稀土元素对铂的室温强度和电阻率之影响

添加微量稀土元素使纯Pt的再结晶温度提高200～300℃,硬度和抗拉强度增高2～3倍。含重稀土铂合金的强度一般高于轻稀土铂合金。Eu和Yb与Pt组成的合金的强度很高。微量稀土元素使铂的电阻率增加很少,当含量增加到1wt%时,电阻率明显升高,而硬度和抗拉强度反而降低。     

RECOVERING RE FROM LEACHING LIQUOR OF RARE EARTH ORE BY EXTRACTION

ＲＥＣＯＶＥＲＩＮＧＲＥＦＲＯＭＬＥＡＣＨＩＮＧＬＩＱＵＯＲＯＦＲＡＲＥＥＡＲＴＨＯＲＥＢＹＥＸＴＲＡＣＴＩＯＮＣｈｉＲｕ＇ａｎ；ＸｕＪｉｎｇｍｉｎｇ；ＨｅＰｅｉｊｉｏｎｇ；ＺｈｕＹｏｎｇｊｕｎ（ＩｎｓｔｉｔｕｔｅｏｆＮｕｃｌｅａｒＥｎｅｒｇｙＴｅｃ...     

钙钛矿催化材料La1-xCexCoO3+δ的制备、表征及甲烷燃烧催化性质

采用柠檬酸发泡法制备了钙钛矿LaCoO3催化材料;研究了Ce对La进行掺杂替代对催化材料性能的影响;通过BET、XRD、SEM等手段对催化材料进行了物性表征;以甲烷完全燃烧为目标反应,研究了钙钛矿La1-xCexCoO3 δ的催化性能.结果表明:铈掺杂对材料晶相有较大影响,当掺杂量x小于0.3时,粉体晶型基本不变,而当掺杂量达到0.5时,有明显CO3O4晶相出现,LaCoO3钙钛矿晶相完整性遭到破坏,当掺杂量大于0.7时,钙钛矿晶相大大弱化甚至消失;LaCoO3是一种性能优良的甲烷燃烧催化材料,Ce的掺杂替代对催化材料活性有明显影响,并增强了催化材料的高温稳定性能,铈最佳掺杂量为0.3;前驱体经700℃焙烧形成了较为完整的钙钛矿晶型,经800℃焙烧后,催化材料最高活性为:t10%=390℃,t90%=603℃.     

快淬AB5型贮氢合金研究

使用快淬工艺制备了两种成分的ＡＢ５型贮氢合金并做了电化学充放电循环实验,比较了它们的起始活化性能、放电容量、电化学循环稳定性、放电电压性能等。发现快淬合金的电化学循环稳定性明显优于铸态合金,放电电压平台性能也较好,但快淬导致起始活化速度慢,放电容量也有所降低。快淬对放电电压平台高低的影响随合金成分的不同而改变     

稀土对电沉积Ni-P合金镀层显微组织的影响

研究了在镀液中添加稀土元素后Ni P合金镀层显微组织的变化。X射线衍射及透射电镜分析结果表明 ,在镀液中添加一定量的稀土元素 ,明显地促进了Ni P合金微晶组织向非晶态组织转变 ,从而提高Ni P合金镀层的耐蚀性。电化学极化曲线测试结果表明 ,稀土元素能够促进电沉积过程的阴极极化。由于稀土离子的特性吸附抑制了合金原子在电极界面的正常形核 ,因而促进了非晶组织的形成。     

钇基重稀土对大断面球铁件本体性能的影响

介绍了QT400-18高炉冷却壁铸件的性能要求,并对使用轻稀土球化剂导致铸件力学性能验收不达标的原因进行分析。采用钇基重稀土球化剂进行试验,结果显示铸件本体力学性能和金相组织都达到要求。指出钇基重稀土有加入量范围宽的特点,在原料不稳定的情况下,重稀土的抗干扰性、抗石墨畸变性、抗衰退性能较为明显,能保证铸件心部的球化等级及力学性能。     

Durability experiment on anti-electron-bombardment of RE2O3-Mo secondary emission material

A durability test to determine anti-bombardment sensitivity of multi-RE2 O3-Mo secondary emission material was carried out and the variation of maximum secondary emission coefficient (δmax) was monitored at regular intervals. After the experiment, the cathode was analyzed with SEM, EDS and XRD techniques. The results show that δmax of multi-RE2O3-Mo cermets cathode heated to 1 100 ℃ under electron bombardment of 300 W/cm2 reaches the peak of 3.35 at 200 h. After 500 h of bombardment, the maximum secondary-electron-yield curve stabilizes. The δmax value of the cathode remains at about 2.5 after 1 000 h and represents a good anti-bombardment property. The high δmax value of the cathode is related with formation of an enriched Y2 O3 layer on the surface under high temperature and with the amount of La2 O3 particles in the shape of nanometer distributed on the surface. Under the experimental conditions, the drop of δmax value may be caused by the reduction of La2 O3 content and the porous layer resulted from evaporation of MoO2, which is formed when Mo at the surface is oxidized.     

Ce变质处理提高Fe-Cr-Ni中熵合金抗点蚀性的研究

目的 研究Ce变质处理提高Fe-Cr-Ni中熵合金在3.5％NaCl溶液中抗点蚀性的机理.方法 通过动电位极化实验,分析Ca变质处理与Ce变质处理的Fe-Cr-Ni中熵合金的抗点蚀性.利用SEM和EDS等手段观察了经不同变质处理后合金中夹杂物的形貌和元素组成,并结合阻抗谱分析与XPS技术研究了Ce对钝化膜保护力的影响....     

纳米晶Nd10.1Fe76.2Co4.5Zr3B6.2 永磁材料制备工艺和磁性能的研究

采用熔体快淬及热处理工艺制备Nd10.1Fe76.2Co4.5Zr3B6.2永磁材料,研究了制备工艺参数和热处理工艺对材料结构和磁性能的影响.结果表明,粘结磁体的磁性能与熔体快淬和热处理工艺密切相关,快淬速度为20m/s的薄带经690℃×4min退火处理可得到最佳磁性能Br=0.714T、JHc=698kA/m、(BH)max=82.0kJ/m3.     

钼及钼合金研究与应用进展

综述了钼单晶、钼铼合金、钼钛锆（TZM）合金、钼硅合金、稀土钼合金、钼铜合金的研究现状与应用进展，详细介绍了稀土钼合金的研究与应用，包括稀土钼的韧化作用机理、稀土掺杂钼粉的粒度控制、稀土钼合金力学性能和热发射性能研究。由于钼及钼合金具有高温性能好、热传导率高、膨胀系数低等特性，因此在航空航天、核能工业等诸多领域得到广泛应用。今后，发展新的制备工艺，提供更高性能的材料，开辟新的应用领域成为钼及钼合金发展的关键。