铁矿石的烧结基础特性之新概念

长期以来,人们对烧结用铁矿石的评价主要集中在化学成分、粒度组成、矿物特征等常温性能方面,而对铁矿石在烧结过程中的高温行为和作用知之甚少.根据对这一问题的深入思考和实验室的基础研究,提出了\     

Effects of Chloride Ion on the Texture of Copper and Cu-ZrB2 Coatings Electrodeposited from Copper Nitrate Solution in Different Plating Modes

For the first time, the texture of copper and Cu-ZrB2 coatings produced from copper nitrate solution was studied. Chloride ion shows different effects on the deposit texture under direct current （DC） and pulse current （PC） conditions. Copper deposits are strongly 〈220〉 textured in DC plating with and without chloride ion. While in PC condition, the predominant texture shifts from 〈220〉 to 〈200〉 as the chloride ion concentration exceeds 20 mg/l. The addition of ZrB2 particles enhances the cathodic polarization of copper deposition, which improves the growth of （111） plane. However, this improvement can be eliminated by further addition of chloride ion.     

铁基合金的贝氏体基元及其生长演化

用透射电镜研究了 Fe-C-Mo 和 Fe-C-Si-Mn 合金中温转变早期产物的组织形态,发现在整个中温转变范围非平衡先析型转变都是按贝氏体铁素体相变基元形成及其扩散生长演化方式进行,说明经生长演化一些时间后的基元难于作为判断贝氏体形核机制的形态学依据。从基元生长演化进程区分了低碳贝氏体和板条马氏体。     

中热固相法制备掺杂钛的钒酸锂正极材料

以Li2CO3和V2O5为原料,用中热固相法制备了掺杂Ti4+的锂离子电池正极材料Li1.1V3―yTiyO8(y=0.05、0.1、0.2),并对其电化学性能进行了研究。研究表明,掺杂Ti能够很好地改善中热固相法产品的电化学性能,且当y=0.1时,Li1.1V3―yTiyO8循环性能最好,首次放电比容量高达250.9 mAh/g。     

2,5-二巯基-1,3,4-噻二唑的电化学性能

以二硫化碳和水合肼为原料合成了2,5-二巯基-1,3,4-噻二唑(DMcT),并通过元素分析、Raman光谱和红外(IR)光谱对DMcT的结构进行了表征。DMcT的两对氧化还原峰电位差分别为0.96V和1.33V,这表明在室温下氧化还原反应速度很慢。酸碱对DMcT氧化还原反应有很大的影响:加入三乙胺之后,DMcT的氧化反应更加容易,还原峰电流增加,但对还原峰电位影响不大;相反,甲磺酸存在时,DMcT的氧化反应更难进行,而还原反应变得更加容易。     

离子交换纤维微观形貌特点及结构修饰研究

利用比表面积测试仪、扫描电子显微镜等物理化学方法对颗粒与纤维状离子交换剂的链间交联与微观形貌进行了研究,通过刚性交联剂对聚丙烯-苯乙烯-二乙烯基苯(PP-ST-DVB)离子交换纤维骨架结构进行了修饰改造。结果表明:离子交换纤维由于不能通过交联剂与致孔剂参与下的单体聚合构建具有丰富微孔的高分子骨架,所以不存在丰富孔结构和高比表面积特征,其内部为连续凝胶相结构;外比表面积大、传质距离短、交联键分布均匀是其反应动力学和渗透压稳定性能优异的主要原因;刚性交联剂在PP-ST-DVB纤维上的附加交联反应使其比表面积从原来的0.5 m~2/g提高到200 m~2/g以上,附加交联反应所形成的分子尺度微孔孔径分布窄,具有超高交联树脂的结构特点。     

危机与契机并存——从学位论文看我国建筑更新领域学术研究发展情况

本文对我国近十余年间建筑更新及建筑保护领域学术论文做了全面的搜集和多角度的统计工作,分析介绍了我国建筑更新领域的学术地位和学术发展特征,并对其存在的问题进行了阐述和深层次剖析,力求为我国建筑更新领域后续研究工作的开展起到参考借鉴作用。     

电视、激光、中波红外多波段增透膜研究

针对多光谱成像中存在的多光谱共光路问题,在ZnSe基底上设计了三波段增透膜。通过选取合适的薄膜材料,利用TFCalc膜系设计软件对膜系进行设计与优化,使用热蒸发和离子源轰击结合的方式沉积膜层,采用分光光度计和傅里叶红外光谱仪测量光谱特性。通过设计粘结层与保护层,有效提高了膜层与基底之间的结合力以及膜层的强度。该膜层可以实现多光谱ZnSe基底在电视（500~800 nm）、1064 nm激光和中波红外（3.7~4.8 μm）三个波段高效增透,且具有良好的环境适应性。     

Multi‐Atomic Layers of Metallic Aluminum for Ultralong Life Lithium Storage with High Volumetric Capacity

Metallic aluminum (Al) have been explored as potential anode materials for lithium storage because of its high theoretical capacity (993 mAh g^–1) and low voltage plateaus. Al possesses high electric conductivity, low cost and environmental friendliness. Unfortunately, Al suffers from huge volume change (>100%) during the lithiation/delithiation process, which inevitably results in the pulverization of electrode and rapid capacity decay during cycling processes. To circumvent above issues, a simple but efficient strategy is demonstrated to fabricate free‐standing multi‐atomic layers of metallic Al by harnessing the good ductility of Al under pressure. The resultant multi‐atomic Al layers are ultrathin, ≈3 nm, and have a large aspect ratio. Such unique features enable multi‐atomic Al nanosheets to construct uniform and compact films with graphene. Thus, the hybrid films with different ratios are achieved, in which the notorious volume change of metallic Al can be efficiently circumvented via the good flexibility of graphene, and the density of whole electrode can be significantly enhanced. As a consequence, the optimized multi‐atomic Al layers‐graphene (AlL‐G) film exhibits a very high volumetric capacity of 1089 mAh cm^–3, high‐rate capability and ultralong cycle life up to 20 000 cycles for lithium storage.     

钽掺杂对二氧化钒多晶薄膜相变特性的影响

将Ta_2O_5与V_2O_5均匀混合,压制成溅射靶,用离子束增强沉积方法在二氧化硅衬底上沉积掺Ta氧化钒薄膜.在氮气中适当退火,形成掺杂二氧化钒多晶薄膜.X射线衍射结果显示,薄膜具有单一的(002)取向.XPS测试表明,膜中V为+4价,Ta以替位方式存在.温度-电阻率测试表明,薄膜具有明显的相变行为,原子比为3%的Ta掺杂后,二氧化钒多晶薄膜相变温度降低到约48℃.Ta原子的半径大于V原子的半径,Ta的掺入在薄膜中引入了张应力;5价Ta 替代4价V,在d轨道中引入多余电子,产生施主能级,这些是掺钽二氧化钒多晶薄膜相变温度降低的原因.