锰含量对衬板用低碳高合金钢组织和性能的影响

用光学金相显微镜、衍射仪及显微硬度计，研究了锰含量对衬板用低碳高合金钢组织和性能的影响。结果表明，当锰含量由2．0％增加到3，0％时，合金的退火态组织由上贝氏体＋屈氏体转变为马氏体，淬火回火后均为单相板条马氏体组织。随锰含量的增加，硬度稍有增大，冲击韧度下降，均匀耐腐蚀性有所降低。含锰量为2％的低碳高合金钢达到了矿山用衬板的使用要求，从成本考虑，是更经济的。     

FORMATION OF MANGANESE SILICIDE THIN FILMS BY SOLID PHASE REACTION

1. IntroductionThe transition metal silicides have attraeted much attention because of their potentialapplicatiOIl in very large scale integration (VLSI) de.ice[1]. Near-noble metal silicides canbe used as Schottky al1d ohn1ic col1tacts in silicon-based d…     

高锰钢的泡沫陶瓷过滤净化

采用泡沫陶瓷过滤片对高锰钢进行过滤处理，对其进行金相分析和测试密度，冲击韧性和耐磨性能，并与未过滤的高锰钢进行对比，实验结果表明，在过滤的高锰钢中，金属夹杂物明显减小，密度提高0．53％，冲击韧性39．5％，耐磨性能提高1．04倍，批量生产结果表明，过滤的高锰钢球磨机衬板的使用寿命提高0．6－0．7倍。     

Phase transition of lithiated-spinel Li2Mn2O4 at high temperature

1 Introduction Lithium manganese oxides are the most attractive cathode materials for rechargeable lithium-ion batteries because of their low-cost and less toxicity when compared with either cobaltates or nickelates[1?3]. Among these oxides, the spinel-fr…     

水韧处理工艺对合金高锰钢组织和性能的影响

研究了水韧处理工艺对Cr、V、Mo合金高锰钢金相组织和力学性能的影响.试验结果表明,水韧处理工艺对合金高锰钢金相组织和力学性能有显著影响,适宜的水韧处理工艺(加热至1100℃,保温4h)可以改善高锰钢金相组织和力学性能,使σb=780MPa、δ5 30%、αK=150J/cm2、HBS=258,使用寿命达到1800h以上.     

铁矿石冶金性能实验方法的改进

在不影响实验结果的前提下，对铁矿石的还原度实验方法进行改进。改进后每个实验时间缩短3～4．5h，且大大降低了实验成本。     

Process for cobalt separation and recovery in the presence of nickel from sulphate solutions by Cyanex 272

The present paper deals with the extraction of cobalt from a solution containing cobalt and nickel in a sulphate medium similar to the leach liquor obtained by the dilute sulphuric acid pressure leaching of the Pacific Ocean nodules matte followed by copper extraction. The commercial extractant Cyanex 272 (bis (2, 4, 4-trimethylpentyl) phosphinic acid) is used for this purpose. The leach liquor used for the present study contains Co =1.78 g/L and Ni=16.78 g/L. Before cobalt extraction, impurities, such as copper and iron, are removed from the leach liquor by the precipitation method. Increasing the concentration of Cyanex 272 increased the extraction percentage of cobalt due to the increase of equilibrium pH. Cobalt extraction efficiency of >99.9 % is achieved with 0.20 M Cyanex 272 in two counter-current stages at an aqueous: organic (A:O) phase ratio of 1.5∶1. Complete stripping of cobalt from the loaded organic containing 2.73 g/L Co was carried out at pH 1.4 by a synthetic cobalt spent electrolyte in two stages at an A:O ratio of 1∶2. The enrichment of cobalt during extraction and stripping operations was about 3.5 times. A complete process flowsheet for the separation and recovery of cobalt is presented.     

稀土镁对铸态高锰钢机械性能的影响

实验了稀土镁对铸态高锰钢机械性能的影响．结果表明，在一定的Ｃ、Ｍｎ、Ｓｉ成分中，加入ＲＥＭｇ合金均使其铸态机械性能有所提高．同时在工业设备上试验证实，加入ＲＥＭｇ的某种成分之高锰钢，在铸态时其耐磨性能、机械性能均已达ＺＧＭｎ１３－１和ＺＧＭｎ１３－２（ＧＢ５６８０－８５）水平并超过了铸态使用的７５Ｍｎ１３     

活性石灰/粉煤灰制备烧结烟气脱硫剂配比试验研究

本文研究了以钢铁企业常用物料活性石灰和自备电厂粉煤灰制备的脱硫剂,在循环流化床脱硫试验装置上进行了烧结烟气脱硫剂配比试验.试验结果表明,活性石灰与粉煤灰的质量比按1:2配置时,脱硫剂钙的利用率较高,具有较好的经济性.     

稀盐酸中锰结核还原浸出溶液净化除铁

针对酸性氯化物中黄铁矿还原浸出锰结核的溶液成分特点，选择黄钠铁矾法进行了沉淀分离铁的研究。结果表明温度和晶种以及溶液ｐＨ值是影响铁矾沉淀的重要因素。在ｐＨ２．０左右，溶液温度高于９０℃，足量晶种加入的情形下，１５０ｍｉｎ后可将溶液中的铁含量降至０．１ｇ／Ｌ。沉矾过程的表观活化能为９４．６６ｋＪ／ｍｏｌ。黄铁矿氧化生成的硫酸根随铁一同沉淀，从而消除了ＳＯ２－４在氯化物体系中的积累。