高压水射流技术粉碎原盐的研究

以原盐为被粉碎研究对象,通过对高压水射流粉碎原盐形貌的观察和成分分析、高压水射流原盐粉碎性能分析,以及高压水射流粉碎原盐各影响因素的正交分析,研究表明高压水射流粉碎技术对原盐具有良好的解理性且粉碎效率高、耗能低。各因素对原盐粉碎效果的影响顺序为:射流压力卤水喷嘴直径、料液混合喷嘴直径、靶面形状。     

低松装密度水雾化铜粉工艺的研究

本文研究了氧化 还原法生产铜粉的新工艺 ,该工艺是通过氧化还原将水雾化铜粉加以表面改性 ,形成海绵状的粉末 ,显著降低水雾化铜粉的松装密度 ,这种铜粉既具有电解铜粉低的松装密度 ,又具有水雾化铜粉高的流动性。讨论了氧化时间、氧化温度对铜粉松装密度的影响。本工艺是一种新型环保、节能、可替代电解法生产铜粉的先进工艺     

Powder Deposition in Three Parallel-Oriented Dies of Different Shapes

Uniformity of bulk density distribution during the die filling process is required to minimize quality problems, such as distortion and cracking, for powder compacts. Understanding the die filling process is necessary in ensuring a uniform powder deposition. The second-generation pressure deposition tester (PDT-II) was used to investigate the deposition process and final pressure distribution of powder filling in toroidal, cylindrical, and E-shaped dies. All tests were conducted using a spray-dried free-flowing granular powder. The results indicated that for toroidal dies: (1) the area around 0° orientation (the leeward end) had the highest pressure values (1186.7 to 2498.0 Pa), with the average pressure values of the remaining area 353.7-648.0 Pa; (2) the pressure distribution was symmetrical about the centerline parallel to the feed shoe movement direction; (3) the highest feed shoe speed (500 mm/s) led to the most nonuniform pressure distribution among the three speeds; (4) higher feed shoe speed did not always result in higher final pressure values; and (5) the right die tended to have higher final pressure values (215.0 to 2498.0 Pa) than the center die (95.4 to 2052.5 Pa). For E-shaped dies: (1) the final pressure values of the middle leg (308.9 to 760.7 Pa) were higher than those of the left and the right legs (148.9 to 530.3 Pa); (2) the area along the backside had the highest final pressure value (1054.6 to 1303.8 Pa); (3) the pressure distribution was symmetrical about the centerline parallel to the feed shoe movement direction; and (4) neither the center die nor the right die always had higher pressure values than the other one at all locations. Comparison between cylindrical and toroidal dies indicated that: (1) neither of the two die shapes (cylinder and toroid) led to consistently higher or lower final pressure values at all locations and (2) for all three feed shoe speeds, the toroidal die had higher average final pressure values in the 0° orientation.     

Hydrogen Absorption and Release Behavior in Hydrogen Decrepitation Process of Nd-Fe-B Alloys

The behavior of hydrogen absorption and release in hydrogen decrepitation (HD) process of Nd-Fe-B alloys were investigated. The results reveal that the reactivity and the amount of hydrogen absorption in HD process are related to the surface activity of the alloy so that the fresh and active surface has a higher efficiency. The presence of Nd-rich phase at the grain boundary is an essential factor of the HD activity of the alloy at room temperature. On degassing, hydrogen is released from the HD powder continuously with increasing temperature. And the residual hydrogen is as low as 0.0015% at 1073K, which shows that the hydrogen is almost exhaused. It is feasible to remove the hydrogen from the HD powder by heating treatment at the temperature of 523-723K for 1h prior to the magnetic field forming in order to decrease the harmful effect of hydrogen on the easy axis alignment of HD magnet.     

铸造Ti—0.2Pd合金SF—1000双级风机叶轮的研制

Ｔｉ－０．２Ｐｄ合金ＳＦ－１０００双级风机叶轮是大型盐酸再生设备的主要部件，采用整体铸造方法制造，无论在技术上还是经济上都是十分有利的。本文主要介绍采用加工石墨，铸铁组合型，真空电弧凝壳熔炼铸造工艺，成功地研制出整体铸造风机叶轮。     

激光法合成SiC超细粉末物理化学过程的研究——Ⅰ.实验规律及粉末特性

用50W连续波CO_2激光器为热源,诱发SiH_4和C_2H_4反应,合成SiC超细粉末。实验确定了反应腔体内压力p、气源中的C/Si原子比、喷嘴内径2r以及激光功率密度与粉末特性之间的关系,并对合成的产物进行物理、化学表征。     

高强度烧结钢

为开拓粉末冶金材料新的应用领域，近年来对高强度烧结钢进行了大量的研究与开发。本文简要介绍Ｈｏｇａｎａｓ公司开发的一些高强粉末冶金材料及对一些高强度烧结材料尺寸变化的控制。     

超细铁粉和氧化铁颗粒的研究

用透射电镜和图像分析仪等研究了超细铁粉和γ-Fe_2O_3粉末的结构、形貌、粒子的平均尺寸以及粒度分布。研究结果表明,多数超细铁粉粒子近似呈球形,并且,铁粉粒子由两相组成,粒子的核心部分是金屑a-Fe,表面的包裹层为氧化物层,它由Fe_3O_4和7-Fe_O_3的混合物组成。氧化层的平均厚度大约占整个粒子直径的20％左右。羰基铁粉粒子(含氧化层)的平均直径为16nm。直径在4～24nm范围的粒子数占总粒子数的91％,而7-Fe_2O_3粉末既有雪茄状粒子,也有小球状粒子。分析表明,球状粒子的平均直径为113nm,雪茄状粒子的平均直径(按<长 宽>/2计算)为148nm。由于超细铁粉粒子很细,且有磁性,制备电镜试样时分散比较困难。本文比较了几种分散方法后,使用了一种较好的分散方法——超声喷管分散法。     

低速爆轰管对黑火药的点传火性能研究

文章采用中心点火管结构的实验装置研究了黑火药的点传火性能。用低速爆轰 (L VD)中心点火管来点燃黑火药时 ,1# ～ 3# 大粒黑药的传火速度为 70 0 m· s-1～ 80 0 m· s-1数量级 ,燃烧波宽度在 3.1ms～ 3.5 ms,最大压力峰值 :1# 为 36 .4 MPa,2 # 为 2 4 .0 MPa,3# 为 38.0 MPa。用普通中心点火管点燃黑火药时 ,2 # 、3# 和钝化 2 # 大粒黑的传火速度分别为 6 1.2 m· s-1、6 8.2 m·s-1和 4 0 .1m· s-1,最大燃烧波宽度分别为 9.2 ms、6 .3ms和 9.5 ms。燃烧波表明 ,L VD中心传火管与普通中心传火管相比较 ,在传火管的不同位置处 ,前者的 P- t曲线一致性远高于后者。     

纳米氧化铟粉体的形貌与结构研究

用湿化学法制备了纳米极氧化铟超细粉体。利用透射电子显微镜、图像分析仪研究了纳米氧化铟粉体的形貌、尺寸分布和结构特征。结果表明，氧化铟粉体呈方片状，尺寸在10-30nm，化学组分高纯，达到了纳米级粉末要求；粉体的尺寸均匀，但在不同条件下制得的粉体，其尺寸相差较大；制备得到的氧化铟超细粉体的结构为体心立方。