纳米层状双金属氢氧化物的制备及结构表征

采用恒定pH 12±0.2,按n(Mg2+)∶n(Al3+)∶n(OH-)∶n(CO2-3)=6∶2∶16∶1配制溶液,采用一步反应液相法,制备纳米层状双金属氢氧化物(LDH)粉体.为了获得无团聚、分散均匀的纳米粉体,探讨了溶剂置换干燥、真空干燥、常压干燥对纳米LDH粉体形成团聚的影响;用X射线衍射仪、透射电镜、红外光谱仪和元素分析仪对样品的物相、形貌、粒径和组成进行了表征.结果表明,溶剂置换干燥能够有效防止纳米粉体形成硬团聚,样品分散性好,呈针状形态,长50 nm,宽5 nm.     

小尺寸钛酸钡粉体的制备与表征

以不同比例无水及八水合氢氧化钡混合物为钡源，并以钛酸四异丙酯为钛源，采用改进的氢氧化物．醇盐法常压下回流10h可得到的颗粒尺寸分布窄，平均粒径约13nm的钛酸钡粉体。借助XRD及TEM对粉体物性进行了表征。实验结果表明，该法制得的钛酸钡粉体为亚稳态立方晶相晶体，晶粒尺寸随钡源中无水氢氧化钡含量的增加或反应温度的降低而减小；降低钡源中无水氢氧化钡的含量及提高反应温度均有利于加快钛酸钡粉体的生成速率。     

Fabrication and structure characterization of ITO transparent conducting film by sol-gel technique

Using In（NO3）3·5H2O and acetylacetone as raw materials and anhydrous SnCl4 as dopant, the transparent conducting indium tin oxide（ITO） films were prepared by sol-gel and dip-coating technique. The phase transformation, structure properties and physical properties （sheet resistance and transmittance） of the films were investigated by DTA-TG, XRD, SEM, four-probe method and UV-Vis spectrometry. The results indicate that it is feasible to fabricate 1TO films on the quartz substrates by sol-gel technique, and the ITO films are formed by accumulating of particles with the size of several decades of nanometers. The prepared ITO film has cubic bixbyite structure, and （111） is its preferred plane. After five-times dip-coating, the 1TO film has a thickness less than 150 nm, a sheet resistance of 110Ω/□, a resistivity of 1.65×10^-3Ω· cm and a transparency of 90% .     

SURFACE MODIFICATION OF TITANIUM FILMS WITH SODIUM ION IMPLANTATION： SURFACE PROPERTIES AND PROTEIN ADSORPTION

Sodium implanted titanium films with different ion doses were characterized to correlate their ion implantation parameters. Native titanium films and ion implanted titanium films were characterized with combined techniques of X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), and light microscopy (LM). The surface presented increased sodium concentration on treated titanium films with ion dose increasing, except for the group with the highest ion dose of 4× 1017 ions/cm2. XPS depth profiling displayed that sodium entered titanium film around 25-50 nm depth depending on its implantation ion dose. AFM characterization showed that sodium ion implantation treatment changed the surface morphology from a relatively smooth titanium film to rough surfaces corresponding to different implantation doses.After sodium implantation, implanted titanium films presented big particles with island structure morphology. The surface morphology and particle growth displayed the corresponding trend.Fibrinogen adsorption on these titanium films was performed to correlate with the surface properties of treated titanium films. The results show that protein adsorption on ion-implanted samples with dose of 2 × 1017 and 4 × 1017 are statistically higher (p ＜ 0. 01) than samples treated with dose of 5×1016 and 1 ×1017, as well as the control samples.     

A new strain Acidithiobacillus albertensis BY-05 for bioleaching of metal sulfides ores

An acidophilic,rod-shaped Gram-negative sulfur oxidizing strain BY-05 was isolated from an acid mine drainage of copper ore in Baiyin area,Gansu Province,China.Ultrastructural studies show that the isolate has a tuft of polar flagella and possesses sulfur granules with clear membrane adhering to the cell innermembrane.Physiological study shows that this isolate grows autotrophically and aerobically by oxidizing S0and reduced inorganic sulfur compounds(SO, 2 23-SO, 2 24- S2 -and ZnS)with the optimum growth at pH 3.5-4.0 and at the temperature range of 25-30℃.The 16S rRNA gene sequence(DQ 423683)of strain BY-05 has 100%sequence similarity to that of Acidithiobacillus albertensis(DSM 14366).So it is identified and named as A. albertensis BY-05.Bioleaching experiments with this new strain show that it can play an important role in recovery of metals from chalcopyrite and sphalerite.     

钢中珠光体球团尺寸的EBSD表征技术

借助光学显微镜和扫描电镜等研究了珠光体球团的表征方法,从阻止裂纹扩展的有效性出发,选择内部取向接近、外部取向差较大的球团簇作为评价珠光体球团尺寸的指标。结果表明,珠光体中铁素体的取向分布与球团吻合,即铁素体的大角度晶界就是球团(簇)界,所以可以通过表征铁素体的晶粒尺寸来评价珠光体球团尺寸。该方法的关键点在于晶界如何定义和样品如何制备。从对EBSD法的可行性分析可知,以15°作为晶内最大取向差来划分珠光体球团。对于珠光体钢,电解抛光法更适用于珠光体中渗碳体片层较宽的样品,而对于珠光体中渗碳体片层过窄的情况更适合选用离子抛光法。      

第四十届国际尖端材料学会年会与展览简介

介绍国外先进材料技术现状与发展趋势，即强调发展新材料技术，低成本生产技术，质量控制技术，重视先进材料应用，两用技术和军转民。     

Diamond growth by carbon ion implantation of diamond

Medium energy (5–25 keV) ¹³C⁺ ion implantation into diamond (100) to a fluence ranging from 10¹⁶ cm⁻² to 10¹⁸ cm⁻² was performed for the study of diamond growth via the approach of ion beam implantation. The samples were characterized with Rutherford backscattering/channelling spectroscopy, Raman spectroscopy, X-ray photoemission spectroscopy and Auger electron spectroscopy. Extended defects are formed in the cascade collision volume during bombardment at high temperatures. Carbon incorporation indeed induces a volume growth but the diamond (100) samples receiving a fluence of 4 × 10¹⁷ to 2 × 10¹⁸ at. cm⁻² (with a dose rate of 5 × 10¹⁵ at. cm⁻² s⁻¹ at 5 to 25 keV and 800 °C) showed no He-ion channelling. Common to these samples is that the top surface layer of a few nanometers has a substantial amount of graphite which can be removed by chemical etching. The rest of the grown layer is polycrystalline diamond with a very high density of extended defects.     

抗氧化纳米铜粉的制备及表征

超细铜粉在以铜代银并在电子浆料、陶瓷材料和化工催化剂等材料的制备中具有较好的应用前景。本研究用Vc作还原剂，PVP，PVA和PAA作为保护剂并在反应前预先配成还原剂／保护剂体系，用于铜氨溶液的还原，可以得到粒度分布均匀的纳米铜粉。所得铜粉用油酸钝化可以有效地防止铜粉的表面氧化。反应温度和n(保护剂)：n(Cu)值对铜粉颗粒的粒径和形状影响很大，当n(PVP)：n(Cu)处于0．03～0．1时，铜颗粒基本上为长方体形。PVA和PAA作为保护剂时所得铜粉颗粒的形状为非球形的n(保护剂)：n(Cu)的范围分别为0．02～0．09和0．02～0．08。其原因可归于高分子分散剂对铜粒子的部分保护作用。     

机械活化-湿化学合成LiMn2O4的组成、结构与表征

以MnO2和LiOH·H2O为原料,采用机械活化与湿化学集成的方法,在水溶液中直接合成了结晶态的尖晶石锂锰氧化物.当锂含量介于3.78%～4.35%之间时,所得锂锰氧化物为纳米级球形粉末,以尖晶石结构为主,含极少量的Mn3O4杂相;在300～800℃温度范围内热处理后,Mn3O4杂相消失,尖晶石结构更趋完善.所合成的含锂5.80%的高锂样品则以LiMnO2层状结构为主,含少量Mn3O4杂相,其SEM形貌为片状;在300～700℃下热处理8 h后,层状LiMnO2转变成尖晶石LiMn2O4,Mn3O4杂相峰明显减弱并随热处理温度的升高而消失;当温度升高至700～800℃时,开始出现缺锂的Li1-xMn2O4相.结果表明:该法制备锂锰氧化物可实现锂、锰、氧在原子级水平的均匀混合,所得产物的热稳定性能良好,其化学计量组成与结构易于调整和控制.