The effect of aluminium coating on elemental standards in X-ray microanalysis

The standardisation of frozen hydrated bulk biological specimens using gelatin standards is described. The relationship between corrected elemental X-ray counts and ionic concentration was found to be linear, and minimum detectable limits for each element are stated. Variations in uncorrected standard curves were found to be due to changes in aluminium coating thickness. There was an inverse relationship between coating thickness and elemental X-ray counts. The factors causing this are discussed. To avoid errors arising from inconsistent aluminium thickness, experimental material should only be compared with standards of similar aluminium net counts. This can be achieved most easily by mounting and analysing specimen and standard together.     

Synthesis of selenium nanoparticles in the presence of silk fibroin

This paper describes a solution-phase approach to the synthesis of selenium nanoparticles by reducing selenious acid solution with ascorbic acid in the presence of silk fibroin. The monodispersed spherical selenium colloid particles obtained were very stable in silk fibroin solution and characterized by Atomic force microscopy and X-ray techniques. The influences of temperature and ultrasonication on the morphology of selenium nanoparticles were also discussed. The experiments showed that the selenium nanoparticles with various morphologies could be obtained under different temperatures and the appropriate ultrasonication time was 60 min. This result indicated that the silk fibroin molecules intimately associated with the surface of the selenium particles and controlled the growth particles.     

PMMA／PBA乳胶IPN阻尼材料的研究

用乳液聚合方法合成了一系列的互穿聚合物网络，其中包括：ＰＭＭＡ／ＰＢＡ和Ｐ（ＭＭＡ－ｃｏ－ＰＭＡ）／ＰＢＡ乳胶互穿聚合物网络（ＬＩＰＮ），ＰＭＭＡ／ＰＢＡ乳胶双向互穿聚合物网络（ＬＢＩＰＮ）以及ＰＭＭＡ／ＰＢＡ界面交联互穿聚合物网络（ＩＣＬＩＰＮ）。动态力学谱和拉伸试验结果表明：（１）ＰＭＭＡ／ＰＢＡ互穿聚合物网络的两组分相容性和阻尼性能可通过ＭＭＡ和ＰＭＡ共聚来改善；（２）双向互穿技术是一种行之     

Determination of the width of the transition layer between the crystalline and amorphous zones in nylon 1010 by SAXS

The width of the transition layer between the crystalline and amorphous zones in nylon 1010 was determined by SAXS with point collimation and long-slit collimation, respectively. The width of the transition layer, E, was found to be 1.7 nm. The results show that the width of the transition layer is independent of crystallinity.     

氮化钛薄膜的高分辨AES谱和XPS谱研究

着重讨论了TiNx薄膜俄歇电子谱的定量分析方法和X射线光电子谱中线形的变化。利用已知组元强度定量分析技术和Ti的LMV俄歇电子峰，探讨TiNx薄膜中N含量的定量方法。由该方法给出的定量结果与X射线光电子谱定量结果相一致。同时，利用X射线光电子谱测定了TiN和Ti2N2p轨道的结合能。并针对Ti2p峰形随N含量的变化，给出新的解释。     

材料研究中系列试样的单标样法 X 射线定量分析

本文提出了用一个标样进行系列试样 X 射线定量相分析的方法.它克服了一般 X 射线定量方法需要混合研磨和手续烦复的缺点以及无标样 X 射线定量方法存在病态方程不易解决的问题.该方法对常规 X 射线定量分析具有普遍的实用性.     

离子注入对Cr12MoV钢表面组织结构和力学性能的影响

研究了Ｃｒ１２ＭｏＶ钢离子注入层的显微组织特征及其对表面性能的影响。结果表明，离子注入使Ｃｒ１２ＭｏＶ钢的表面硬度和耐磨性能得到显著改善，且存在着一个最佳的注入剂量，约为３×１０＾１＾７Ｎ＾＋／ｃｍ＾２左右。离了注入在Ｃｒ１２ＭｏＶ钢表面层中形成了大量细小弥散的第二相粒子，并使α－Ｆｅ晶格发生严重畸变，从而引起材料表面强化。     

Growth of Fe on Si (100) at room temperature and formation of iron silicide

Low-energy electron diffraction (LEED), Auger electron spectroscopy and X-ray photoelectron spectroscopy (XPS) investigations of both the growth of an iron film on silicon (100) at room temperature and the subsequent formation of iron silicide are the subjects of this paper. An in-situ cleaned silicon (100) wafer without carbon or oxygen contamination exhibiting the known 2 × 1 reconstruction in the LEED pattern served as the substrate. Iron was deposited on this reconstructed surface at 300 K. The comparison of theoretical calculations based on three growth mechanisms with XPS data obtained with take-off angles of 0° and 50° clearly demonstrates a layer-by-layer growth of the iron film on silicon (100). At 300 K no formation of iron silicide was observed, although an interaction between iron and silicon could be detected at the interface. The formation of iron silicide was observed at annealing temperatures of 630–730 K. Quantitative XPS analysis yields the presence of FeSi₂, when the thickness is large enough. Neither the iron film on silicon nor the silicide shows any LEED pattern.     

一种双光束自动测试光栅绝对与相对光谱衍射效率的原理性方案

提出了一种快速自动测试光栅光谱衍射效率的新方法。重点推导了测试平面光栅绝对光谱衍射效率与相对光谱衍射效率公式，介绍了双光束高精度自动测试光栅光谱衍射效率曲线的基本原理、方案与方法，并分析了测试精度。研究表明，本方案的测试速度和精度均比一般测试方法提高一倍，并能有效地消除光源波动对测量结果的影响，测量误差小于５×１０－３。