烟气轮机叶片应力分析与寿命评估方法评述

烟气轮机是炼油厂催化裂化装置的关键设备,合理预测叶片疲劳寿命是保障烟机安全运行的有效手段。从力学建模和边界条件两个方面简要阐述了叶片的应力分析方法,并系统分析了影响烟机叶片疲劳寿命的主要因素,提出了利用改进的局部应力应变法进行叶片寿命预测的合理性和叶片疲劳寿命的评估方法。     

晶须取向对SiCw/6061Al复合材料热压缩变形行为的影响

采用SEM 和 Magiscan-2A 图像分析系统研究了晶须取向对SiCw/6061Al复合材料在300℃压缩变形行为的影响.结果表明:晶须取向影响着晶须折断程度和转动角度; 随着晶须取向角的增加,晶须转动和折断行为所导致的软化效果下降.同时晶须取向也影响复合材料的热压缩应力-应变曲线的形状.在热压缩变形过程中,晶须取向角为0°和30°的复合材料表现出明显应变软化现象, 晶须取向角为45°的复合材料无明显软化现象.晶须取向角为90℃的复合材料表现出应变硬化现象.     

Wear and Creep Characteristics of a Carbon‐Derived Si3N4/SiC Micro/Nanocomposite

In the presented work some properties of a recently developed Si₃N₄/SiC micro/nanocomposite have been investigated. The material was tested using a pin on disc configuration. Under unlubricated sliding conditions using Si₃N₄ pin at 50 % humidity, the friction coefficient was in the range of 0,6 ‐ 0,7. The reduction of humidity resulted in a lower coefficient of friction, in vacuum the coefficient of friction had a value of about 0,6. The wear resistance in vacuum was significantly lower then that in air. The wear patterns on the Si₃N₄+SiC disc revealed that mechanical fracture was the wear controlling mechanism. Creep tests were realized in four point bending configuration in the temperature interval 1200‐1400 °C at stresses 50,100 and 150 MPa and the minimal creep deformation rate was established for each stress level. The activation energy, established from the minimal creep deformation had a value of about 360 kJ/mol and the stress exponent values were in the range of 0.8‐1.28. From the achieved stress exponents it can be assumed that under the studied load/temperature conditions the diffusion creep was the most probable creep controlling mechanism.     

Phase behavior,density, and crystallization of polyethylene in n‐pentane and in n‐pentane/CO2 at high pressures

The phase behavior and volumetric properties of polyethylene (PE) in solutions of n‐pentane and n‐pentane/CO₂ were studied in a temperature (T) range of 370–440 K at pressures up to 60 MPa. Measurements were conducted with a variable‐volume view‐cell system equipped with optical sensors to monitor the changes in the transmitted light intensity as the P or the T of the system was changed. Lower‐critical‐solution‐temperature‐type behavior was observed for all of the liquid–liquid (L–L) phase boundaries, which shifted to higher pressures in solutions containing CO₂. The solid–fluid (S–F) phase boundaries were investigated over a P range of 8–54 MPa and took place in a narrow T range, from 374 to 378 K in this P interval. The S–F phase boundary showed a unique feature in that the demixing temperatures showed both increasing and decreasing trends with P depending on the P range. This was observed in both the PE/n‐pentane and PE/n‐pentane/CO₂ mixtures. The density of these solutions were measured as a function of P at selected temperatures or as a function of T at selected pressures that corresponded to the paths followed in approaching the phase boundaries (S–F or L–L) starting from a homogeneous one‐phase condition. The data showed a smooth variation of the overall mixture density along these paths. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 89: 2201–2209, 2003     

A Relational Model of Workplace Victimization: Social Roles and Patterns of Victimization in Dyadic Relationships.

This article proposes a model of the ways in which dyadic interactions between employees who occupy 1 of 4 archetypal social roles in organizations can lead to either episodic or institutionalized patterns of victimization. The model shows how the occurrence of victimization involving these 4 role types is influenced by organizational variables such as power differences, culture, and access to social capital. The model integrates behavioral and social structural antecedents of victimization to develop a relational perspective on the dynamics of harmful behavior in the workplace. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

Fatigue limit evaluation of notches,small cracks and defects: an engineering approach

In this paper, the average stress method for the fatigue limit evaluation of stress raising geometrical features is revised and extended. In particular, an analytical close‐form approach was used and the linear elastic stress equations were modified by taking into account the effect of nominal stress on the local stress distribution. Hence, the average tangential stress was correctly evaluated over a distance of 2a₀, where a₀ was El Haddad's short crack constant, for long and small notches as well as for crack‐like notches. When this model is applied to a wide range of geometrical features subjected to mode I fatigue loading, the classical shape of the curves of the Kitagawa–Takahashi diagram was obtained for changes in crack‐like notch size. Similarly, notch sensitivity was estimated by reducing the notch tip radius. The accuracy of the proposed method in predicting fatigue limits was then checked by using experimental data taken from the literature and generated on testing specimens weakened by rounded and sharp notches as well as by small artificial defects.     

具有阻力特性材料的σ_f－σ关系及一种新的阻力曲线测定方法

通过对相变增韧陶瓷及一种可切削玻璃－陶瓷动态疲劳（恒应力速率）试验中高应力速率区断裂应力下降现象的理论分析，发现这种现象与材料的阻力特性（Ｒ－ｃｕｒｖｅ）密切相关。确立的σ_ｆ－σ理论关系能够很好地描述整个应力速率区间内的动态疲劳试验结果。高应力速率区σ_ｆ－σ在双对数坐标下为负斜率直线，直线斜率为（ｍ为阻力曲线ＫＲ＝ｋ（△ａ）~ｍ的指数），断裂主要由材料阻力行为控制；低应力速率区，σ_ｆ－σ在双对数坐标下为正斜率直线，直线斜率为　（ｎ为应力腐蚀指数），断裂主要由材料应力腐蚀行为控制。建立了测定材料阻力特性的一种新方法，分别用这种方法及压痕／弯曲方法对一种可切削玻璃－陶瓷的阻力特性进行了实验测定，两种方法所得结果有很好的一致性。     

On the corrosion fatigue crack initiation model and expression of metallic notched elements

In the present study, attempts are made to extend the application of the mechanical model for the fatigue crack initiation (FCI) and the FCI life formula of metallic notched elements in laboratory air to those in the corrosive environment. The test results and analysis of the corrosion FCI (CFCI) life of aluminum alloys and Ti---6A1---4V show that the expression of the CFCI life obtained by modifying the FCI life formula in laboratory air can give a good fit to the test results of the CFCI life. The salt water (3.5% NaCl) environment has no effects on the CFCI resistant coefficient compared with the FCI resistant coefficient in laboratory air. However, 3.5% NaCl environment greatly decreases the CFCI threshold of aluminum alloy, but has little effect on the CFCI threshold of Ti---6A1---4V. The loading frequency ranging from 1 Hz to 10 Hz has no appreciable effect on the CFCI life, and thus, the CFCI threshold of aluminum alloys investigated. Hence, the expression for the CFCI life of metallic notched elements proposed in this study is a better one, which reveals a correlation between the CFCI life and the governing parameters, such as, the geometry of the notched elements, the nominal stress range, the stress ratio, the tensile properties and the CFCI threshold. However, this new expression of the CFCI life needs to be verified by more test results.     

氧化铝陶瓷缺口件循环疲劳及断裂机理

用实验方法研究了Ａｌ＿２Ｏ＿３陶瓷缺口试件在循环载荷作用下的疲劳寿命。结果表明，缺口导致的应力集中效应显著降低了循环疲劳寿命；若用缺口根部最大应力为应力水平，则不同缺口半径陶瓷试件具有相同疲劳断裂规律，说明陶瓷材料的疲劳集中系数和理论应力集中系数相同。本文还分析讨论了陶瓷材料的循环疲劳寿命表达式和循环疲劳断裂机理。     

Grain Boundary Sliding in Fatigue of Pure Aluminum

The distributions of plastic strain near grain boundaries induced by fatigue loading were investigatedby the fiducial grid method in pure aluminum specimens, and the resulted grain boundary sliding(GBS) was systematically analysed. The results show that the strain field near a grain boundary isnonuniform. GBS is restricted by the junction of grain boundaries and causes discontinuities of bothdisplacement and strain. A peak value of shear strain was created in short-range area across the grainboundary. GBS plays an important role in cyclic softening and secondary hardening. The control fac-tor of GBS is the relative orientation between two grains and the macro orientation of the grainboundary rather than the ∑ value of the boundary.