On-line corrosion monitoring in geothermal district heating systems. II. Localized corrosion

Corrosion monitoring in district heating systems has traditionally been performed by using off-line methods, such as weight loss. The disadvantage is that the method is very slow, especially in low-corrosive environments, and that it only provides information about the past corrosion (accumulated over period of time). The purpose of the work is to test on-line monitoring methods in geothermal hot water in the district heating system in Reykjavik, Iceland. Geothermal water poses certain problems with regards to corrosion monitoring due to low conductivity, high pH and the presence of sulphide. These conditions make the geothermal environment low corrosive. However, a quality control is needed, especially since the sulphide causes the steel pipes to be more vulnerable towards localized corrosion. The methods used in this study were: linear polarization resistance (LPR), harmonic analysis (HA), electrochemical noise (EN) and zero resistance ammetry (ZRA). The Pitting Factor was measured with EN and showed promising results for measuring-localized corrosion on-line. A crevice corrosion cell also gave good results but had a low lifetime. However, the results of a galvanic corrosion cell (Fe/Cu) proved more difficult to interpret since they were dependent both on the dissolved oxygen and the sulphide level.     

Low-cycle fatigue properties of eutectic solders at high temperatures

This paper details the deformation mechanism and low‐cycle fatigue life of eutectic solder alloys at high temperature (around 0.8T_m). Grain boundary sliding generally nucleates a wedge‐type cavity that reduces the low‐cycle fatigue life of metals. In this study, grain boundary sliding has promoted intergranular failure contributing to the reduction in fatigue life of Sn–Ag–Cu alloy. However, grain boundary sliding has exerted no deleterious effects on fatigue resistance of eutectic Pb–Sn and Bi–Sn alloys. The phase boundary sliding with very fine microstructure induces exceptional ductility in these alloys leading to superior low‐cycle fatigue endurance for theses eutectic Pb–Sn and Bi–Sn alloys.     

Al_(10)Zn_(2.9)Mg_(1.7)Cu超高强铝合金的喷射成形制备研究

采用喷射成形技术制备了Al1 0 Zn2 .9Mg1 .7Cu高强高韧铝合金沉积坯件 ,研究了喷射成形制备过程中各工艺参数对沉积坯件的成形性、显微组织、致密度的影响 ,确定了适当的工艺参数 ,研究了沉积坯件的热挤压及热处理工艺 ,对材料的组织进行了分析并对不同状态的材料性能进行了比较。研究结果表明 :当喷射成形工艺参数合理时 ,沉积坯件具有良好的成形性与致密度 ,在随后的热挤压过程中 ,通过较低的挤压比即可使材料达到全致密 ;通过对合金进行适当的热处理 ,材料的极限抗拉强度达到 810MPa ,同时延伸率保持在 8%～ 11% ,该材料是一种理想的轻质高强结构材料。     

我国内螺纹铜管的生产技术与发展方向

本文论述了我国内螺纹铜管业生产、工艺、产品技术条件、齿型及市场现状 ,提出了内螺纹铜管的研发方向。     

热镀钢丝膜层的冷凝计算

分析了热镀钢丝自液池引出过程中的热传导，得出了温度分布的解析解，从而计算钢丝表面膜层达到凝固温度时的提抽高度，为结构设计及确定冷却装置的合理位置提供依据。     

高速钢W6Mo5Cr4V2的脱磷试验

在３０ｋｇ感应炉上用ＣａＯ－Ｎａ２ＣＯ３－ＣａＦ２－ＦｅｘＯ（ＭｏＯ３）渣、ＭｏＣｌ６粉剂和Ａｌ－Ｃａ合金作脱磷剂对高速钢Ｗ６Ｍｏ５Ｃｒ４Ｖ２进行脱磷试验。结果表明，ＣａＯ－Ｎａ２ＣＯ３－ＣａＦ２－ＦｅｘＯ渣的脱磷效果最好，一般脱磷率可达２６％￣５６％。     

Catalytic behavior of YBa2Cu3O7-x in the partial oxidation of methanol to formaldehyde

The partial oxidation of methanol to formaldehyde was studied over YBa₂Cu₃O_7-x catalyst in a flow reactor. The structural change of YBa₂Cu₃O_7-x before and after the reaction was measured by means of XRD and iodometric titration method. The catalytic characteristics of YBa₂Cu₃O_7-x for the partial oxidation of methanol to formaldehyde was due to copper ions. It was found that Cu⁺² was responsible for the higher selectivity for formaldehyde.     

钢带捆扎对木箱强度的影响

从力学角度分析了钢带捆扎对木箱强度的影响，指出木箱经钢带捆扎后，可减小箱底的最大弯矩，提高木箱的承载能力和减少板厚。同时还在无支撑间隔的基础上，详细介绍了钢带捆扎的设计方法。     

Cr12钢的预处理工艺研究

本文研究了Ｃｒ１２钢经４种不同的预处理工艺处理后钢中碳化物的大小，数量，分布及钢的硬度，强度和韧性，试验结果表明，经调质处理，高温固溶淬火＋高温退火处理后，Ｃｒ１２钢中碳化物的大小，分布及其组织，性能均优于常规球化退火预处理的。通过扫描电镜对冲击断口的分析，初步探讨了新的预处理工艺提高韧性的原因。     

Effect of cationic surfactant and inorganic anions on the electrochemical behavior of carbon steel in formation water

Corrosion behavior of carbon steel in formation water associated crude oil from Egyptian western desert was studied at various concentrations of dodecyl dimethyl ammonium chloride (CS) as a cationic surfactant. Polarization curves indicate that CS has a good inhibition efficiency for carbon steel in formation water and behaves as cathodic inhibitor. The inhibition efficiency was found to increase with increase in CS concentration until reaches a maximum constant value corresponding to the critical micelle concentration of CS and decrease with increase in solution temperature. The adsorption of CS follows the kinetic thermodynamic model and Flory-Huggins isotherm. Thermodynamic parameters obtained indicate that that the presence of the CS increases the activation energy. Polarization and Impedance measurements indicate that the addition of KI has a significant synergistic effect with CS and results in increase the inhibition efficiency of CS in formation water.