High-velocity oxyfuel thermal spray coatings for biomedical applications

Plasma spraying is used to produce most commercially available bioceramic coatings for dental implants; however, these coatings still contain some inadequacies. Two types of coatings produced by the high- velocity oxyfuel (HVOF) combustion spray process using commercially available hydroxyapatite (HA) and fluorapatite (FA) powders sprayed onto titanium were characterized to determine whether this relatively new coating process can be applied to bioceramic coatings. Diffuse reflectance Fourier transform infrared (FTIR) spectroscopy, x- ray diffraction (XRD), and scanning electron microscopy (SEM) were used to characterize the composition, microstructure, and morphology of the coatings. The XRD and FTIR techniques revealed an apatitic structure for both HA and FA coatings. However, XRD patterns indicated some loss in crystallinity of the coatings due to the spraying process. Results from FTIR showed a loss in the intensity of the OH^∼ and F^∼ groups due to HVOF spraying; the phosphate groups, however, were still present. Analysis by SEM showed a coating morphology similar to that obtained with plasma spraying, with complete coverage of the titanium substrate. Interfacial SEM studies revealed an excellent coating-to-substrate apposition. These results indicate that with further optimization the HVOF thermal spray process may offer another method for producing bioceramic coatings.     

不锈钢在Cl^- ＋H2SO4溶液中轻载下的腐蚀磨损

从腐蚀磨损速率、钝化膜承载能力以及点蚀与腐蚀磨损的关系等方面，研究Cl对不锈钢在H2SO4溶液中轻载下的腐蚀磨损行为的影响，在自然电位下，Cl对腐蚀磨损存在一临界载荷，低于此载荷腐蚀磨损速率略有降低：高于此载荷，腐蚀磨损率增加，轻载下磨痕内的点蚀坑较多而深，高载下点蚀坑少且浅，在钝化区，Cl将降低钝化膜的承载能力，使腐蚀磨损率增加。     

用稀土钇提高离子镀TiN膜层与基体结合力的研究

研究了不同含量稀土钇对离子镀ＴｉＮ膜与基体结合力的影响，结果表明，加入稀土钇后，大大提高ＴｉＮ膜与基体的结合力，并使膜层内ＴｉＮ相增加，此外，稀土钇能明显提高镀膜过程中钛料蒸发率，在相同镀膜内，能使ＴｉＮ膜层加厚。     

焊接工艺对2205双相不锈钢焊接接头综合性能的影响

采用等离子弧焊打底 TIG焊盖面及等离子弧焊打底 MIG焊盖面焊接工艺焊接了2205双相不锈钢,研究了2205双相不锈钢的焊接性,并对焊后固溶处理与未进行固溶处理的焊件组织特征、力学性能及抗腐蚀性进行了比较,研究了不同焊接热输入和固溶处理工艺对焊接接头综合性能的影响.     

45钢的离子氮碳共渗-离子渗氧复合处理

研究了45钢离子氮碳共渗-离子渗氧复合处理工艺。试验表明，45钢经离子氮碳共渗-离子渗氧复合处理后，表层可获得化合物和氧化物的复合层，该复合处理可以明显提高45钢的耐磨性。     

富钛BaO-TiO2(Ti/Ba=4～4.5)系微波介质陶瓷

采用固相反应法制备了富钛BaTi4+xO9+2x(x=0.0-0.50)微波介质陶瓷,探讨了TiO2含量以及烧结温度对物相组成和介电性能的影响.在1300～1350 ℃烧结BaTi4+xO9+2x陶瓷即可达到约98%的相对密度.当x≤0.28时,BaTi4+xO9+2x陶瓷为BaTi4O9单相.随TiO2含量的增加,BaTi4+xO9+2x陶瓷从BaTi4O9单相逐渐转变成以BaTi4O9为主相,同时出现TiO2和Ba2Ti9O20相,并且随烧结温度提高,TiO2含量较多的试样中出现更多的Ba2Ti9O20相.随TiO2含量的增加介电常数逐渐增大,而Qf值呈下降趋势.Qf值从x=0.0时的约40 000 GHz逐渐降低至x=0.50时的15 000 GHz.     

（V30Ti35Cr25Fe10）97．5Si2．5合金的结构与吸放氢性能

采用XRD，SEM和PCT测试研究了（V30Ti35Cr25Fe10）97.5Si2.5（at％）合金的组织结构与吸放氢性能。结果表明：合金由BCC相和C14 Laves相组成，BCC相含量为75％，晶胞参数为α=0．3021nm，Laves相含量为25％，晶胞参数为α=0．4920nm和c=0．7996nm。由于含有大量的Laves相，合金具有良好的活化性能，室温下不需孕育期就可以快速吸氢，5min内达到吸氢饱和状态，饱和吸氢量达到2．98％（质量分数，下同）。在一定氢压下，合金的容量可由合金中BCC相和Laves相的容量按组分的含量进行线性组合而成。     

Cu中间层SiCp/Al MMCs TLP扩散连接过程分析

采用铜箔作中间层,在连接温度为853 K、无压的条件下进行了瞬间液相连接,对TLP扩散连接过程及其动力学模型进行了分析,并对试验结果进行了的验证.结果表明TLP扩散连接理论模型和试验结果之间还存在着一些差异,对等温凝固过程还需要进一步探讨.分析认为,AlMMCs中大量的晶界、亚晶界、位错等短路扩散通道的存在,直接影响TLP连接过程及其动力学.     

AA1235铝箔坯料的中温相转变

研究了AA1235铝箔坯料中温温度范围内相形成和转变的规律。结果表明,AA1235铝箔坯料在中温温度范围内存在两个相变反应:一个是从铝基体中析出α(AlFeSi)相的脱溶相变,另一个是β′(AlFeSi)→α(AlFeSi)的相变;α(AlFeSi)相的尺寸非常细小,在nm数量级;中间退火过程中Fe、Si元素在铝基体中的固溶度存在一极小值点,即最佳固溶贫化点,该现象的存在是上述两个对固溶度的变化起相反作用的相变过程共同作用的结果。     

Zr3V30Dx氘化物物相及其热解析行为研究

测定了氘化对Zr3V3ODx物相的影响，发现Zr3V30Dx氘化物只有x≥2．0才能稳定存在，由于氘在晶格中的占位不同，随氘含量增加分别出现两种η-碳化物相的氘化物——β相和γ相。对Zr3V3ODx氘化物的热解析行为研究表明：Zr3V30Dx氘化物的稳定性随氘含量的增加而降低，β声相和γ相表现出不同的解析行为，其变化规律与Zr3V3ODx氘化物中的氘占位原则相一致。