetic behavior and a fully amorphous structure. -Fe was found in the amorphous matrix for a cylinder with a diameter of 2.5 mm. The success of synthesis of the Fe-based bulk metallic glass from industrial materials is important for the future progress in research and practical application of new bulk metallic glasses.     

黄原胶对消失模铸造涂料性能的影响

为提高消失模铸造水基涂料的质量,探讨了黄原胶作为微量添加剂对涂料性能的影响.试验研究表明,铸造涂料中加入适量的黄原胶可提高悬浮性、显著增大涂料粘度和涂挂性、改善涂料的流变行为.黄原胶还可显著提高涂层的强度,但使涂层透气性略有降低.鉴于黄原胶的优异性能,可望在消失模铸造水基涂料中获得应用.     

基于射钉法的小方坯凝固过程数值模拟

结合方坯连铸机二冷各段的实际情况，在二冷各段末对铸坯进行射钉取样，利用硫印法测定方坯二冷区内目标点凝固壳的厚度，建立了方坯传热数学模型，并利用射钉结果修正数学模型中的各段的传热系数，提高数学模型的准确性。将射钉法确定的坯壳厚度与数学模型计算结果相比较，结果表明，利用修正过的数学模型可以模拟整个铸机的传热凝固过程。     

覆膜砂离心铸造球墨铸铁管性能的研究

论述了以覆膜砂离心铸造和用含锰及微量元素含量较高的再生铁进行球化处理浇注球铁管的方法，研究了模内孕育，随流孕育和金属铋孕育对铸态球铁管塑性的影响，考察了锰，硅和碳当量及衬砂层厚度对铸态球铁管塑性的影响规律。