Study of Bake Hardenability and Strengthening Mechanism of Hot Rolled Low Carbon Steel

The controlled rolling and controlled cooling,bake hardening experiments have been carried out for the test steel,mechanical property test of the sample and microstructure analysis have been made by tensile testing machine,optical microscope,TEM and X-ray diffractometer.The results show that fine and uniform microstructures can achieve much higher BH and BHT values;With the increase of pre-strain there is a trend of increase first and then decrease in the BH and BHT values;bake hardening mechanism mainly consists of Cottrell atmosphere strengthening,second phase strengthening,dislocation strengthening.     

不同成分体系对超低碳烘烤硬化钢性能的影响

研究了不同成分体系超低碳烘烤硬化钢的性能特征,生产结果表明:Ti-BH钢屈服强度和BH值较低,伸长率和"值富裕量较大,并且BH值波动较大.通过对不同成分体系钢板的微合金化原理进行分析,确定了不同成分体系烘烤硬化钢性能不同的原因,并据此将烘烤硬化钢的成分体系由Ti-ULC改为Nb+Ti复合体系.更改后的烘烤硬化钢性能指标...     

ULC BH钢常规轧制和铁素体区轧制组织与性能比较

在实验室完成超低烘烤硬化钢的常规奥氏体区和铁素体区润滑轧制,观察了组织,比较了在2种不同轧制制度下的组织差别;并通过MTS810拉伸实验机的综合性能测试,比较了2种制度下的性能。可以看出,在铁素体区轧制除值外,其它性能均能满足要求。作者认为,造成 值降低的主要原因是铁素体区的固溶碳原子较多所致,但具体原因还有待进一步研究。但是,通过铁素体区轧制并结合合理的退火制度,可生产出满足要求的超低碳烘烤硬化钢。     

用呋喃树脂砂生产薄壁铸钢件热裂纹成因的分析

将呋喃树脂砂工艺铸钢件上出现的热裂纹分为“缩裂纹”和“拉裂纹”。对两种裂纹的和观形貌微区成分做了分析,深入探讨了两种裂纹具有的不同形成原因和形成过程,为采取有效对策解决裂提供了技术依据。     

Effect of hook characteristics on the fracture behaviour of dissimilar friction stir welded aluminium alloy and mild steel sheets

ABSTRACT

Under tensile shear loading, fracture modes of dissimilar lap welds produced by friction stir scribe technology were studied. Three fracture modes were observed. For zone A fracture, the initial crack was restrained, and the joint ultimately fractured in the base mild steel. For zone B fracture, the initial crack progressed through the aluminium sheet just above the Al/steel interface. For zone C fracture, the initial crack proceeded along the steel hook to the aluminium sheet surface. Fracture mode and joint strength were greatly influenced by steel hook size, and the steel hook size was affected by welding parameters and tool scribe height. In this study, the experimental joint strength achieved the calculated joint load limit.     

现代预焙铝电解槽焦粒预热焙烧启动研究

本文介绍了在280kA电解槽上最早使用焦粒预热启动的成功经验，从焦粒通电焙烧到灌电解质，整个过程分步进行了列举说明，并且对每个步骤中存在的问题也做了评论。记录了启动过程中的电压、电流值及温度变化，特别对温度曲线62阴极钢棒的温度做了详细的描述。使用这种方法，我们成功的缩短了焙烧时间，减少了能量消耗，避免了启动时因铝水的热冲击而导致电解槽内衬早期破损，延长了电解槽的使用寿命。     

三期焙烧BPS系统的工艺优化

BPS系统工艺优化目的：实现沥青挥发分充分燃烧，改进烟气排放效果；降低天然气单耗；改进阳极焙烧质量。关键是如何控制2区炉室挥发分大量释放的合理时间与燃烧位置。     

预时效对车身用6016铝合金烘烤硬化性能的影响

采用硬度测试、拉伸试验和透射电镜等手段研究了不同预时效处理对6016铝合金烘烤前后微观组织和力学性能的影响。结果表明:6016铝合金具有较强的自然时效硬化能力,自然时效24 h的6016铝硬度比固溶态合金硬度增加了45.6%。自然时效超过24 h以后,合金硬度值变化不大。通过预时效处理可以显著提高6016铝合金的烘烤硬化效果。经550 ℃×30 min固溶+160 ℃×10 min预时效处理后,6016铝合金规定塑性延伸强度为131.4 MPa,伸长率为24.7%。再经175 ℃×30 min烘烤后合金规定塑性延伸强度达到199.5 MPa,烘烤硬化值(BH)为68.1 MPa,此工艺为6016铝合金车身板最佳的热处理工艺。     

相变诱导塑性钢TRIP590的烘烤硬化特性

采用拉伸试验机、扫描电镜(SEM)和透射电镜(TEM)等手段研究了预应变处理+烘烤工艺对TRIP590试验钢烘烤硬化(BH)特性的影响。结果表明:试验钢微观组织主要由75.5%的铁素体+15.0%的贝氏体+9.5%的残留奥氏体(体积分数)组成。随着预应变量的增大,BH值呈现增大的趋势,且前期的增长幅度较大。预应变由2%增加到8%时,BH值由22 MPa增大到88 MPa,达到最大值。随烘烤时间的延长和烘烤温度的提高,BH值均呈现增加的趋势。BH值变化规律与内耗峰值变化规律一致,证明了TRIP590钢烘烤硬化现象的柯氏气团钉扎本质。经2%预应变+烘烤处理后,基体内部可以明显看到固溶原子对位错的钉扎现象。