Microscopic fatigue processes in a plain-weave glass-fibre composite

This paper focuses on the microscopic damage and progressive failure of a composite reinforced by plain-weave glass cloth under tensile fatigue loading. The fatigue process was divided into three stages like that of multi-directional laminates. It was found that the internal damage at each stage (matrix cracks, debonds in the weft, successive debonds in the warp and ‘metadelaminations’ between warps and wefts) occurred near the cross-over point of the fabric. The modulus decay mechanism was explained by considering the progression of this internal damage. From the end of the first stage to the beginning of the middle stage, a characteristic damage state (CDS) (called a ‘meta-CDS’) was observed. It was found that woven composites have a unit area of damage accumulation (called a ‘unit cell’) and the damage of each unit cell and its distribution control the total fatigue damage of the material.     

Rene′95粉末合金喷丸强化研究

研究了Ｒｅｎｅ′９５热等静压粉末高温合金喷丸后的残余应力场、组织结构、致密度及其与疲劳性能的关系。结果指出，喷丸强化能够有效地提高合金高周和低周疲劳强度。     

MICROSTRUCTURE AND FATIGUE PROPERTIES OF A WELDED DUPLEX STAINLESS STEEL

Abstract— In response to the increasing structural applications in duplex steels for welded structures, fatigue behaviour of a SAF 2304 grade duplex stainless steel was investigated, considering both the base metal and GTAW welded joints. Fatigue curves and fatigue limits under rotary bending fatigue were obtained. The study focused attention on the microstructural features of fatigue crack propagation of the two series of experiments, thereby permitting an evaluation of the tortuous crack path of welded joints and the mechanisms related to threshold microstructural barriers.     

低速爆轰管对黑火药的点传火性能研究

文章采用中心点火管结构的实验装置研究了黑火药的点传火性能。用低速爆轰 (L VD)中心点火管来点燃黑火药时 ,1# ～ 3# 大粒黑药的传火速度为 70 0 m· s-1～ 80 0 m· s-1数量级 ,燃烧波宽度在 3.1ms～ 3.5 ms,最大压力峰值 :1# 为 36 .4 MPa,2 # 为 2 4 .0 MPa,3# 为 38.0 MPa。用普通中心点火管点燃黑火药时 ,2 # 、3# 和钝化 2 # 大粒黑的传火速度分别为 6 1.2 m· s-1、6 8.2 m·s-1和 4 0 .1m· s-1,最大燃烧波宽度分别为 9.2 ms、6 .3ms和 9.5 ms。燃烧波表明 ,L VD中心传火管与普通中心传火管相比较 ,在传火管的不同位置处 ,前者的 P- t曲线一致性远高于后者。     

Fatigue behaviour of a phenolic matrix composite

This paper presents results of a fatigue life investigations carried out in plate specimens of a fibre-glass-reinforced phenolic matrix composite. Tensile and Young's modulus data were obtained at four different testing temperatures (room temperature, 100, 150 and 200 °C). The fatigue S−N data were obtained at room temperature only and for two stress ratio values (R=0 and 0.4). Fatigue and tensile behaviour was assesesed in the composite with the fibres aligned in the longitudinal loading direction. The results were obtained for two values of volume fraction (0.28 and 0.42) and three different glass surface treatments. A detailed comparison of fatigue results is given taking into account several fatigue parameters and also the testing variables. Results of observations of SEM fracture surfaces are also presented.     

Thermal—Mechanical Fatigue Behavior and Life Analysis of Cast Ni—base Superalloy K417

In-phase(IP) and out-of-phase(OP)thermal-mechanical fatigue(TMF) behavior of cast Ni-base superalloy K417 was studied.All experiments were carried out under total strain control with temperature cycling between 400-850℃.Both in-phase and out-of-phase TMF specimens exhibited cyclic hardening followed by cyclic softening at the minimum temperature.Besides,they cyclically hardened in the early stage of life followed by cyclic softening at the minimum temperature.Besides,they cyclically hardened in the early stage of life followed by cyclic softening at the maximum temperature.OP TMF life was longer than of IP TMF.Various damage mechanisms operating in different controlled strain ranges and phasing were discussed.A few life prediction methods for isothermal fatigue were used to handle TMF fatigue and their applicability to superalloy K417 was evaluated.The SEM analysis of the fracture surface showed that transgranular fracture was the principal cracking mode for both IP and OP TMF.Oxidation was the main damage mechanism in causing shorter fatigue life for IP TMF compared with OP TMF.     

HSLA-80/100钢的焊接

对ＨＳＬＡ－８０／１００钢的焊接性、焊接材料及焊接工艺进行了综述，并指出了现存在的主要问题。     

Crack growth in aluminium alloy sheet material under flight-simulation loading

Crack propagation tests were carried out on 2024-T3 sheet specimens to study the effects of omitting low-amplitude cycles from the gust-dominated TWIST load sequence (MiniTWIST) and the removal of small load ranges from the manoeuvre-dominated FALSTAFF load sequence (short FALSTAFF). In other tests high-amplitude loads of TWIST and MiniTWIST were truncated at different levels. The results are compared with data from similar test programmes, including crack initiation. Attention is paid to unstationary crack growth retardation and a transient retardation during initial crack growth started by an artificial crack.     

用于频率合成器的低损耗声表面波滤波器

简述了产生声表面波滤波器插入损耗的主要机理和获得低损耗的原则；介绍了根据此原则对１００～５００ＭＨｚ５种滤波器的研制过程和结果。实验表明，采用镜像阻抗连接换能器结构可达到３～４ｄＢ的低损耗，并成功地应用于频率合成器中。